Abstract: A dry granular ceramic tile from a wet slurry spraying process and a preparation method thereof, comprises: applying an overglaze on a green body, applying a pattern by ink-jet printing, applying a dry granular glaze by bell-shaped spraying, and sintering to obtain ceramic tiles. The dry granular glaze contains: by mass percentage, dry granular frit A: 15%, dry granular frit B: 12% to 15%, dry granular frit C: 13% to 17%. The softening temperature of the dry granular frit A is 1135° C. to 1175° C., 980° C. to 1050° C. for the dry granular frit B, and 1020° C. to 1127° C. for the dry granular frit C. The dry granular frits used in the present invention adopts a combination of dry granular frits with three different melting points, and using such a matching method, it is convenient for the effective adjustment of the brick shape and the firing temperature during production.

Abstract: A dry granular ceramic tile from a wet slurry spraying process and a preparation method thereof, comprises: applying an overglaze on a green body, applying a pattern by ink-jet printing, applying a dry granular glaze by bell-shaped spraying, and sintering to obtain ceramic tiles. The dry granular glaze contains: by mass percentage, dry granular frit A: 15%, dry granular frit B: 12% to 15%, dry granular frit C: 13% to 17%. The softening temperature of the dry granular frit A is 1135° C. to 1175° C., 980° C. to 1050° C. for the dry granular frit B, and 1020° C. to 1127° C. for the dry granular frit C. The dry granular frits used in the present invention adopts a combination of dry granular frits with three different melting points, and using such a matching method, it is convenient for the effective adjustment of the brick shape and the firing temperature during production.

Abstract: Disclosed are a semi-transparent ceramic sheet decorated through ink light-absorbance and a preparation method thereof. The semi-transparent ceramic sheet comprises a semi-transparent green body, an inner inkjet pattern layer infiltrating into the semi-transparent green body from an upper surface of the semi-transparent green body, a decoloration glaze layer located on the upper surface, and a surface pattern layer located on the decoloration glaze layer. The decoloration glaze layer is capable of decoloring the ink of the inner inkjet pattern layer. The semi-transparent ceramic sheet is provided with the decoloration glaze layer so that the inkjet decoration of the inner inkjet pattern layer cannot be displayed on the surface, and the decorative pattern on the surface of the green body is the surface pattern layer and the inner inkjet pattern layer is completely in the inner layer of the green body.

Abstract: Disclosed are a semi-transparent ceramic sheet decorated through ink light-absorbance and a preparation method thereof. The semi-transparent ceramic sheet comprises a semi-transparent green body, an inner inkjet pattern layer infiltrating into the semi-transparent green body from an upper surface of the semi-transparent green body, a decoloration glaze layer located on the upper surface, and a surface pattern layer located on the decoloration glaze layer. The decoloration glaze layer is capable of decoloring the ink of the inner inkjet pattern layer. The semi-transparent ceramic sheet is provided with the decoloration glaze layer so that the inkjet decoration of the inner inkjet pattern layer cannot be displayed on the surface, and the decorative pattern on the surface of the green body is the surface pattern layer and the inner inkjet pattern layer is completely in the inner layer of the green body.