Abstract: The invention is a method of treating, restoring or sealing a surface comprising applying an emulsion comprising a latex polymer, a cationic emulsifier, and optionally a recycling agent to the surface to wet the surface and depositing a surface treatment layer on the surface, wherein the depositing step occurs while the surface is wetted. The invention also includes a surface pretreatment composition comprising water, at least one acrylic latex polymer, an aromatic recycling agent, and at least one cationic emulsifier. Furthermore, the invention includes the surface resulting from the application of the emulsion used in the invention and concentrated emulsions for use with the surface treatment composition.

Abstract: A composition for rejuvenating asphalt pavement according to the present invention comprises an asphalt binder, water, a cationic surfactant, a recycling agent, and a cationic, co-agglomerated styrene butadiene rubber latex, which includes sulfur and a vulcanizing agent. The composition is also useful as a scrub seal, fog seal, sand seal as well as for crack filling and the prevention of reflective cracking. The inventive composition may be used in emulsions with different setup times. The invention also includes a method for treatment of aged and cracked asphalt by application of the disclosed compositions.

Abstract: A composition for rejuvenating asphalt pavement according to the present invention comprises an asphalt binder, water, a cationic surfactant, a recycling agent, and a cationic, co-agglomerated styrene butadiene rubber latex, which includes sulfur and a vulcanizing agent. The composition is also useful as a scrub seal, fog seal, sand seal as well as for crack filling and the prevention of reflective cracking. The inventive composition may be used in emulsions with different setup times. The invention also includes a method for treatment of aged and cracked asphalt by application of the disclosed compositions.

Abstract: The invention is a product, comprising a substrate and a film that limits the transmission of water vapor comprising a polymer derived from one or more nonionic monomers polymerized in the presence of at least one nonionic surfactant and in the absence of ionic surfactants. The cloud temperature of the at least one nonionic surfactant is preferably less than the polymerization temperature. The nonionic surfactant is preferably an alkylene oxide (EO)m(PO)n adduct of an alkyl alcohol, alkylbenzene alcohol or dialkylbenzene alcohol, wherein (m+n)?14. The invention includes a dispersion formed by polymerizing nonionic monomers at a polymerization temperature in the presence of at least one nonionic surfactant with a cloud temperature less than the polymerization temperature; a water vapor barrier composition; a film formed from the dispersion; a method of making the dispersion; a method of making a film; and a method of reducing the ability of water vapor to be transmitted with respect to a substrate.

Abstract: The invention is a dispersion essentially free of ionic surfactants comprising one or more copolymerizable monomers and a nonionic surfactant comprising alkylene oxide adduct of an alkyl alcohol, alkylbenzene alcohol or dialkylbenzene alcohol wherein the alkylene oxide includes one or more of ethylene oxide (EO)m and propylene oxide (PO)n, wherein (m+n)?14. The invention also includes an aqueous polymer dispersion essentially free of ionic surfactants comprising polymer particles, water, and a nonionic surfactant comprising an alkylene oxide adduct of an alkyl alcohol, alkylbenzene alcohol or dialkylbenzene alcohol wherein the alkylene oxide includes one or more of ethylene oxide (EO)m and propylene oxide (PO)n, wherein (m+n)?14, wherein the polymer particles are derived from one or more nonionic monomers and dispersed in the water and the nonionic surfactant is entrained in said polymer particles.

Abstract: The invention is a method of producing an essentially electrically neutral polymer dispersion, comprising a polymerizing one or more monomers in the presence of a nonionic surfactant, wherein the polymerization preferably occurs in the absence of ionic surfactants. The invention also includes methods of producing positively or negatively charged polymer dispersions comprising producing the essentially nonionic polymer dispersion and further adding a cationically-charged or anionically-charged surfactant or electrolyte. The invention further includes dispersions produced by the methods of the invention and polymer films and powders produced from these dispersions.

