Abstract: The present disclosure relates to a duplex stainless steel comprising in weight % (wt %): C less than 0.03; Si less than 0.60; Mn 0.40 to 2.00; P less than 0.04; S less than or equal to 0.01; Cr more than 30.00 to 33.00; Ni 6.00 to 10.00; Mo 1.30 to 2.90; N 0.15 to 0.28; Cu 0.60 to 2.20; Al less than 0.05; balance Fe and unavoidable impurities. The present disclosure also relates to a component or a construction material comprising the duplex stainless steel. Additionally, the present disclosure also relates to a process for manufacturing a component comprising said duplex stainless steel.

Abstract: The present disclosure relates to a drill component having a martensitic stainless steel which has good corrosion resistance in combination with optimized and well-balanced mechanical properties, such as high hardness, resistance against wear and abrasion, high tensile strength and high impact toughness.

Abstract: The present disclosure relates to a martensitic stainless steel suitable for rock drill steel rods. Furthermore, the present disclosure also relates to the use of the martensitic stainless steel and to products manufactured thereof, especially drill rods.

Abstract: The present disclosure relates to a duplex stainless steel comprising in weight % (wt %): C less than 0.03; Si less than 0.60; Mn 0.40 to 2.00; P less than 0.04; S less than or equal to 0.01; Cr more than 30.00 to 33.00; Ni 6.00 to 10.00; Mo 1.30 to 2.90; N 0.15 to 0.28; Cu 0.60 to 2.20; Al less than 0.05; balance Fe and unavoidable impurities. The present disclosure also relates to a component or a construction material comprising the duplex stainless steel. Additionally, the present disclosure also relates to a process for manufacturing a component comprising said duplex stainless steel.

Abstract: The present disclosure relates to a drill component having a martensitic stainless steel which has good corrosion resistance in combination with optimized and well-balanced mechanical properties, such as high hardness, resistance against wear and abrasion, high tensile strength and high impact toughness.

Abstract: The present disclosure relates to a martensitic stainless steel suitable for rock drill steel rods. Furthermore, the present disclosure also relates to the use of the martensitic stainless steel and to products manufactured thereof, especially drill rods.

Abstract: An austenitic stainless steel alloy having the following composition in percent of weight (wt %): 0.02?C?0.06; Si<1.0; 2.0?Mn?6.0; 2.0?Ni?4.5; 17?Cr?19; 2.0?Cu?4.0; 0.15?N?0.25; 0?Mo?1.0; 0?W?0.3; 0?V?0.3; 0?Ti?0.5; 0?Al?1.0; 0?Nb?0.5; 0?Co?1.0; the balance Fe and normally occurring impurities, wherein the contents of the alloying elements are balanced so that the following conditions are fulfilled: Nieqv?1.42*Creqv??13.42; and Nieqv+0.85*Creqv?29.00 wherein Creqv=[% Cr]+2*[% Si]+1.5*[% Mo]+5*[% V]+5.5*[% Al]+1.75*[% Nb]+1.5*[% Ti]+0.75*[% W] Nieqv[% Ni]+[% Co]+0.5*[% Mn]+0.3*[% Cu]+25*[% N]+30*[% C]; and ?70° C.<MD30<?25° C., wherein MD30=(551?462*([% C]+[% N])?9.2*[% Si]?8.1*[% Mn]?13.7*[% Cr]?29*([% Ni]+[% Cu])?68*[% Nb]?18.5*[% Mo])° C.

Abstract: A stainless steel music string having a composition in percent by weight (wt %) of, 0.01?C?0.04; 0.01?N?0.06; 0.1?Si?1.0; 0.2?Mn?2.0; 5.0?Ni?10; 16?Cr?20; 0.2?Cu?3.0; 0?Mo?2.0; 0?W?0.5; 0?V?0.5; 0?Ti?1.0; 0?Al?1.0; 0?Nb?1.0; 0?Co?1.0, and the balance being Fe and normally occurring impurities The music string also includes at least 90% martensite phase by volume.

Abstract: An austenitic stainless steel alloy having the following composition in percent of weight (wt %): 0.02?C?0.06; Si<1.0; 2.0?Mn?6.0; 2.0?Ni?4.5; 17?Cr?19; 2.0?Cu?4.0; 0.15?N?0.25; 0?Mo?1.0; 0?W?0.3; 0?V?0.3; 0?Ti?0.5; 0?Al?1.0; 0?Nb?0.5; 0?Co?1.0; the balance Fe and normally occurring impurities, wherein the contents of the alloying elements are balanced so that the following conditions are fulfilled: Nieqv?1.42*Creqv??13.42; and Nieqv+0.85*Creqv?29.00 wherein Creqv=[% Cr]+2*[% Si]+1.5*[% Mo]+5*[% V]+5.5*[% Al]+1.75*[% Nb]+1.5*[% Ti]+0.75*[% W] Nieqv[% Ni]+[% Co]+0.5*[% Mn]+0.3*[% Cu]+25*[% N]+30*[% C]; and ?70° C.<MD30<?25° C., wherein MD30=(551?462*([% C]+[% N])?9.2*[% Si]?8.1*[% Mn]?13.7*[% Cr]?29*([% Ni]+[% Cu])?68*[% Nb]?18.5*[% Mo])° C.

Abstract: An austenitic Ni-based alloy with improved workability, good corrosion resistance and good structure stability useful as heat exchanger tubing in sulphur-, chloride- or alkaline-containing environments. The material has an austenitic structure which contains in weight-% up to 0.025% C, 20-27% Cr, 8-12% Mo, up to 0.5% Si, up to 0.5% Mn, up to 0.3% Al, up to 0.1% N, 3-15% Fe, up to 0.5% Ti, up to 0.5% Nb, the remainder being Ni and usual impurities.