Abstract: A speech recognition system that recognizes speech data is provided. The speech recognition system includes a speech recognition part that performs speech recognition of the speech data, and calculates a likelihood of the speech data with respect to a registered word that is pre-registered, a reliability judgment part that performs reliability judgment on the speech recognition based on the likelihood, and a judgment reference change processing part that changes a judgment reference for the reliability judgment, according to an utterance speed of the speech data.

Abstract: A speech recognition system that recognizes speech data is provided. The speech recognition system includes a speech recognition part that performs speech recognition of the speech data, and calculates a likelihood of the speech data with respect to a registered word that is pre-registered, a reliability judgment part that performs reliability judgment on the speech recognition based on the likelihood, and a judgment reference change processing part that changes a judgment reference for the reliability judgment, according to an utterance speed of the speech data.

Abstract: A high-strength, high damage-resistant rail made of 0.6 to 0.85 wt % C, 0.1 to 1.0 wt % Si, 0.5 to 1.5 wt % Mn, 0.035 wt % or less P, 0.040 wt % or less S, and 0.05 wt % or less Al, with the balance being Fe and inevitable impurities, and having corner and head side portions having a Brinell hardness of 341 to 405, and a head top portion in which a Brinell hardness of a site 20-mm distant from the central portion of the head top portion in a width direction is 341 to 405, and a hardness of the central portion of the head top portion is at least 10 lower in Brinell hardness than that of the site 20-mm distant from the central portion.

Abstract: The present invention provides a high-strength, high damage-resistant rail consisting essentially of 0.6 to 0.85 wt % of C, 0.1 to 1.0 wt % of Si, 0.5 to 1.5 wt % of Mn, 0.035 wt % or less of P, 0.040 wt % or less of S, and 0.

Abstract: A method for manufacturing a high strength rail with good toughness, comprises cooling a rail to Ar.sub.3 transformation point or less after hot rolling; heating said cooled rail at a temperature of an austenite temperature zone ranging from Ac.sub.3 transformation point to 950.degree. C.; and cooling the heated rail. The chemical composition of the rail consists of 0.50 to 0.85 wt. % C, 0.50 to 1.50 wt. % Mn, 0.035 wt. % S or less, 0.10 to 1.00 wt. % Si, 0.035 wt. % P or less, 0.050 wt. % Al or less and the balance of Fe and inevitable impurities.

Abstract: A method for heat-treating a steel rail head, which comprises: heating a steel rail head to the austenization temperature; then, cooling the rail head by means of a hot water jet until a surface temperature of the rail head decreases to a temperature not below 420.degree. C.; and then cooling the rail head by means of an air jet at least to the pearlite transformation temperature, thereby transforming the structure of a surface portion of the rail head into a uniform and fine pearlite structure. The above-described method includes a method in which the rail head is previously cooled by means of a water spray until the surface temperature of the rail head decreases to a temperature not below 530.degree. C. prior to the cooling of the rail head by means of the above-mentioned hot water jet.