Abstract: A dual-cure method for forming a solid polymeric structure is provided. An end-capped, imide-terminated prepolymer is combined with at least one photopolymerizable olefinic monomer, at least one photoinitiator, and a diamine, to form a curable resin composition, which, in a first step, is irradiated under conditions effective to polymerize the at least one olefinic monomer, thus forming a scaffold composed of the prepolymer and the polyolefin with the diamine trapped therein. The irradiated composition is then thermally treated at a temperature effective to cause a transimidization reaction to occur between the prepolymer and the diamine, thereby releasing the end caps of the prepolymer and providing the solid polymeric structure. A curable resin composition comprising an end-capped, imide-terminated prepolymer, at least one photopolymerizable olefinic monomer, at least one photoinitiator, and a diamine, is also provided, as are related methods of use.

Abstract: A dual-cure method for forming a solid polymeric structure is provided. An end-capped, imide-terminated prepolymer is combined with at least one photopolymerisable olefinic monomer, at least one photoinitiator, and a diamine, to form a curable resin composition, which, in a first step, is irradiated under conditions effective to polymerize the at least one olefinic monomer, thus forming a scaffold composed of the prepolymer and the polyolefin with the diamine trapped therein. The irradiated composition is then thermally treated at a temperature effective to cause a transimidization reaction to occur between the prepolymer and the diamine, thereby releasing the end caps of the prepolymer and providing the solid polymeric structure. A curable resin composition comprising an end-capped, imide-terminated prepolymer, at least one photopolymerisable olefinic monomer, at least one photoinitiator, and a diamine, is also provided, as are related methods of use.

Abstract: A dual-cure method for forming a solid polymeric structure is provided. An end-capped, imide-terminated prepolymer is combined with at least one photopolymerisable olefinic monomer, at least one photoinitiator, and a diamine, to form a curable resin composition, which, in a first step, is irradiated under conditions effective to polymerize the at least one olefinic monomer, thus forming a scaffold composed of the prepolymer and the polyolefin with the diamine trapped therein. The irradiated composition is then thermally treated at a temperature effective to cause a transimidization reaction to occur between the prepolymer and the diamine, thereby releasing the end caps of the prepolymer and providing the solid polymeric structure. A curable resin composition comprising an end-capped, imide-terminated prepolymer, at least one photopolymerisable olefinic monomer, at least one photoinitiator, and a diamine, is also provided, as are related methods of use.

Abstract: A dual-cure method for forming a solid polymeric structure is provided. An end-capped, imide-terminated prepolymer is combined with at least one photopolymerisable olefinic monomer, at least one photoinitiator, and a diamine, to form a curable resin composition, which, in a first step, is irradiated under conditions effective to polymerize the at least one olefinic monomer, thus forming a scaffold composed of the prepolymer and the polyolefin with the diamine trapped therein. The irradiated composition is then thermally treated at a temperature effective to cause a transimidization reaction to occur between the prepolymer and the diamine, thereby releasing the end caps of the prepolymer and providing the solid polymeric structure. A curable resin composition comprising an end-capped, imide-terminated prepolymer, at least one photopolymerisable olefinic monomer, at least one photoinitiator, and a diamine, is also provided, as are related methods of use.

Abstract: Provided are an imide-terminated prepolymer, a preparation method therefor, a curable resin composition, use thereof and a dual curing method. An end capped, imide-terminated prepolymer is mixed with at least one photopolymerizable ethylenic monomer, at least one photoinitiator and diamine, and optionally a pigment to form a curable resin composition, which, in a first step, is irradiated under conditions effective to polymerize the at least one ethylenic monomer. The irradiated composition is then heat-treated under conditions effective to cause a transimidation reaction between the prepolymer and the diamine to provide a solid polymer.

Abstract: A dual-cure method for forming a solid polymeric structure is provided. An end-capped, imide-terminated prepolymer is combined with at least one photopolymerizable olefinic monomer, at least one photoinitiator, and a diamine, to form a curable resin composition, which, in a first step, is irradiated under conditions effective to polymerize the at least one olefinic monomer, thus forming a scaffold composed of the prepolymer and the polyolefin with the diamine trapped therein. The irradiated composition is then thermally treated at a temperature effective to cause a transimidization reaction to occur between the prepolymer and the diamine, thereby releasing the end caps of the prepolymer and providing the solid polymeric structure. A curable resin composition comprising an end-capped, imide-terminated prepolymer, at least one photopolymerizable olefinic monomer, at least one photoinitiator, and a diamine, is also provided, as are related methods of use.

Abstract: A dual-cure method for forming a solid polymeric structure is provided. An end-capped, imide-terminated prepolymer is combined with at least one photopolymerisable olefinic monomer, at least one photoinitiator, and a diamine, to form a curable resin composition, which, in a first step, is irradiated under conditions effective to polymerize the at least one olefinic monomer, thus forming a scaffold composed of the prepolymer and the polyolefin with the diamine trapped therein. The irradiated composition is then thermally treated at a temperature effective to cause a transimidization reaction to occur between the prepolymer and the diamine, thereby releasing the end caps of the prepolymer and providing the solid polymeric structure. A curable resin composition comprising an end-capped, imide-terminated prepolymer, at least one photopolymerisable olefinic monomer, at least one photoinitiator, and a diamine, is also provided, as are related methods of use.

Abstract: A dual-cure method for forming a solid polymeric structure is provided. An end-capped, imide-terminated prepolymer is combined with at least one photopolymerizable olefinic monomer, at least one photoinitiator, and a diamine, to form a curable resin composition, which, in a first step, is irradiated under conditions effective to polymerize the at least one olefinic monomer, thus forming a scaffold composed of the prepolymer and the polyolefin with the diamine trapped therein. The irradiated composition is then thermally treated at a temperature effective to cause a transimidization reaction to occur between the prepolymer and the diamine, thereby releasing the end caps of the prepolymer and providing the solid polymeric structure. A curable resin composition comprising an end-capped, imide-terminated prepolymer, at least one photopolymerizable olefinic monomer, at least one photoinitiator, and a diamine, is also provided, as are related methods of use.

Abstract: A dual-cure method for forming a solid polymeric structure is provided. An end-capped, imide-terminated prepolymer is combined with at least one photopolymerizable olefinic monomer, at least one photoinitiator, and a diamine, to form a curable resin composition, which, in a first step, is irradiated under conditions effective to polymerize the at least one olefinic monomer, thus forming a scaffold composed of the prepolymer and the polyolefin with the diamine trapped therein. The irradiated composition is then thermally treated at a temperature effective to cause a transimidization reaction to occur between the prepolymer and the diamine, thereby releasing the end caps of the prepolymer and providing the solid polymeric structure. A curable resin composition comprising an end-capped, imide-terminated prepolymer, at least one photopolymerizable olefinic monomer, at least one photoinitiator, and a diamine, is also provided, as are related methods of use.