Abstract: A packaged additive for preparing a cementitious composition comprises a water-soluble paper container and at least one non-liquid additive packaged within the water-soluble paper container. A kit for preparing a hardenable cementitious composition comprises the packaged additive and a separate packaged base cementitious material. Also disclosed is a method for preparing a hardenable cementitious composition using the packaged additive and separate base cementitious material components of the kit, and a method for repairing a flaw in a cementitious structure using the hardenable cementitious composition prepared with the packaged additive and the separate base cementitious material.

Abstract: The present invention relates to an aqueous dispersion comprising (a) at least one (meth)acrylic polymer; (b) at least one vinyl acetate polymer selected from vinyl acetate homopolymer and vinyl acetate copolymers comprising in polymerized form vinyl acetate and ethylene; (c) water; and (d) optionally up to 50% by weight of an inorganic filler, based on the total weight of the aqueous dispersion, wherein the weight ratio of (meth)acrylic polymer(s) (a) to vinyl acetate polymer(s) (b) is from 70:30 to 30:70. The aqueous dispersion may be used as a joint compound or sealing compound.

Abstract: The present invention relates to an aqueous dispersion comprising (a) at least one (meth)acrylic polymer; (b) at least one vinyl acetate polymer selected from vinyl acetate homopolymer and vinyl acetate copolymers comprising in polymerized form vinyl acetate and ethylene; (c) water; and (d) optionally up to 50% by weight of an inorganic filler, based on the total weight of the aqueous dispersion, wherein the weight ratio of (meth)acrylic polymer(s) (a) to vinyl acetate polymer(s) (b) is from 70:30 to 30:70. The aqueous dispersion may be used as a joint compound or sealing compound.

Abstract: There is disclosed a method for preparing a thermoplastic elastomer, said method comprising:(I) mixing(A) a thermoplastic resin selected from the group consisting of a polyolefin and a poly(butylene terephthalate),(B) a diorganopolysiloxane having a plasticity of at least 30 and having an average of at least 2 alkenyl radicals in its molecule,(C) an organohydrido silicon compound which contains an average of at least 2 silicon-bonded hydrogen groups in its molecule,(D) optionally, a reinforcing filler and(E) a hydrozilation catalyst; and(II) dynamically curing said diorganopolysiloxane (B), wherein the amount of said diorganopolysiloxane (B) used is such that at least one property of the thermoplastic elastomer selected from tensile strength or elongation is at least 25% greater than the respective property for a corresponding simple blend wherein said diorganopolysiloxane is not cured.