Abstract: The present invention relates to an ultra-high strength, hot-dip galvanized steel sheet having excellent surface quality and coating adherence and to a method for manufacturing thereof, the ultra-high strength, hot-dip galvanized steel sheet comprising: 0.1-0.3% by weight carbon (C); 0.1-2.0% by weight silicon (Si); 0.005-1.5% by weight aluminum (Al); 1.5-3.5% by weight manganese (Mn); 0.04% by weight or less phosphorus (P) (excluding 0% by weight); 0.015% by weight or less sulphur (S) (excluding 0% by weight); 0.02% by weight or less nitrogen (N) (excluding 0% by weight); the balance being Fe; and other inevitable impurities, and further comprising 0.01 wt.% to 0.07 wt.% of at least one kind of element selected from the group consisting of bismuth (Bi), tin (Sn) and antimony (Sb).

Abstract: Provided is a high-strength hot-dip galvanized steel sheet having good surface quality and spot weldability. The high-strength hot-dip galvanized steel sheet includes a base steel sheet and a zinc plating layer formed on the base steel sheet. The base steel sheet includes carbon (C): 0.1% to 0.3%, silicon (Si): 0.5% to 2.5%, manganese (Mn): 2.0% to 8.0%, soluble aluminum (sol.Al): 0.001% to 0.5%, phosphorus (P): 0.04% or less (excluding 0%), sulfur (S): 0.015% or less, nitrogen (N): 0.02% or less, chromium (Cr): 0.01% to 0.7%, titanium (Ti): (48/14)*[N] % to 0.1%, and a balance of iron (Fe) and inevitable impurities. The base steel sheet has a microstructure comprising ferrite in an area fraction of 5% to 30%, austenite in an area fraction of 5% to 20%, bainite and martensite in an area fraction of 50% to 80%, and precipitates in an area fraction of 2% or less.

Abstract: Provided are a method for coating a steel plate with a metal and a metal-coated steel plate manufactured by the method. The method includes: heating powder of a first metal at a temperature lower than a softening temperature; heating a gas to a temperature of 200° C. to 600° C.; vacuum-ejecting the heated first metal powder together with the heated gas to form a metal coating layer; and forming a plating layer of a second metal on the metal coating layer.

Abstract: A high strength galvanized steel sheet having excellent surface qualities, plating adhesion, and formability is provided, wherein a galvanized layer is formed on a cold-rolled steel sheet comprising 0.1-0.3 wt % of C, 1-2.5 wt % of Si, 2.5-8 wt % of Mn, 0.001-0.5 wt % of sol. Al, at most 0.04 wt % of P, at most 0.015 wt % of S, at most 0.02 wt % of N (excluding 0 wt %), 0.1-0.7 wt % of Cr, at most 0.1 wt % of Mo, (48/14)*[N] to 0.1 wt % of Ti, 0.005-0.5 wt % of Ni, 0.01-0.07 wt % of Sb, at most 0.1 wt % of Nb, and at most 0.005 wt % of B, with the remainder being Fe and other inevitable impurities.

Abstract: The present invention relates to an ultra-high strength, hot-dip galvanized steel sheet having excellent surface quality and coating adherence and to a method for manufacturing thereof, the ultra-high strength, hot-dip galvanized steel sheet comprising: 0.1-0.3% by weight carbon (C); 0.1-2.0% by weight silicon (Si); 0.005-1.5% by weight aluminum (Al); 1.5-3.5% by weight manganese (Mn); 0.04% by weight or less phosphorus (P) (excluding 0% by weight); 0.015% by weight or less sulphur (S) (excluding 0% by weight); 0.02% by weight or less nitrogen (N) (excluding 0% by weight); the balance being Fe; and other inevitable impurities, and further comprising 0.01 wt.% to 0.07 wt.% of at least one kind of element selected from the group consisting of bismuth (Bi), tin (Sn) and antimony (Sb).