Abstract: A method of making soft, strong, high bulk tissue is disclosed. The method includes pre-conditioning a wet web by straining the wet web in the cross-machine direction prior to transferring the wet web to a throughdrying fabric. The pre-conditioned web provides improved sheet softness and conforms more readily to the surface contour of the throughdrying fabric, thereby creating greater caliper (bulk) in the resulting dried sheet. The bulk is maintained during a subsequent creping step by maintaining the dried sheet in registration with the throughdrying fabric when the dried sheet is applied to the surface of the creping cylinder.

Abstract: The present invention is directed to a bicomponent strengthening system and the paper webs produced with the bicomponent strengthening system. Through use of the strengthening system, paper webs may be produced in which the strength characteristics of the web may be specifically tailored. The first component of the system comprises a polymer having at least about 1.5 m-eq primary amine functionality per gram of polymer and a molecular weight of at least about 10,000 Daltons. The second component may be either a polymeric anionic compound or a polymeric aldehyde functional compound. For example, the polyamine polymer component may be a polyvinylamine or polysaccharide having primary amine functionality. In one embodiment, the second component may be a cationic polymeric aldehyde functional compound. For example, the second component may be a cationic glyoxylated polyacrylamide. In another embodiment, the second component may be a polymeric anionic compound comprising carboxy functionality.

Abstract: The present invention is directed to a bicomponent strengthening system and the paper webs produced with the bicomponent strengthening system. Through use of the strengthening system, paper webs may be produced in which the strength characteristics of the web may be specifically tailored. The first component of the system comprises a polymer having at least about 1.5 m-eq primary amine functionality per gram of polymer and a molecular weight of at least about 10,000 Daltons. The second component may be either a polymeric anionic compound or a polymeric aldehyde functional compound. For example, the polyamine polymer component may be a polyvinylamine or polysaccharide having primary amine functionality. In one embodiment, the second component may be a cationic polymeric aldehyde functional compound. For example, the second component may be a cationic glyoxylated polyacrylamide. In another embodiment, the second component may be a polymeric anionic compound comprising carboxy functionality.