Abstract: A short fiber and continuous filament composite yarn having a high grade cotton spun yarn-like soft touch, satisfactory resilience, and uniform appearance, including a core portion formed by a plurality of cold drawn, non-crimped individual filaments substantially in the form of a bundle and a peripheral portion formed around the core portion and comprising a plurality of cold drawn-cut, non-crimped short fibers having a smaller shrinkage in boiling water, and optionally, a lower denier than those of the individual filaments, random portions of the short fibers being penetrated into the bundle of the individual filaments and intertwined with the individual filaments, and other portions of the short fibers forming a plurality of loops projecting in the form of waves having different wave heights, from the core portion toward the outside thereof to form multilayered loop structures around the core portion.

Abstract: A thermally improved polyester weft yarn is provided by melt-spinning a blend of a polyethylene terephthalate polymer and a small amount of polymer having a glass transition temperature of at least 10.degree. C. higher than that of the polyethylene terephthalate polymer. The yarn has a break elongation of 70% to 200% and a dry heat shrinkage of +5% to -2%, and is capable of withstanding a severe heat-treatment, for example, at 245.degree. C. for 2 minutes during dipping and curing process of a tire cord fabric comprising the same. Even after such heat-treatment, the yarn shows a residual break elongation of more than 60%. Thus, the weft yarn extends uniformly, without breakage, to a toroidal shape during a tire building process, keeping warp cords at a equi-distance relation. A tire cord fabric comprising the weft yarn of the invention finds its use as the carcass in the form of single ply in a radial tire.