Abstract: A process for producing amethyst crystals which involves growing colourless quartz crystals by a hydrothermal method of a temperature drop in a high-pressure autoclave on crystalline quartz seed plates oriented parallel to pinacoid crystallographic planes {0001} or to planes inclined to said pinacoid planes at an angle of up to 15.degree. with the use of silica as a charge, said growing being effected from aqueous solutions of ammonium fluoride with a concentration of from 5 to 30% by weight and containing iron introduced into the autoclave in the form of its oxydic or hydroxydic compounds in an amount ranging from 5 to 30 g/l of the solution. Said growing of colourless quartz crystals is effected at a crystallization temperature within the range of from 150.degree. to 500.degree.C under a pressure of from 10 to 1,200 kg/cm.sup.2 and at a crystal growth rate of from 0.05 to 1.5 mm/day.