Abstract: The present invention provides a polymeric-type antistatic agent containing a polymer composition consisting of a polymeric-type antistatic agent containing a resin or/and an elastomer as a main component thereof; or/and a thermoplastic resin having a polar group or/and an elastomer having the polar group. At least one kind of an anion-containing salt, having a fluoro group and a sulfonyl group, is added to the polymer composition without intermediary of a medium consisting of a low-molecular-weight polyether-containing compound or a low-molecular-weight polar compound whose number-average molecular weight is not more than 5000. The present invention also provides a composition, for a conductive roller or the like, containing polymer components and the polymeric-type antistatic agent dispersed in the polymer components.

Abstract: The present invention provides a polymeric-type antistatic agent containing a polymer composition consisting of a polymeric-type antistatic agent containing a resin or/and an elastomer as a main component thereof; or/and a thermoplastic resin having a polar group or/and an elastomer having the polar group. At least one kind of an anion-containing salt, having a fluoro group and a sulfonyl group, is added to the polymer composition without intermediary of a medium consisting of a low-molecular-weight polyether-containing compound or a low-molecular-weight polar compound whose number-average molecular weight is not more than 5000. The present invention also provides a composition, for a conductive roller or the like, containing polymer components and the polymeric-type antistatic agent dispersed in the polymer components.

Abstract: The present invention provides a polymeric-type antistatic agent containing a polymer composition consisting of a polymeric-type antistatic agent containing a resin or/and an elastomer as a main component thereof; or/and a thermoplastic resin having a polar group or/and an elastomer having the polar group. At least one kind of an anion-containing salt, having a fluoro group and a sulfonyl group, is added to the polymer composition without intermediary of a medium consisting of a low-molecular-weight polyether-containing compound or a low-molecular-weight polar compound whose number-average molecular weight is not more than 5000. The present invention also provides a composition, for a conductive roller or the like, containing polymer components and the polymeric-type antistatic agent dispersed in the polymer components.

Abstract: There is provided a rubber composition capable of producing a tire which improves rolling resistance performance, wet skid performance and drivability of a vehicle in good balance, and a tire having a tread comprising thereof. A rubber composition comprising 30 to 150 parts by weight of the total of (1) silica with a nitrogen adsorption specific area of 100 m2/g or less and (2) silica with a nitrogen adsorption specific area of 180 m2/g or more based on 100 parts by weight of a rubber component, wherein the content of silica (1) and silica (2) satisfies the following formula, and a tire having a tread comprising thereof: [Content of silica (1)]×0.2?[content of silica (2)]?[content of silica (1)]×6.5.

Abstract: A polymer composition for a conductive roller composed of a rubber component whose main component is an epichlorohidrin rubber containing ethylene oxide at not less than 55 mol % nor more than 95 mol %. Thioureas are added to 100 g of the rubber component as a crosslinking agent at a rate not less than 0.014 mol nor more than 0.080 mol. In a compression set test of a vulcanized rubber described in JIS K6262, a compression set measured at 70° C. for 22-24 hours is less than 15%; and in a volume resistivity value test described in JIS K6911, a volume resistivity value measured at an applied voltage of 1000V is less than 107.5 [?·cm].

Abstract: An electroconductive roller including an electroconductive cellular material layer, comprised of a polyurethane composition, which has an average foamed cell diameter not more than 100 ?m and a variation ?D of the foamed cell diameter not more than 50 ?m. The electroconductive roller has a hardness variation ?Hs not more than 8 degrees and a circumferential non-uniformity index RMAX/RMIN in an electric resistance thereof not more than 1.3. The electroconductive cellular material layer is made of a thermosetting one-part polyurethane composition. And the polyurethane composition is cured instantly at a temperature not less than a thermosetting critical temperature for curing thereof, after it is foamed by a mechanical foaming method.

Abstract: Different from conventional so-called mix-type film capacitors involving several disadvantages, in which the dielectric layers consist of a combination of a dielectric plastic resin film and an insulating paper sheet, the invention provides an all-film oil-impregnated capacitor in which the dielectric layers consist only of a plastic resin film such as a biaxially oriented polypropylene resin film (OPP film) suitable for use in microwave ovens. The all-film capacitor of the invention can be obtained and has satisfactory properties only when prepared by using specified materials including the OPP film, aluminum foil and capacitor oil and under specified conditions relative to the dielectric tangent values and dielectric capacity values before and after impregnation with a capacitor oil as well as the conditions in the step of oil impregnation.

Abstract: 0.3-5.0 parts by weight of phenol resin, sulfur, and vulcanizing accelerator are added to 100 parts by weight of EPDM rubber. They are kneaded, and the EPDM rubber is vulcanized and molded. Generation of blooming can be suppressed without inhibiting the vulcanizing speed and the vulcanizing start timing.

Abstract: 0.3-5.0 parts by weight of phenol resin, sulfur, and vulcanizing accelerator are added to 100 parts by weight of EPDM rubber. They are kneaded, and the EPDM rubber is vulcanized and molded. Generation of blooming can be suppressed without inhibiting the vulcanizing speed and the vulcanizing start timing.

