Abstract: The invention provides a composition comprising a first composition, comprising a first ethylene/alpha-olefin/non-conjugated polyene and a second ethylene ethylene/alpha-olefin/non-conjugated polyene, and wherein the first composition comprises the following property: Mw>1389.6 [g/mole] MV+115,000 g/mole, wherein MV is the Mooney Viscosity (ML 1+4, 125C), and Mw is the weight average molecular weight, as determined by conventional GPC.

Abstract: The present disclosure provides an article. The article includes an adhesive layer with two opposing surfaces. The adhesive layer includes (i) a functionalized ethylene-based polymer having a melt index from 0.1 g/10 min to 300 g/10 min; (ii) from 0.01 wt % to 45 wt % of a functionalized hydrocarbon; (iii) a tackifier; and (iv) optionally, a crosslinking agent.

Abstract: A composition useful as an adhesive for binding a fabric, e.g., a cotton cloth, to a rubber substrate, e.g., a base sheet comprising EPDM, is described, the composition comprising at least the following: (A) A functionalized, halogenated olefin-based polymer having a melt index (12, 190° C./2.16) greater than, or equal, to 30 grams per 10 minutes (g/10 min); (B) A tackifier; and/or (B?) An olefin-based polymer having a density from 0.855 to 0.900 grams per cubic centimeter (g/cc) and a weight average molecular weight (Mw) of less than, or equal to, 60,000 grams per mole.

Abstract: The instant invention provides a polymeric blend composition, injection molded articles, films and sheets made therefrom. The polymeric blend composition according to the present invention comprises: (a) a first component selected from the group consisting of an ethylene/alpha-olefin copolymer and a propylene/ethylene copolymer; wherein said ethylene/alpha-olefin co-polymer has density in the range of from 0.857 to 0.902 g/cm3, a melt index (I2) in the range of from 0.5 to 30 g/10 minutes, a DCS melting point temperature (second heat) in the range of from 40 to 99° C., a heat of fusion in the range of from 18 to 108 Jg?1, and a crystallinity in the range of from 6 to 37 weight percent; and wherein propylene/ethylene copolymer has a melt flow rate in the range of from 1 to 30 g/10 minutes, a DCS melting point temperature (second heat) in the range of from 55 to 85° C.

Abstract: The instant invention provides a polymeric blend composition, injection molded articles, films and sheets made therefrom. The polymeric blend composition according to the present invention comprises: (a) a first component selected from the group consisting of an ethylene/alpha-olefin copolymer and a propylene/ethylene copolymer; wherein said ethylene/alpha-olefin co-polymer has density in the range of from 0.857 to 0.902 g/cm3, a melt index (I2) in the range of from 0.5 to 30 g/10 minutes, a DCS melting point temperature (second heat) in the range of from 40 to 99° C., a heat of fusion in the range of from 18 to 108 Jg?1, and a crystallinity in the range of from 6 to 37 weight percent; and wherein propylene/ethylene copolymer has a melt flow rate in the range of from 1 to 30 g/10 minutes, a DCS melting point temperature (second heat) in the range of from 55 to 85° C.

Abstract: Plasticized polyisocyanate compositions contain (a) an isocyanate terminated reaction product of a polymeric MDI with a difunctional poly(propylene oxide) homopolymer or difunctional copolymer of at least 85% by weight propylene oxide and up to 15% by weight ethylene oxide, which homopolymer or copolymer has a molecular weight of from about 400 to 2200 and (b) at least one alkyl ester of one or more fatty acids, the polyisocyanate composition having an isocyanate content of from about 8 to about 14% by weight and a Brookfield viscosity of no greater than 5000 cps at 25° C. The plasticized prepolymers are particularly useful in foam formulations for insulating cavities in automotive parts and thermal insulating panels such as the walls of buildings or appliances.