Abstract: A method for manufacturing a photochromic lens includes: a step of injecting a polymerizable composition through an injection part in an injection molding apparatus and filling a gap with the polymerizable composition through a space; a step of heating the filled polymerizable composition to be polymerized and cured and forming a photochromic layer on a resin substrate; and a step of taking out a resulting laminate composed of the resin substrate and the photochromic layer, in which the polymerizable composition includes an isocyanate compound, a thiol compound, a polyol compound, and a photochromic compound.

Abstract: A polymerizable composition for an optical material of the present invention includes (A) a compound of which pKa value is 1 to 9, (B) a di- or higher functional iso(thio)cyanate compound, and (C) a di- or higher functional active hydrogen compound.

Abstract: A polymerizable composition for an optical material containing two or more different monomers for an optical material, and a polymerization catalyst, in which at least one of the two or more different monomers for an optical material is an isocyanate compound containing an aromatic ring, a content of the polymerization catalyst with respect to a total of 100 parts by mass of the two or more different monomers for an optical material is from 0.010 parts by mass to 0.50 parts by mass, and the viscosity measured by a B-type viscometer at 25° C. and 60 rpm is from 10 mPa·s to 1,000 mPa·s.

Abstract: A polymerizable composition for optical material including two or more different monomers for optical material and a polymerization catalyst, in which the content of the polymerization catalyst relative to the total amount of the monomers for optical material is from 0.1150 to 0.2000 parts by mass, the viscosity of the polymerizable composition for optical material is from 10 mPa·s to 1000 mPa·s as measured with a B-type viscometer at 20° C. and 60 rpm, and at least one of the two or more different monomers for optical material is an episulfide compound.

Abstract: A polymerizable composition for an optical material containing two or more different monomers for an optical material, and a polymerization catalyst, in which at least one of the two or more different monomers for an optical material is an isocyanate compound containing an aromatic ring, a content of the polymerization catalyst with respect to a total of 100 parts by mass of the two or more different monomers for an optical material is from 0.010 parts by mass to 0.50 parts by mass, and the viscosity measured by a B-type viscometer at 25° C. and 60 rpm is from 10 mPa·s to 1,000 mPa·s.

Abstract: A polymerizable composition for an optical material containing two or more different monomers for an optical material, and a polymerization catalyst, in which at least one of the two or more different monomers for an optical material is an isocyanate compound containing no aromatic rings, a content of the polymerization catalyst with respect to a total of 100 parts by mass of the two or more different monomers for an optical material is from more than 0.05 parts by mass to 2.0 parts by mass, and a viscosity measured by a B-type viscometer at 25° C. and 60 rpm is from 10 mPa·s to 1,000 mPa·s.

Abstract: A polymerizable composition for an optical material containing two or more different monomers for an optical material, and a polymerization catalyst, in which at least one of the two or more different monomers for an optical material is an isocyanate compound containing no aromatic rings, a content of the polymerization catalyst with respect to a total of 100 parts by mass of the two or more different monomers for an optical material is from more than 0.05 parts by mass to 2.0 parts by mass, and a viscosity measured by a B-type viscometer at 25° C. and 60 rpm is from 10 mPa·s to 1,000 mPa·s.

Abstract: A polythiol composition includes a polythiol compound (A) including at least one of 4,8-dimercaptomethyl-1,11-dimercapto-3,6,9-trithiaundecane, 4,7-dimercaptomethyl-1,11-dimercapto-3,6,9-trithiaundecane, or 5,7-dimercaptomethyl-1,11-dimercapto-3,6,9-trithiaundecane, and a polythiol compound (B) that is 4-mercaptomethyl-1,8-dimercapto-3,6-dithiaoctane.

Abstract: A polymerizable composition for an optical material containing two or more different monomers for an optical material, and a polymerization catalyst, in which at least one of the two or more different monomers for an optical material is an isocyanate compound containing an aromatic ring, a content of the polymerization catalyst with respect to a total of 100 parts by mass of the two or more different monomers for an optical material is from 0.010 parts by mass to 0.50 parts by mass, and the viscosity measured by a B-type viscometer at 25° C. and 60 rpm is from 10 mPa·s to 1,000 mPa·s.

Abstract: A polymerizable composition for an optical material includes a compound represented by General Formula (1) and a polymerization reactive compound.

