Abstract: A process for preparing dicalcium silicate includes providing a starting material comprising calcium carbonate (CaCO3) and silicon dioxide (SiO2), wherein a molar ratio of calcium:silicon (C:S) is from 1.5:1 to 2.5:1. At least one of an inorganic alkali metal salt and an alkaline earth metal salt is added as a mineralizing agent to the starting material in an amount of from 0.5 wt.-% to 20 wt.-%, based on a total weight of the starting material. The starting material is reacted with the mineralizing agent in a gas atmosphere having a CO2 partial pressure of from 0.05 MPa to 0.2 MPa at a temperature of from 900° C. to 1100° C. so as to obtain a dicalcium silicate product. The dicalcium silicate product comprises a content of an unreacted starting material of <5 wt.-% and a total carbon content of <1.5 wt.-%, each based on a weight of the dicalcium silicate product.

Abstract: A process for preparing dicalcium silicate includes providing a starting material comprising calcium carbonate (CaCO3) and silicon dioxide (SiO2), wherein a molar ratio of calcium:silicon (C:S) is from 1.5:1 to 2.5:1. At least one of an inorganic alkali metal salt and an alkaline earth metal salt is added as a mineralizing agent to the starting material in an amount of from 0.5 wt.-% to 20 wt.-%, based on a total weight of the starting material. The starting material is reacted with the mineralizing agent in a gas atmosphere having a CO2 partial pressure of from 0.05 MPa to 0.2 MPa at a temperature of from 900° C. to 1100° C. so as to obtain a dicalcium silicate product. The dicalcium silicate product comprises a content of an unreacted starting material of <5 wt.-% and a total carbon content of <1.5 wt.-%, each based on a weight of the dicalcium silicate product.

Abstract: The invention relates to a monophase amorphous hydraulic binder containing silicon, calcium and oxygen atoms in an arrangement comprising silicate building units having an average connectedness of at least Q1, with none or a part of the calcium atoms being substituted for by a metal atom M[6]x+ sixfold or higher-coordinated with oxygen and/or none or no more than 45 atomic percent of the silicon atoms being substituted for by a metal atom M[4]y+ tetrahedrally coordinated with oxygen, the molar ratio of [CaO+(x/2)·(M[6]x+Ox/2)]:[SiO2+M[4]y+Oy/2] having a value of 0.2 to 1.5, and the binder having less than 3.5% by weight of water, as well as a mixture containing this binder.

Abstract: The invention relates to a monophase hydraulic binder containing silicon, calcium, oxygen and hydrogen atoms in an arrangement comprising silicate building units having an average connectedness of higher than Q1.5 and silanol groups, with none or a part of the calcium atoms being substituted for by a metal atom M[6]x+ sixfold or higher-coordinated with oxygen and/or none or a part of the silicon atoms being substituted for by a metal atom M[4]y+ tetrahedrally coordinated with oxygen, the molar ratio of [CaO+(x/2)·(M[6]x+Ox/2)]: [SiO2+M[4]y+Oy/2] having a value of 0.2 to 2.0, and the binder having an H2O content of 3.5% by weight to 20% by weight, as well as a mixture containing this binder.

Abstract: The invention relates to a monophase hydraulic binder containing silicon, calcium, oxygen and hydrogen atoms in an arrangement comprising silicate building units having an average connectedness of no more than Q1.5 and silanol groups, with none or a part of the calcium atoms being substituted for by a metal atom M[6]x+ sixfold or higher-coordinated with oxygen and/or none or a part of the silicon atoms being substituted for by a metal atom M[4]y+ tetrahedrally coordinated with oxygen, the molar ratio of [CaO+(x/2)·(M[6]x+Ox/2)]:[SiO2+M[4]y+Oy/2] having a value of 0.75 to 2.75, and the binder containing an H2O content of 3.5% by weight to 20% by weight, as well as a mixture containing this binder.

Abstract: The invention relates to a monophase amorphous hydraulic binder containing silicon, calcium and oxygen atoms in an arrangement comprising silicate building units having an average connectedness of at least Q1, with none or a part of the calcium atoms being substituted for by a metal atom M[6]x+ sixfold or higher-coordinated with oxygen and/or none or no more than 45 atomic percent of the silicon atoms being substituted for by a metal atom M[4]y+ tetrahedrally coordinated with oxygen, the molar ratio of [CaO+(x/2)·(M[6]x+Ox/2)]:[SiO2+M[4]y+Oy/2] having a value of 0.2 to 1.5, and the binder having less than 3.5% by weight of water, as well as a mixture containing this binder.

Abstract: A method for producing components including preparing an aqueous suspension of solids including calcium oxide CaO and silicon dioxide SiO2 with a molar ratio of Ca:Si that is between 0.5:1.0 and 2.5:1.0. Nanocrystalline C—S—H phases are produced by grinding the aqueous suspension and keeping its temperature at or below 100° C. The aqueous phase is separated out from the suspension to form a residue containing the nanocrystalline C—S—H phases. The residued is removed and a powdery product is made by drying the residue. A mold is filled with the powdery product and pressure is applied to form the component. The component is removed from the mold.

Abstract: The invention relates to a monophase hydraulic binder containing silicon, calcium, oxygen and hydrogen atoms in an arrangement comprising silicate building units having an average connectedness of higher than Q1.5 and silanol groups, with none or a part of the calcium atoms being substituted for by a metal atom M[6]x+ sixfold or higher-coordinated with oxygen and/or none or a part of the silicon atoms being substituted for by a metal atom M[4]Yy+ tetrahedrally coordinated with oxygen, the molar ratio of [CaO+(x/2) (M[6]x+Ox/2)]: [SiO2+M[4]y+Oy/2] having a value of 0.2 to 2.0, and the binder having an H2O content of 3.5% by weight to 20% by weight, as well as a mixture containing this binder.

Abstract: The invention relates to a monophase hydraulic binder containing silicon, calcium, oxygen and hydrogen atoms in an arrangement comprising silicate building units having an average connectedness of no more than Q1.5 and silanol groups, with none or a part of the calcium atoms being substituted for by a metal atom M[6]x+ sixfold or higher-coordinated with oxygen and/or none or a part of the silicon atoms being substituted for by a metal atom M[4]y+ tetrahedrally coordinated with oxygen, the molar ratio of [CaO+(x/2)·(M[6]x+Ox/2)]:[SiO2+M[4]y+Oy/2] having a value of 0.75 to 2.75, and the binder containing an H2O content of 3.5% by weight to 20% by weight, as well as a mixture containing this binder.

Abstract: A method for producing components including preparing an aqueous suspension of solids including calcium oxide CaO and silicon dioxide SiO2 with a molar ratio of Ca:Si that is between 0.5:1.0 and 2.5:1.0. Nanocrystalline C—S—H phases are produced by grinding the aqueous suspension and keeping its temperature at or below 100° C. The aqueous phase is separated out from the suspension to form a residue containing the nanocrystalline C—S—H phases. The residued is removed and a powdery product is made by drying the residue. A mold is filled with the powdery product and pressure is applied to form the component. The component is removed from the mold.