Abstract: Different from conventional so-called mix-type film capacitors involving several disadvantages, in which the dielectric layers consist of a combination of a dielectric plastic resin film and an insulating paper sheet, the invention provides an all-film oil-impregnated capacitor in which the dielectric layers consist only of a plastic resin film such as a biaxially oriented polypropylene resin film (OPP film) suitable for use in microwave ovens. The all-film capacitor of the invention can be obtained and has satisfactory properties only when prepared by using specified materials including the OPP film, aluminum foil and capacitor oil and under specified conditions relative to the dielectric tangent values and dielectric capacity values before and after impregnation with a capacitor oil as well as the conditions in the step of oil impregnation.

Abstract: A polymer composition for a conductive roller composed of a rubber component whose main component is an epichlorohidrin rubber containing ethylene oxide at not less than 55 mol % nor more than 95 mol %. Thioureas are added to 100 g of the rubber component as a crosslinking agent at a rate not less than 0.014 mol nor more than 0.080 mol. In a compression set test of a vulcanized rubber described in JIS K6262, a compression set measured at 70° C. for 22-24 hours is less than 15%; and in a volume resistivity value test described in JIS K6911, a volume resistivity value measured at an applied voltage of 1000V is less than 107.5[&OHgr;·cm].

Abstract: A polymer composition for a conductive roller composed of a rubber component whose main component is an epichlorohidrin rubber containing ethylene oxide at not less than 55 mol % nor more than 95 mol %. Thioureas are added to 100 g of the rubber component as a crosslinking agent at a rate not less than 0.014 mol nor more than 0.080 mol. In a compression set test of a vulcanized rubber described in JIS K6262, a compression set measured at 70° C. for 22-24 hours is less than 15%; and in a volume resistivity value test described in JIS K6911, a volume resistivity value measured at an applied voltage of 1000V is less than 107.5[&OHgr;·cm].

Abstract: The present invention provides a polymeric-type antistatic agent containing a polymer composition consisting of a polymeric-type antistatic agent containing a resin or/and an elastomer as a main component thereof; or/and a thermoplastic resin having a polar group or/and an elastomer having the polar group. At least one kind of an anion-containing salt, having a fluoro group and a sulfonyl group, is added to the polymer composition without intermediary of a medium consisting of a low-molecular-weight polyether-containing compound or a low-molecular-weight polar compound whose number-average molecular weight is not more than 5000. The present invention also provides a composition, for a conductive roller or the like, containing polymer components and the polymeric-type antistatic agent dispersed in the polymer components.

Abstract: A conductive roller including a core metal and a conductive elastic layer disposed on a peripheral surface of the core metal. The conductive roller has an electrostatic capacity not more than 50 pF at 100 Hz and an electric resistance not less than 105&OHgr; nor more than 109 &OHgr; at an applied voltage 1000V.

Abstract: A conductive layer of a conductive member for an image-forming apparatus is composed of a conductive polymer composition containing an ionic-conductive addition salt. The conductive polymer composition has a continuous phase and one or more uncontinuous phases including at least one first uncontinuous phase. The continuous phase and the uncontinuous phase form a sea-island structure. A salt capable of dissociating into cations and anions is unevenly distributed to the first uncontinuous phase. A polymer composing the first uncontinuous phase has a higher degree of affinity for the salt capable of dissociating into cations and anions than a polymer composing the continuous phase to prevent the salt (or the cations, the anions) from shifting out of the first uncontinuous phase or out of the polymer composition. The conductive polymer composition can contain melamine cyanurate so that it is flame-retardant.

Abstract: A conductive roller including at least one conductive elastic layer 1 formed of a polymer composition includes a main-component polymer not containing chlorine nor bromine and containing polyether or/and a cyan group; and an anion-containing salt having a fluoro group and a sulfonyl group. The anion-containing salt having the fluoro group and the sulfonyl group includes at least one salt selected from among a salt of bisfluoroalkylsulfonylimide, a salt of fluoroalkylsulfonic acid, and a salt of tris (fluoroalkylsulfonyl) methide.

Abstract: 0.3-5.0 parts by weight of phenol resin, sulfur, and vulcanizing accelerator are added to 100 parts by weight of EPDM rubber. They are kneaded, and the EPDM rubber is vulcanized and molded. Generation of blooming can be suppressed without inhibiting the vulcanizing speed and the vulcanizing start timing.

Abstract: 0.3-5.0 parts by weight of phenol resin, sulfur, and vulcanizing accelerator are added to 100 parts by weight of EPDM rubber. They are kneaded, and the EPDM rubber is vulcanized and molded. Generation of blooming can be suppressed without inhibiting the vulcanizing speed and the vulcanizing start timing.

Abstract: 0.3-5.0 parts by weight of phenol resin, sulfur, and vulcanizing accelerator are added to 100 parts by weight of EPDM rubber. They are kneaded, and the EPDM rubber is vulcanized and molded. Generation of blooming can be suppressed without inhibiting the vulcanizing speed and the vulcanizing start timing.

Abstract: A polymer composition for a conductive roller composed of a rubber component whose main component is an epichlorohidrin rubber containing ethylene oxide at not less than 55 mol % nor more than 95 mol %. Thioureas are added to 100 g of the rubber component as a crosslinking agent at a rate not less than 0.014 mol nor more than 0.080 mol. In a compression set test of a vulcanized rubber described in JIS K6262, a compression set measured at 70° C. for 22-24 hours is less than 15%; and in a volume resistivity value test described in JIS K6911, a volume resistivity value measured at an applied voltage of 1000V is less than 107.5[&OHgr;·cm].