Abstract: The oxidized aluminum pigment comprises not more than 95% by weight metallic aluminum, wherein the pigment is a flaky particle, and has a color travel from the hue angle range of about 50° to about 100° at the aspecular observation angle of 15° to a hue angle range of about 200° to about 270° at the aspecular observation angle of 110°. The oxidized aluminum pigment may be made by the steps of: providing a flaky aluminum pigment, and oxidizing the aluminum pigment in a water-in-oil emulsion comprising a surfactant in the presence of a base. The water-in-oil emulsion comprises a mixture of water dispersed in a hydrocarbon solvent. The aluminum pigment is predominantly in the hydrocarbon solvent during the oxidation step, and the amount of water in the mixture is in the range of about 5% to about 40% of the total weight of the emulsion.

Abstract: The oxidized aluminum pigment comprises not more than 95% by weight metallic aluminum, wherein the pigment is a flaky particle, and has a color travel from the hue angle range of about 50° to about 100° at the aspecular observation angle of 15° to a hue angle range of about 200° to about 270° at the aspecular observation angle of 110°. The oxidized aluminum pigment may be made by the steps of: providing a flaky aluminum pigment, and oxidizing the aluminum pigment in a water-in-oil emulsion comprising a surfactant in the presence of a base. The water-in-oil emulsion comprises a mixture of water dispersed in a hydrocarbon solvent. The aluminum pigment is predominantly in the hydrocarbon solvent during the oxidation step, and the amount of water in the mixture is in the range of about 5% to about 40% of the total weight of the emulsion.

Abstract: A three-dimensional structure of monodispersed particles, wherein the particles are formed from an emulsion polymerization comprising both hydrophobic and hydrophilic monomers.

Abstract: A pearlescent pigment, wherein the pigment is an inorganic material and the color of a homogeneous coating of the pigment, measured over a black background has a CIELAB hue angle, hab, from about 40 to about 320 degrees, wherein L* is from about 35 to about 80, and the chroma value is less than 5. A substrate is coated with iron oxide by oxidizing an iron salt to form a pigment. The pigment may be made by a process of coating iron oxide on a substrate by oxidizing an iron salt. During the coating of the iron oxide, the pH of the mixture is increased. The coating formed has a Fe(III)/Fe(II) ratio of greater than 2. The pigments may be used in a variety of applications including coating, ink, plastic, and cosmetic compositions.