Abstract: The present invention relates to an Ni-based superalloy for hot forging, containing, in terms of % by mass, C: more than 0.001% and less than 0.100%, Cr: 11% or more and less than 19%, Co: more than 5% and less than 25%, Fe: 0.1% or more and less than 4.0%, Mo: more than 2.0% and less than 5.0%, W: more than 1.0% and less than 5.0%, Nb: 0.3% or more and less than 4.0%, Al: more than 3.0% and less than 5.0%, Ti: more than 1.0% and less than 3.0%, and Ta: 0.01% or more and less than 2.0%, with the balance being unavoidable impurities and Ni, in which the component composition satisfies the following two relationships: 3.5?([Ti]+[Nb]+[Ta])/[Al]×10<6.5 and 9.5?[Al]+[Ti]+[Nb]+[Ta]<13.0.

Abstract: The present invention relates to a method for producing a precipitation strengthened Ni-based superalloy material having a predetermined composition, containing a blooming forging step of performing a forging at a temperature range of from Ts to Tm and performing an air cooling to form a billet having an average crystal grain size of #1 or more, an overaging thermal treatment step of heating and holding the billet at a temperature range of from Ts to Ts+50° C. and slowly cooling it to a temperature of Ts or lower, and a crystal grain fining forging step of performing another forging at a temperature range of from Ts?150° C. to Ts and performing another air cooling, in which Ts is from 1,030° C. to 1,100° C., and an overall average crystal grain size is #8 or more after the crystal grain fining forging step.

Abstract: The present invention relates to a method for producing a precipitation strengthened Ni-based superalloy material having a predetermined composition, containing a blooming forging step of performing a forging at a temperature range of from Ts to Tm and performing an air cooling to form a billet having an average crystal grain size of #1 or more, an overaging thermal treatment step of heating and holding the billet at a temperature range of from Ts to Ts+50° C. and slowly cooling it to a temperature of Ts or lower, and a crystal grain fining forging step of performing another forging at a temperature range of from Ts?150° C. to Ts and performing another air cooling, in which Ts is from 1,030° C. to 1,100° C., and an overall average crystal grain size is #8 or more after the crystal grain fining forging step.

Abstract: The present invention relates to an Ni-based superalloy for hot forging, containing, in terms of % by mass, C: more than 0.001% and less than 0.100%, Cr: 11% or more and less than 19%, Co: more than 5% and less than 25%, Fe: 0.1% or more and less than 4.0%, Mo: more than 2.0% and less than 5.0%, W: more than 1.0% and less than 5.0%, Nb: 2.0% or more and less than 4.0%, Al: more than 3.0% and less than 5.0%, and Ti: more than 1.0% and less than 3.0%, with the balance being unavoidable impurities and Ni, in which the component composition satisfies the following two relationships: 3.5?([Ti]+[Nb])/[Al]×10<6.5 and 9.5?[Al]+[Ti]+[Nb]<13.0.

Abstract: The present invention relates to a method for producing a precipitation strengthened Ni-based superalloy material having a predetermined composition, containing a blooming forging step of performing a forging at a temperature range of from Ts to Tm and performing an air cooling to form a billet having an average crystal grain size of #1 or more, an overaging thermal treatment step of heating and holding the billet at a temperature range of from Ts to Ts+50° C. and slowly cooling it to a temperature of Ts or lower, and a crystal grain fining forging step of performing another forging at a temperature range of from Ts?150° C. to Ts and performing another air cooling, in which Ts is from 1,030° C. to 1,100° C., and an overall average crystal grain size is #8 or more after the crystal grain fining forging step.

Abstract: The present invention relates to a method for producing a precipitation strengthened Ni-based superalloy material having a predetermined composition, containing a blooming forging step of performing a forging at a temperature range of from Ts to Tm and performing an air cooling to form a billet having an average crystal grain size of #1 or more, an overaging thermal treatment step of heating and holding the billet at a temperature range of from Ts to Ts+50° C. and slowly cooling it to a temperature of Ts or lower, and a crystal grain fining forging step of performing another forging at a temperature range of from Ts?150° C. to Ts and performing another air cooling, in which Ts is from 1,030° C. to 1,100° C., and an overall average crystal grain size is #8 or more after the crystal grain fining forging step.

Abstract: The present invention relates to an Ni-based superalloy for hot forging, containing, in terms of % by mass, C: more than 0.001% and less than 0.100%, Cr: 11% or more and less than 19%, Co: more than 5% and less than 25%, Fe: 0.1% or more and less than 4.0%, Mo: more than 2.0% and less than 5.0%, W: more than 1.0% and less than 5.0%, Nb: 2.0% or more and less than 4.0%, Al: more than 3.0% and less than 5.0%, and Ti: more than 1.0% and less than 3.0%, with the balance being unavoidable impurities and Ni, in which the component composition satisfies the following two relationships: 3.5?([Ti]+[Nb])/[Al]×10<6.5 and 9.5?[Al]+[Ti]+[Nb]<13.0.

Abstract: The present invention relates to an Ni-based superalloy for hot forging, containing, in terms of % by mass, C: more than 0.001% and less than 0.100%, Cr: 11% or more and less than 19%, Co: more than 5% and less than 25%, Fe: 0.1% or more and less than 4.0%, Mo: more than 2.0% and less than 5.0%, W: more than 1.0% and less than 5.0%, Nb: 0.3% or more and less than 4.0%, Al: more than 3.0% and less than 5.0%, Ti: more than 1.0% and less than 3.0%, and Ta: 0.01% or more and less than 2.0%, with the balance being unavoidable impurities and Ni, in which the component composition satisfies the following two relationships: 3.5?([Ti]+[Nb]+[Ta])/[Al]×10<6.5 and 9.5?[Al]+[Ti]+[Nb]+[Ta]<13.0.