Abstract: A method for the manufacture of dense-sintered glass-ceramic shaped objects which have a coefficient of thermal expansion, .alpha., of -0.5.times.10.sup.-6 /K to 1.8.times.10.sup.-6 /K in the range between 20.degree. C. and 700.degree. C. whereby ceramizable glass powder and/or glass-ceramic powder from the system Li.sub.2 O-Al.sub.2 O.sub.3 -SiO.sub.2 is slip-cast by means of porous molds, dried, pretempered if necessary at temperatures up to 600.degree. C., vitrified and then sintered until the sintering temperature is reached up to relative densities of greater than 0.96 and ceramized, and whereby the glass powder and/or the glass ceramic-powder is prepared in a first grain size fraction of less than 63 .mu.m, in particular less than 45 .mu.m, and in a second grain size fraction of less than 7 .mu.m, in a ratio of the fractions to one another between 2:1 and 4:1, to form a stable, pourable slurry.