Abstract: A method for preparing a biodegradable polyester elastomer includes a following steps comprising: dissolving a predetermined amount of titanium dioxide in an aqueous mixture of sulphuric acid, DI water, and ethanol to form a first solution; refluxing the first solution in a silicone oil bath and a stirring speed of 300-450 rpm at a temperature of 90-100° C. to form a second solution; preparing a solid superacid catalyst by drying, grinding and calcining sulfated titania and using this catalyst to produce a biodegradable polyester elastomer.

Abstract: A method for preparing a biodegradable polyester elastomer includes a step of carrying out an esterification reaction to produce a glycerol-sebacic acid prepolymer, a glycerol-maleic acid prepolymer, or a glycerol-adipic acid prepolymer. The esterification reaction is carried out between sebacic acid, maleic acid, or adipic acid and glycerol in a molar ratio of 1:1-2 with an effective amount of sulfated titania under a vacuum pressure of 300-600 mTorr. Therefore, the production time of the biodegradable polyester elastomer can be reduced significantly.

Abstract: A method for preparing a biodegradable polyester elastomer includes a step of carrying out an esterification reaction to produce a glycerol-sebacic acid prepolymer, a glycerol-maleic acid prepolymer, or a glycerol-adipic acid prepolymer. The esterification reaction is carried out between sebacic acid, maleic acid, or adipic acid and glycerol in a molar ratio of 1:1-2 with an effective amount of sulfated titania under a vacuum pressure of 300-600 mTorr. Therefore, the production time of the biodegradable polyester elastomer can be reduced significantly.

Abstract: Disclosed is a biodegradable polyester elastomer which is formed by an esterification reaction between an acidic compound and an alcohol compound using a superacidic catalyst. Thereby, the reaction time of the esterification reaction can be reduced remarkably.