Abstract: Hot melt adhesives with particularly high setting rates are obtained from the reaction products of polyisocyanates and hybroxypolyesters, the hydroxypolyester preferably being strictly aliphatic and containing at least 12 methylene groups in the polyester unit of diol and dicarboxylic acid.

Abstract: In corundum abrasive grain which is ceramically coated with ground frit, a binder and fine grain highly abrasive material for the purpose of improving adhesion of the abrasive grain in its processing to resin-bonded abrasives and their use in wet grinding. The fine grain material forms from 1 to 5 weight percent of the untreated corundum grain and ranges in size from 10 to 50 microns, which corresponds to from 1 to 10 percent of the average diameter of the initial grain.

Abstract: A linear saturated crystalline polyester of an acid moiety and a moiety of a dihydric alcohol, at least 40% of the acid moiety being a terephthalic acid moiety, said polyester containing moieties of 1,4-butanediol and 1,6-hexanediol, the ratio of the 1,4-butanediol moieties to 1,6-hexanediol moieties being 10:90 to 90:10; the use of such polyesters as a fusion coating mass, particularly in securing textile substances to a substrate.

Abstract: An improvement in a process for coating a substrate by a powder coating process wherein a polyester powder is applied to said substrate which improvement comprises using as the polyester powder a partially crystalline powder of a polyester condensation product of an acid component comprising an acid or ester of at least terephthalic acid and a diol component at least 50 molar percent of which is 1,4-butanediol; a polyester coating powder which is a partially crystalline polyester of an acid component at least part of which is an acid or ester of terephthalic acid and a diol component at least 50 molar percent of which is 1,4-butanediol, said powder having a glass transition temperature between -20.degree. and +50.degree. C., measured as the attenuation maximum in accordance with Deutsche Industrie Norm 53,445 a reduced n.sub.red viscosity of at least 0.

Abstract: An apparatus for the continuous manufacture of phenolic resin foam in an endless sheet which includes mixing means for expandable liquid phenolic resin with a blowing agent and an acid-containing curing agent, optionally with the addition of additives, and means for processing the mixture in a temperature-controllable double belt press. The apparatus also comprises a device for cooling the phenolic resin to a temperature of from about 8.degree. to about 15.degree. C.

Abstract: An improvement in a process for coating a substrate by a powder coating process wherein a polyester powder is applied to said substrate which improvement comprises using as the polyester powder a partially crystalline powder of a polyester condensation product of an acid component comprising an acid or ester of at least terephthalic acid and a diol component at least 50 molar percent of which is 1,4-butanediol; a polyester coating powder which is a partially crystalline polyester of an acid component at least part of which is an acid or ester of terephthalic acid and a diol component at least 50 molar percent of which is 1,4-butanediol, said powder having a glass transition temperature between -20.degree. and +50.degree. C., measured as the attenuation maximum in accordance with Deutsche Industrie Norm 53,445 a reduced n.sub.red viscosity of at least 0.

Abstract: An apparatus for the continuous manufacture of phenolic resin foam in an endless sheet which includes means for mixing expandable liquid phenolic resin with a blowing agent and an acid-containing curing agent, optionally with the addition of additives, and means for processing the mixture in a temperature-controllable double belt press. The apparatus also comprises a device for cooling the phenolic resin to a temperature of from about 8 to about 15.degree. C.