Abstract: Disclosed are a low-shrinkage, high-strength, and large ceramic plate and a manufacturing method thereof. The method comprises the following steps: (1) preparing a ceramic raw material powder; (2) subjecting an acicular wollastonite to surface coating with a silane coupling agent and to pre-dispersion with a fumed silica to obtain a pre-treated acicular wollastonite; and (3) thoroughly mixing the ceramic raw material powder and the pre-treated acicular wollastonite and granulating the resulting mixture, the amount of the pre-treated acicular wollastonite added being 10 wt % to 30 wt % of the ceramic raw material powder, and subjecting the resulting granules to dry pressing and sintering to obtain the large ceramic plate. The acicular wollastonite is incorporated into the manufacturing of the large ceramic plate to take full advantage of the reinforcing effect and low sintering shrinkage characteristics of the acicular wollastonite. The invention reduces sintering shrinkage and increases product strength.

Abstract: Disclosed are a semi-transparent ceramic sheet decorated through ink light-absorbance and a preparation method thereof. The semi-transparent ceramic sheet comprises a semi-transparent green body, an inner inkjet pattern layer infiltrating into the semi-transparent green body from an upper surface of the semi-transparent green body, a decoloration glaze layer located on the upper surface, and a surface pattern layer located on the decoloration glaze layer. The decoloration glaze layer is capable of decoloring the ink of the inner inkjet pattern layer. The semi-transparent ceramic sheet is provided with the decoloration glaze layer so that the inkjet decoration of the inner inkjet pattern layer cannot be displayed on the surface, and the decorative pattern on the surface of the green body is the surface pattern layer and the inner inkjet pattern layer is completely in the inner layer of the green body.

Abstract: Disclosed are a low-shrinkage, high-strength, and large ceramic plate and a manufacturing method thereof. The method comprises the following steps: (1) preparing a ceramic raw material powder; (2) subjecting an acicular wollastonite to surface coating with a silane coupling agent and to pre-dispersion with a fumed silica to obtain a pre-treated acicular wollastonite; and (3) thoroughly mixing the ceramic raw material powder and the pre-treated acicular wollastonite and granulating the resulting mixture, the amount of the pre-treated acicular wollastonite added being 10 wt % to 30 wt % of the ceramic raw material powder, and subjecting the resulting granules to dry pressing and sintering to obtain the large ceramic plate. The acicular wollastonite is incorporated into the manufacturing of the large ceramic plate to take full advantage of the reinforcing effect and low sintering shrinkage characteristics of the acicular wollastonite. The invention reduces sintering shrinkage and increases product strength.

Abstract: Disclosed are a semi-transparent ceramic sheet decorated through ink light-absorbance and a preparation method thereof. The semi-transparent ceramic sheet comprises a semi-transparent green body, an inner inkjet pattern layer infiltrating into the semi-transparent green body from an upper surface of the semi-transparent green body, a decoloration glaze layer located on the upper surface, and a surface pattern layer located on the decoloration glaze layer. The decoloration glaze layer is capable of decoloring the ink of the inner inkjet pattern layer. The semi-transparent ceramic sheet is provided with the decoloration glaze layer so that the inkjet decoration of the inner inkjet pattern layer cannot be displayed on the surface, and the decorative pattern on the surface of the green body is the surface pattern layer and the inner inkjet pattern layer is completely in the inner layer of the green body.

Abstract: A low-temperature fast-fired lightweight ceramic heat insulation plate and a preparation method thereof. The preparation method comprises: performing ball milling and powder spraying on a raw material containing foamable ceramic waste slag to prepare foamable powder, the foamable ceramic waste slag accounting for 80-100 wt % of the weight of the raw material; uniformly mixing 100 weight portions of the foamable powder with 3-15 weight portions of granular powder of a low-melting-point organic matter to obtain mixed powder materials; pressing the mixed powder materials under 10-20 MPa to prepare a ceramic green body; and firing the ceramic green body at a temperature of 1100-1170° C. to prepare the lightweight energy-saving ceramic heat insulation plate.

Abstract: A low-temperature fast-fired lightweight ceramic heat insulation plate and a preparation method thereof. The preparation method comprises: performing ball milling and powder spraying on a raw material containing foamable ceramic waste slag to prepare foamable powder, the foamable ceramic waste slag accounting for 80-100 wt % of the weight of the raw material; uniformly mixing 100 weight portions of the foamable powder with 3-15 weight portions of granular powder of a low-melting-point organic matter to obtain mixed powder materials; pressing the mixed powder materials under 10-20 MPa to prepare a ceramic green body; and firing the ceramic green body at a temperature of 1100-1170° C. to prepare the lightweight energy-saving ceramic heat insulation plate.