Abstract: A method of producing artificial bio-soil aggregates based on foamed concrete for plant growth that can ensure sufficient moisture and plant nutrients for the habitat of plants in non-soil conditions; obtain a lightweight, durable, and deep soil layer, and continuously provide a favorable environment for plant growth. A paste is prepared by mixing cement with an admixture, such as ochre and burnt-furnace slag; foamed concrete is formed by adding foam bubbles with an appropriate foaming rate to said paste, thereby producing soil concrete. When the foamed concrete is used, a designated compressive strength can be ensured and a number of pore spaces are formed, which allow the air to be sucked and expelled therethrough and store moisture therein. Also, hydrogel that is incorporated into the foamed concrete may supply nutrients required for plant growth, improve pest resistance, and store and supply a large amount of water.

Abstract: An objective of the present invention is to provide a method of producing artificial bio-soil aggregates based on foamed concrete for plant growth that can ensure sufficient moisture and plant nutrients for the habitat of plants in non-soil conditions; obtain a lightweight, durable, and deep soil layer, and continuously provide a favorable environment for plant growth. To achieve the above objective, according to the present invention a paste is prepared by mixing cement with an admixture, such as ochre and burnt-furnace slag; foamed concrete is formed by adding foam bubbles with an appropriate foaming rate to said paste, thereby producing soil concrete. When the foamed concrete is used, a designated compressive strength can be ensured and a number of pore spaces are formed, which allow the air to be sucked and expelled therethrough and store moisture therein.

Abstract: The present invention relates to an alkali-activated binder which can be used as a binder for replacing cement, and more particularly, to an alkali-activated binder, and to mortar, concrete, concrete products, and wet loess paving material comprising the binder, in which inorganic sodium-free alkaline materials are contained to reduce the total amount of Na2O and K2O in concrete, thus improving the workability and the strength stability and inhibiting the alkali-aggregate reaction.

Abstract: The present invention relates to a cement-free alkali-activated binder. More particularly, the present invention relates to a cement-free alkali-activated binder having a novel combination ratio, which can improve the compressive strength of mortar and concrete in which the cement-free alkali-activated binder is used as a binding material instead of cement, and which can solve the low field applicability of mortar and concrete in terms of quick setting characteristics, fluidity loss, economic efficiency and the like, and to mortar or concrete comprising the same. The cement-free alkali-activated binder can improve field applicability by controlling the content and combination ratio of an alkali activator included in the cement-free alkali-activated binder, and can solve the problems of the toxicity of cement, the carbon dioxide (CO2) produced during the manufacturing of cement and the exhaustion of natural resources due to the production of cement.

Abstract: The present invention relates to an alkali-activated binder which can be used as a binder for replacing cement, and more particularly, to an alkali-activated binder, and to mortar, concrete, concrete products, and wet loess paving material comprising the binder, in which inorganic sodium-free alkaline materials are contained to reduce the total amount of Na2O and K2O in concrete, thus improving the workability and the strength stability and inhibiting the alkali-aggregate reaction.