Abstract: An injection molding apparatus includes a substantially circular first substrate, a substantially circular second substrate disposed to face a surface of the first substrate, a fixing member which fixes a peripheral end portion of the first substrate and a peripheral end portion of the second substrate, and an injection portion which is provided in the fixing member and from which a composition is injected into a gap between the first substrate and the second substrate, in which a space connecting with the injection portion and the gap is provided in at least a part of a periphery of the gap, and a width of the space in a thickness direction is larger than a width of the gap in the thickness direction.

Abstract: In an optical material, a transmittance curve satisfies the following characteristics (1) and (2) and a hue in the CIE 1976 (L*, a*, b*) color space satisfies the following characteristic (3), (1) the transmittance curve has a maximum value of a transmittance at a wavelength of from 400 nm to 450 nm or from 520 nm to 570 nm, and a largest value of the transmittance at the wavelength of from 400 nm to 450 nm and a transmittance at from 520 nm to 570 nm are 50% or more, (2) the transmittance curve has a minimum value of a transmittance at a wavelength of from 470 nm to 500 nm, and the minimum value is 40% or less, and (3) in the hue in the CIE 1976 (L*, a*, b*) color space, a* is from 2.5 to 5.5 and b* is from 5 to 25.

Abstract: A process for producing a plastic lens includes a step of stirring and mixing a solution including a polymerization reactive compound in a preparation tank; a step of transferring the polymerizable composition obtained in the step from the preparation tank to a lens casting mold; a step of curing the polymerizable composition; and a step of obtaining a plastic lens molded product by separating the obtained resin from the lens casting mold. The step of transferring the polymerizable composition includes a step of re-mixing the polymerizable composition discharged from the preparation tank and injecting the polymerizable composition into the lens casting mold.

Abstract: A polymerizable composition for an optical material containing two or more different monomers for an optical material, and a polymerization catalyst, in which at least one of the two or more different monomers for an optical material is an isocyanate compound containing no aromatic rings, a content of the polymerization catalyst with respect to a total of 100 parts by mass of the two or more different monomers for an optical material is from more than 0.05 parts by mass to 2.0 parts by mass, and a viscosity measured by a B-type viscometer at 25° C. and 60 rpm is from 10 mPa·s to 1,000 mPa·s.

Abstract: A polymerizable composition for an optical material containing two or more different monomers for an optical material, and a polymerization catalyst, in which at least one of the two or more different monomers for an optical material is an isocyanate compound containing an aromatic ring, a content of the polymerization catalyst with respect to a total of 100 parts by mass of the two or more different monomers for an optical material is from 0.010 parts by mass to 0.50 parts by mass, and the viscosity measured by a B-type viscometer at 25° C. and 60 rpm is from 10 mPa·s to 1,000 mPa·s.

Abstract: There is provided a polymerizable composition for an optical material including a polyether-modified compound having a polyether group represented by General Formula (4) below, and a polymerization reactive compound. (In General Formula (4), R25 represents a linear or branched alkylene group having 1 to 20 carbon atoms, R26 represents a hydrogen atom, a linear or branched alkyl group having 1 to 20 carbon atoms, a linear or branched alkenyl group having 2 to 20 carbon atoms, or a linear or branched alkynyl group having 2 to 20 carbon atoms, a plurality of present R25's may be the same or different, and k is an integer equal to or more than 1.

Abstract: A polymerizable composition for an optical material includes a compound represented by General Formula (1) and a polymerization reactive compound.

Abstract: A process for producing a polymerizable composition for an optical material of the present invention includes a step of mixing (A) at least one kind of thiol compound having at least two mercapto groups, (B) a tin compound represented by general formula (1), and (C) at least one kind of isocyanate compound having at least two isocyanato groups, in which the polymerizable composition for an optical material obtained in the above step has a haze value of 0.05 or less.

Abstract: A polymerizable composition for an optical material of the present invention includes (A) a compound of which pKa value is 1 to 9, (B) a di- or higher functional iso(thio)cyanate compound, and (C) a di- or higher functional active hydrogen compound.

Abstract: A process for producing a plastic lens includes a step of stirring and mixing a solution including a polymerization reactive compound in a preparation tank; a step of transferring the polymerizable composition obtained in the step from the preparation tank to a lens casting mold; a step of curing the polymerizable composition; and a step of obtaining a plastic lens molded product by separating the obtained resin from the lens casting mold. The step of transferring the polymerizable composition includes a step of re-mixing the polymerizable composition discharged from the preparation tank and injecting the polymerizable composition into the lens casting mold.