Abstract: A method of forming a composition comprising adding at least one first compound that is at least one of an alkali metal salt, an ammonium salt, an alkali metal hydroxide, or an ammonium hydroxide and at least one second compound that is at least one of a Group IIA salt, a Group IIIA salt, a Group IIIB salt, a copper salt, a zinc salt, a cadmium salt, a manganese salt, an iron salt, a cobalt salt, or a nickel salt to a latex. This method allows for the formation of nanoparticles in the composition.

Abstract: A method of forming a composition comprising adding at least one first compound that is at least one of an alkali metal salt, an ammonium salt, an alkali metal hydroxide, or an ammonium hydroxide and at least one second compound that is at least one of a Group IIA salt, a Group IIIA salt, a Group IIIB salt, a copper salt, a zinc salt, a cadmium salt, a manganese salt, an iron salt, a cobalt salt, or a nickel salt to a latex. This method allows for the formation of nanoparticles in the composition.

Abstract: A composition for rejuvenating asphalt pavement according to the present invention comprises an asphalt binder, water, a cationic surfactant, a recycling agent, and a cationic, co-agglomerated styrene butadiene rubber latex, which includes sulfur and a vulcanizing agent. The composition is also useful as a scrub seal, fog seal, sand seal as well as for crack filling and the prevention of reflective cracking. The inventive composition may be used in emulsions with different setup times. The invention also includes a method for treatment of aged and cracked asphalt by application of the disclosed compositions.

Abstract: An asphalt-based, cold paving/coating formulation that provides increased flexibility with respect to the choice of aggregate types, asphalt emulsion types, type and amount of the surfactants used to produce the asphalt emulsion, asphalt emulsion pH's and application temperature's than conventional cold paving/coating formulations while providing good mix times and curing behavior. The asphalt-based formulation can be formed by mixing water; an asphalt emulsion; at least one first compound in aqueous solution selected from the group consisting of alkali metal salts, alkali metal hydroxides, ammonium salts, and ammonium hydroxide; at least one second compound in aqueous solution selected from the group consisting of Group IIA salts, Group IIIA salts, Group IIIB salts, copper salts, zinc salts, cadmium salts, manganese salts, iron salts, cobalt salts, and nickel salts; and optionally aggregate. Also, a method of preparing an asphalt-based formulation using these components.

Abstract: A polystyrene seed latex composition is provided having a total emulsion polymer content of from 0.2 to 2.0 weight percent and a particle diameter less than 150 Å. The seed latex is produced on a continuous basis by feeding to a continuous stirred reactor an emulsion stream and initiator stream. The feed streams are mixed in the stirred reactor at room temperature to produce the seed latex. Preferably, the initiator stream comprises a sodium formaldehyde sulfoxylate reducing agent. The amount of initiator charged into the continuous seed reactor is sufficient to complete both the seed and a subsequent continuous latex polymerization reaction.

Abstract: The present invention is a method of incorporating a water insoluble organic chemical into a styrene-butadiene rubber latex dispersion and the resulting styrene-butadiene rubber latex dispersion. A styrene-butadiene rubber latex dispersion is provided comprising an aqueous phase and a disperse phase, with the disperse phase including particles of styrene-butadiene rubber. An organic solvent that is miscible in water and the water insoluble organic chemical are added together to the styrene-butadiene rubber latex dispersion. The addition of the water-miscible organic solvent allows the water insoluble organic chemical to pass from the aqueous phase into the disperse phase thus limiting separation of the water insoluble organic chemical from the latex dispersion. The resulting SBR latex has increased properties over conventional latices that use the same amount of the water insoluble organic chemical but that do not include the water-miscible organic solvent.

