Abstract: The present invention provides a glass fiber-reinforced thermoplastic resin composition in which a particular relationship is satisfied between the glass fiber content (W (parts by weight)) and the melt viscosity (?) of the thermoplastic resin composition at molding temperature as determined at a shear rate of 1,000 sec?1. According to the present invention, there can be obtained a glass fiber-reinforced thermoplastic resin having increased strength and rigidity and excellent in practical characteristics such as impact resistance and antifreeze liquid resistance. In addition, molded articles obtained by injection-molding the composition are available as components having reduced anisotropies of mechanical characteristics and mold shrinkage factor.

Abstract: The present invention provides a process for producing a polyamide resin composition, comprising the steps of: impregnating a molten polyamide resin into glass fiber rovings; taking off the polyamide-impregnated glass fiber rovings during twisting thereof to provide a strand; and pelletizing the strand to provide a resin composition, wherein a melt viscosity of the polyamide resin is set to fall within a particular range. According to the present invention, there can be provided a process for producing a glass fiber-reinforced polyamide resin composition excellent in the impregnation of the resin into the glass fiber rovings and capable of offering a molding excellent in mechanical strength and color tone.

Abstract: The present invention provides a glass fiber-reinforced thermoplastic resin composition in which a particular relationship is satisfied between the glass fiber content (W (parts by weight)) and the melt viscosity (?) of the thermoplastic resin composition at molding temperature as determined at a shear rate of 1,000 sec?1. According to the present invention, there can be obtained a glass fiber-reinforced thermoplastic resin having increased strength and rigidity and excellent in practical characteristics such as impact resistance and antifreeze liquid resistance. In addition, molded articles obtained by injection-molding the composition are available as components having reduced anisotropies of mechanical characteristics and mold shrinkage factor.

Abstract: The invention provides a long fiber filler reinforced resin pellet composed of a long fiber filler and a thermoplastic resin blend. In the pellet, the long fiber filler is aligned to form a spiral with a central axis along the longitudinal direction of the pellet, and the pellet has a skin layer part with a lower content of the long fiber filler, and a core part with a higher content of the long fiber filler, thereby the cross-section of the core part is in a range of 30% to 70% of the cross-section of the pellet. The thermoplastic resin blend in the pellet is composed of polyphenylene ether and a thermoplastic resin other than polyphenylene ether.

Abstract: The present invention provides a process for producing a polyamide resin composition, comprising the steps of: impregnating a molten polyamide resin into glass fiber rovings; taking off the polyamide-impregnated glass fiber rovings during twisting thereof to provide a strand; and pelletizing the strand to provide a resin composition, wherein a melt viscosity of the polyamide resin is set to fall within a particular range. According to the present invention, there can be provided a process for producing a glass fiber-reinforced polyamide resin composition excellent in the impregnation of the resin into the glass fiber rovings and capable of offering a molding excellent in mechanical strength and color tone.