Abstract: Provided are a plated steel sheet and a method for manufacturing same, the plated steel sheet comprising: a base steel sheet; a Zn—Mg—Al plating layer provided on at least one surface of the base steel sheet; and an Fe—Al inhibition layer provided between the base steel sheet and the Zn—Mg—Al plating layer. The plating layer comprises, by weight %, 4 to 10% of Mg and 5.1-25% of Al and the remainder being Zn and unavoidable impurities with respect to components not including iron (Fe) diffused from the base steel sheet. The plating layer comprises a 24-50% MgZn2 phase in phase fraction. In the MgZn2 phase, an Al single phase is present in the ratio of 1-30% relative to the cross-sectional area of the total MgZn2 phase.

Abstract: A plated steel sheet having excellent fusion resistance, and a manufacturing method. therefor are provided. Provided is a hot forming plated steel sheet having a plated layer formed on one surface or the both surfaces of a base steel sheet and having excellent fusion resistance, wherein a surface layer portion of the plated layer is comprised of an hard alloy layer with a surface area ratio of 1% or more including hard alloy phases, the hard alloy layer having a thickness of 0.1-100 ?m, and a balance of a soft plating layer, wherein the hard alloy phases comprise Al, Zn, Mg, Si, Fe and a balance of unavoidable impurities, a sum of Al, Zn and Fe being 70 wt % or more on the basis of weight % thereof.