Abstract: Described herein are tires comprising a rubber composition based on at least an elastomer matrix comprising at least one copolymer of butadiene and of vinylaromatic monomer and a hydrocarbon resin. The hydrocarbon resin is based on a cyclic monomer selected from the group consisting of a distillation cut from a petroleum refinery stream, C4, C5 and C6 cyclic olefins and mixtures thereof. The hydrocarbon resin has a content of aromatic protons (H Ar, expressed in mol %), a glass transition temperature (Tg, expressed in ° C.), and a number average molecular weight (Mn, expressed in g/mol) that are represented by (1) 12 mol %?H Ar?19 mol %, (2) Tg?95?2.2*(H Ar), (3) Tg??53+(0.265*Mn) and (4) 300 g/mol?Mn?450 g/mol.

Abstract: Described herein are tires comprising a rubber composition based on at least an elastomer and a hydrocarbon resin. The hydrocarbon resin is based on a cyclic monomer selected from the group consisting of a distillation cut from a petroleum refinery stream, C4, C5 and C6 cyclic olefins and mixtures thereof. The hydrocarbon resin has a content of aromatic protons (H Ar, expressed in mol %), a glass transition temperature (Tg, expressed in ° C.), and a number average molecular weight (Mn, expressed in g/mol) that are represented by (1) 12 mol %?H Ar?19 mol %, (2) Tg?95-2.2*(H Ar), (3) Tg??53+(0.265*Mn) and (4) 300 g/mol?Mn?450 g/mol.

Abstract: Described herein are tires comprising a rubber composition based on at least an elastomer matrix comprising from 50 to 100 phr of one or more copolymers of butadiene and of vinylaromatic monomer, having a content of vinylaromatic units of between 0 and 5% by weight and a Tg within a range extending from ?110° C. to ?70° C.; and a hydrocarbon resin, wherein the hydrocarbon resin is based on a cyclic monomer selected from the group consisting of a distillation cut from a petroleum refinery stream, and/or C4, C5 or C6 cyclic olefins and mixtures thereof, and wherein the hydrocarbon resin has a content of aromatic protons (H Ar, expressed in mol %), a glass transition temperature (Tg, expressed in ° C.), and a number average molecular weight (Mn, expressed in g/mol) that are represented by (1) H Ar>6 mol %, (2) Tg?95?2.2*(H Ar), and (3) Tg??53+(0.265*Mn).

Abstract: Described herein are tires comprising a rubber composition based on at least an elastomer matrix comprising from 50 to 100 phr of one or more copolymers of butadiene and of vinylaromatic monomer, having a content of vinylaromatic units of between 0 and 5% by weight and a Tg within a range extending from ?110° C. to ?70° C.; and a hydrocarbon resin, wherein the hydrocarbon resin is based on a cyclic monomer selected from the group consisting of a distillation cut from a petroleum refinery stream, and/or C4, C5 or C6 cyclic olefins and mixtures thereof, and wherein the hydrocarbon resin has a content of aromatic protons (H Ar, expressed in mol %), a glass transition temperature (Tg, expressed in ° C.), and a number average molecular weight (Mn, expressed in g/mol) that are represented by (1) H Ar?6 mol %, (2) Tg?95?2.2*(H Ar), (3) Tg?125?(0.08*Mn).

Abstract: Described herein are tires comprising a rubber composition based on at least an elastomer and a hydrocarbon resin, wherein [[said]]the hydrocarbon resin is based on a cyclic monomer selected from the group consisting of a distillation cut from a petroleum refinery stream, and/or C4, C5 or C6 cyclic olefins and mixtures thereof, and wherein the hydrocarbon resin has a number average molecular weight (Mn) of between 150 and 800 g/mol, and a content of aromatic protons (H Ar, expressed in mol %), a glass transition temperature (Tg, expressed in ° C.), and a number average molecular weight (Mn, expressed in g/mol) that are represented by (1) H Ar<6 mol %, (2) Tg?95?2.2*(H Ar), (3) Tg?125?(0.08*Mn).

Abstract: Described herein are tires comprising a rubber composition based on at least an elastomer and a hydrocarbon resin, wherein the hydrocarbon resin is based on a cyclic monomer selected from the group consisting of a distillation cut from a petroleum refinery stream, and/or C4, C5 or C6 cyclic olefins and mixtures thereof, and wherein the hydrocarbon resin has a content of aromatic protons (H Ar, expressed in mol %), a glass transition temperature (Tg, expressed in ° C.), and a number average molecular weight (Mn, expressed in g/mol) that are represented by (1) H Ar>6 mol %, (2) Tg?95?2.2*(H Ar), and (3) Tg??53+(0.265*Mn).

Abstract: A rubber composition is based on at least: a diene elastomer; a reinforcing inorganic filler; an agent for coupling the reinforcing inorganic filler with the diene elastomer, said coupling agent being an organofunctional silane comprising at least one oligomer of general formula (I), as described in the claims, bearing at least one blocked mercaptosilane unit and at least one mercaptosilane unit, a hydrocarbon-based resin predominantly composed of monomers chosen from the group consisting of cyclopentadiene, dicyclopentadiene, methylcyclopentadiene and mixtures thereof, and a crosslinking system. A semi-finished article and a tire may comprise at least one such rubber composition.

Abstract: A rubber composition is based on at least: a diene elastomer; a reinforcing inorganic filler; an agent for coupling the reinforcing inorganic filler with the diene elastomer, said coupling agent being a blocked mercaptosilane of formula (I), as described in the claims; a hydrocarbon-based resin predominantly composed of monomers chosen from the group consisting of cyclopentadiene, dicyclopentadiene, methylcyclopentadiene and mixtures thereof, and a crosslinking system. A semi-finished article and a tire may comprise at least one such rubber composition.