Abstract: This invention relates to a stainless steel gasket having markedly improved strength and fatigue properties due to precipitation strengthening. Its composition comprises C: at most 0.03%, Si: at most 1.0%, Mn: at most 2%, Cr: 16.0%-18.0%, Ni: 6.0%-8.0%, N: at most 0.25%, if necessary Nb: at most 0.30%, and a remainder of Fe and unavoidable impurities. After cold rolling, final annealing is carried out, and after a structure is formed of recrystallized grains with an average grain diameter of at most 5 ?m having an area ratio of 50-100% and an unrecrystallized portion having an area ratio of 0-50%, a metal gasket is formed by steps including temper rolling with a reduction of at least 30% to make the area ratio of a strain induced martensite phase at least 40%, and forming and heat treatment at 200-350° C.

Abstract: This invention relates to a stainless steel gasket having markedly improved strength and fatigue properties due to precipitation strengthening. Its composition comprises C: at most 0.03%, Si: at most 1.0%, Mn: at most 2%, Cr: 16.0%-18.0%, Ni: 6.0%-8.0%, N: at most 0.25%, if necessary Nb: at most 0.30%, and a remainder of Fe and unavoidable impurities. After cold rolling, final annealing is carried out, and after a structure is formed of recrystallized grains with an average grain diameter of at most 5 &mgr;m having an area ratio of 50-100% and an unrecrystallized portion having an area ratio of 0-50%, a metal gasket is formed by steps including temper rolling with a reduction of at least 30% to make the area ratio of a strain induced martensite phase at least 40%, and forming and heat treatment at 200-350° C.

Abstract: An austenitic stainless steel for use in engine gaskets having a high fatigue strength and resistance to settlement and method of manufacture thereof. The austenitic stainless steel is prepared by cold rolling at least 40%, annealing at a temperature of 700° C. to 900° C. followed by temper rolling with a reduction of at least 40%. The metal structure obtained by annealing is a recovered unrecrystallized structure or a mixed structure of a recovered unrecrystallized structure and a recrystallized structure. The austenitic stainless steel includes at most 0.03% C, at most 1.0% Si, at most 2.0% Mn, 16.0% to 18.0% Cr, 6.0% to 8.0% Ni and up to 0.20% N.

Abstract: Engine gaskets for automobiles are fabricated from an as-quenched stainless steel having a martensitic-ferritic duplex-phase phase structure in which martensite comprises from 40% to 80%. The steel has a composition comprising on a weight basis; C+N: 0.1%-0.3%, Si: not greater than 0.5%, Mn: not greater than 0.7%, Cr: 10%-17%, and Ni: 0-0.6% and a Vickers hardness of from 300 to 500, The steel can be produced by quenching the steel after heating at 850-1000° C.

Abstract: A thermoset acrylic resin composition for coating metallic materials, particularly stainless steel, having a superior adhesion thereonto and hence a superior resistance to forming after coated, and a stainless steel piece coated with a coating material comprising the above composition, followed by baking, and having a superior colorability and endurability, are provided, which composition is obtained by radical-copolymerizing (a) an acrylic or methacrylic acid ester having 1-12 C in the ester moiety, in 40-80% by weight, (b) a hydroxyl group- or epoxy group-containing acrylic or methacrylic acid ester, in 20-5% by weight, (c) a vinyl group-containing polysiloxane in 20-0.01% by weight and (d) a vinyl group-containing silane compound in 20-2% by weight, these % by weight being based on the total weight of monomers (a)-(d).