Abstract: An method for producing a silicon ingot includes melting polycrystalline silicon in a crucible enclosed in a vacuum chamber to form a melt, generating a cusped magnetic field within the vacuum chamber, dipping a seed crystal into the melt, withdrawing the seed crystal from the melt to pull a single crystal that forms the silicon ingot, wherein the silicon ingot has a diameter greater than about 150 millimeters (mm), and simultaneously regulating a plurality of process parameters such that the silicon ingot has an oxygen concentration less than about 5 parts per million atoms (ppma). The plurality of process parameters include a wall temperature of the crucible, a transport of silicon monoxide (SiO) from the crucible to the single crystal, and an evaporation rate of SiO from the melt.

Abstract: An method for producing a silicon ingot includes melting polycrystalline silicon in a crucible enclosed in a vacuum chamber to form a melt, generating a cusped magnetic field within the vacuum chamber, dipping a seed crystal into the melt, withdrawing the seed crystal from the melt to pull a single crystal that forms the silicon ingot, wherein the silicon ingot has a diameter greater than about 150 millimeters (mm), and simultaneously regulating a plurality of process parameters such that the silicon ingot has an oxygen concentration less than about 5 parts per million atoms (ppma). The plurality of process parameters include a wall temperature of the crucible, a transport of silicon monoxide (SiO) from the crucible to the single crystal, and an evaporation rate of SiO from the melt.

Abstract: An method for producing a silicon ingot includes melting polycrystalline silicon in a crucible enclosed in a vacuum chamber to form a melt, generating a cusped magnetic field within the vacuum chamber, dipping a seed crystal into the melt, withdrawing the seed crystal from the melt to pull a single crystal that forms the silicon ingot, wherein the silicon ingot has a diameter greater than about 150 millimeters (mm), and simultaneously regulating a plurality of process parameters such that the silicon ingot has an oxygen concentration less than about 5 parts per million atoms (ppma). The plurality of process parameters include a wall temperature of the crucible, a transport of silicon monoxide (SiO) from the crucible to the single crystal, and an evaporation rate of SiO from the melt.

Abstract: An method for producing a silicon ingot includes melting polycrystalline silicon in a crucible enclosed in a vacuum chamber to form a melt, generating a cusped magnetic field within the vacuum chamber, dipping a seed crystal into the melt, withdrawing the seed crystal from the melt to pull a single crystal that forms the silicon ingot, wherein the silicon ingot has a diameter greater than about 150 millimeters (mm), and simultaneously regulating a plurality of process parameters such that the silicon ingot has an oxygen concentration less than about 5 parts per million atoms (ppma). The plurality of process parameters include a wall temperature of the crucible, a transport of silicon monoxide (SiO) from the crucible to the single crystal, and an evaporation rate of SiO from the melt.

Abstract: The present invention relates to a process for growing a single crystal silicon ingot, which contains an axially symmetric region having a predominant intrinsic point defect and which is substantially free of agglomerated intrinsic point defects in that region. The process comprising cooling the ingot from the temperature of solidification to a temperature of less than 800° C. and, as part of said cooling step, quench cooling a region of the constant diameter portion of the ingot having a predominant intrinsic point defect through the temperature of nucleation for the agglomerated intrinsic point defects for the intrinsic point defects which predominate in the region.

Abstract: A heat shield assembly is adapted for location within a crystal puller, with respect to a crucible, above molten source material held by the crucible in the puller. The heat shield assembly has a central opening sized and shaped for surrounding the ingot as the ingot is pulled from the molten material and is generally interposed between the ingot and the crucible as the ingot is pulled from the source material. The heat shield assembly comprises an outer reflector having an inner surface and an outer surface in generally opposed, spaced relationship with a side wall of the crucible, and an inner reflector located inward of the outer reflector. The inner reflector is constructed of a material having a low emissivity and has an outer surface in generally opposed relationship with the inner surface of the outer reflector.

Abstract: A crystal puller for growing monocrystalline silicon ingots according to the Czochralski method includes a housing and a crucible in the housing for containing molten silicon. The crucible has a side wall having a transmittance of at least about 80% generally throughout a light wavelength range of about 500 to about 2500 nanometers. A pulling mechanism is included for pulling a growing ingot upward from the molten silicon. In operation, polycrystalline silicon is charged to the crucible and the crucible is heated to melt the polycrystalline silicon for forming a molten silicon melt in the crucible. A seed crystal is then brought into contact with the molten silicon in the crucible and a monocrystalline silicon ingot is pulled up from the molten silicon.