Abstract: An asphalt-based, cold paving/coating formulation that provides increased flexibility with respect to the choice of aggregate types, asphalt emulsion types, type and amount of the surfactants used to produce the asphalt emulsion, asphalt emulsion pH's and application temperature's than conventional cold paving/coating formulations while providing good mix times and curing behavior. The asphalt-based formulation can be formed by mixing water; an asphalt emulsion; at least one first compound in aqueous solution selected from the group consisting of alkali metal salts, alkali metal hydroxides, ammonium salts, and ammonium hydroxide; at least one second compound in aqueous solution selected from the group consisting of Group IIA salts, Group IIIA salts, Group IIIB salts, copper salts, zinc salts, cadmium salts, manganese salts, iron salts, cobalt salts, and nickel salts; and optionally aggregate. Also, a method of preparing an asphalt-based formulation using these components.

Abstract: A composition for rejuvenating asphalt pavement according to the present invention comprises an asphalt binder, water, a cationic surfactant, a recycling agent, and a cationic, co-agglomerated styrene butadiene rubber latex, which includes sulfur and a vulcanizing agent. The composition is also useful as a scrub seal, fog seal, sand seal as well as for crack filling and the prevention of reflective cracking. The inventive composition may be used in emulsions with different setup times. The invention also includes a method for treatment of aged and cracked asphalt by application of the disclosed compositions.

Abstract: The present invention is a method of incorporating a water insoluble organic chemical into a styrene-butadiene rubber latex dispersion and the resulting styrene-butadiene rubber latex dispersion. A styrene-butadiene rubber latex dispersion is provided comprising an aqueous phase and a disperse phase, with the disperse phase including particles of styrene-butadiene rubber. An organic solvent that is miscible in water and the water insoluble organic chemical are added together to the styrene-butadiene rubber latex dispersion. The addition of the water-miscible organic solvent allows the water insoluble organic chemical to pass from the aqueous phase into the disperse phase thus limiting separation of the water insoluble organic chemical from the latex dispersion. The resulting SBR latex has increased properties over conventional latices that use the same amount of the water insoluble organic chemical but that do not include the water-miscible organic solvent.

Abstract: The present invention relates to the coagglomeration of random vinyl substituted aromatic/C4-C6 conjugated diolefin polymers With sulfur. Said coagglomerate is storage stable and easily blended with asphalt under a variety of mixing conditions. Further, polymer/asphalt blends prepared with the sulfur coagglomerated polymers show improved storage stability against phase separation.

Abstract: The present invention relates to the coagglomeration of random vinyl substituted aromatic/C4-C6 conjugated diolefin polymers with sulfur. Said coagglomerate is storage stable and easily blended with asphalt under a variety of mixing conditions. Further, polymer/asphalt blends prepared with the sulfur coagglomerated polymers show improved storage stability against phase separation.

Abstract: The present invention relates to the coagglomeration of random vinyl substituted aromatic/C.sub.4 -C.sub.6 conjugated diolefin polymers with sulfur. Said coagglomerate is storage stable and easily blended with asphalt under a variety of mixing conditions. Further, polymer/asphalt blends prepared with the sulfur coagglomerated polymers show improved storage stability against phase separation.

Abstract: The present invention relates to random vinyl substituted aromatic/C.sub.4 -C.sub.6 conjugated diolefin polymer modified asphalt mixtures wherein the modifier is a keto-containing amide such as diacetone acrylamide (DAAM), an oxazoline containing copolymer, and an ethoxylated trimethylolpropane triacrylate.

Abstract: The present invention relates to a method for improving the compatibility of random vinyl substituted aromatic/C.sub.4 -C.sub.6 conjugated diolefin polymer/asphalt mixtures comprising adding a modifier to said random vinyl substituted aromatic/C.sub.4 -C.sub.6 conjugated diolefin polymer/asphalt mixture selected from the group consisting of:(a) polymers containing an epoxy functionality(b) polymers containing a carboxyl functionality(c) monomers, oligomers, and polymers containing an amine functionality;(d) monomers, oligomers, and polymers containing an ester functionality; or mixtures thereof.