Abstract: A selective nickel-based hydrogenation catalyst and the preparation thereof, characterized in that: provided that the catalyst is weighed 100%, it comprises nickel oxide 14-20% as active component, lanthanum oxide and/or cerium oxide 2-8%, and VIB element oxide 1-8% as aids, 2-8% silica, 1-8% alkaline earth metal oxides, and alumina as the balance. The catalyst specific surface area is 60-150 m2/g, and the pore volume is 0.4-0.6 ml/g. The catalyst has good hydrogenation performance, especially impurity and colloid resistance and hydrogenation stability. The catalyst can be applied to the diolefin selective hydrogenation of medium or low-distillate oil, especially of the full-distillates pyrolysis gasoline.

Abstract: A selective nickel-based hydrogenation catalyst and the preparation thereof, characterized in that: provided that the catalyst is weighed 100%, it comprises nickel oxide 14-20% as active component, lanthanum oxide and/or cerium oxide 2-8%, and VIB element oxide 1-8% as aids, 2-8% silica, 1-8% alkaline earth metal oxides, and alumina as the balance. The catalyst specific surface area is 60-150 m2/g, and the pore volume is 0.4-0.6 ml/g. The catalyst has good hydrogenation performance, especially impurity and colloid resistance and hydrogenation stability. The catalyst can be applied to the diolefin selective hydrogenation of medium or low-distillate oil, especially of the full-distillates pyrolysis gasoline.

Abstract: A method for preparing hydrorefining catalyst comprises the following steps: (1) mixing an aqueous ammonia solution with a polyamine complexing agent to form a mixed solvent; (2) adding a cobalt salt to the mixed solvent, dissolving the cobalt salt, and then adding a molybdenum salt and optional salts of other active components, and dissolving them to prepare an impregnating solution; and (3) impregnating a support with the impregnating solution, followed by aging, drying, and activating the impregnated support to form a hydrorefining catalyst. The hydrorefining catalyst prepared by this method has good activity, selectivity and stability in use.

Abstract: A method for preparing hydrorefining catalyst comprises the following steps: (1) mixing an aqueous ammonia solution with a polyamine complexing agent to form a mixed solvent; (2) adding a cobalt salt to the mixed solvent, dissolving the cobalt salt, and then adding a molybdenum salt and optional salts of other active components, and dissolving them to prepare an impregnating solution; and (3) impregnating a support with the impregnating solution, followed by aging, drying, and activating the impregnated support to form a hydrorefining catalyst. The hydrorefining catalyst prepared by this method has good activity, selectivity and stability in use.

Abstract: A selective hydrogenation catalyst, with alumina as carrier, and palladium as active component that distributed on the surface of the carrier in an egg-shell form, characterized in that: provided that the catalyst is weighed 100%, it comprises 0.2-0.5 wt % active component Pd, 2-8 wt % aids lanthanum and/or cerium, and 2-8 wt % alkaline earth metal. The specific surface area of the catalyst is 70-150 m2/g, the pore volume is 0.3-0.6 ml/g, and the crystal form of the carrier may be ? form or ?, ? mixed form mainly composed of ? form. The catalyst is suitable for the selective hydrogenation of medium or low distillate oil, especially for the first stage selective hydrogenation of pyrolysis gasoline. The catalyst has good hydrogenation performance, and can keep good hydrogenation activity and stability especially under the condition that the feed contains a small quantity of water, and the content of colloid, arsenic, and diolefin is higher.

Abstract: A selective hydrogenation catalyst, with alumina as carrier, and palladium as active component that distributed on the surface of the carrier in an egg-shell form, characterized in that: provided that the catalyst is weighed 100%, it comprises 0.2-0.5 wt % active component Pd, 2-8 wt % aids lanthanum and/or cerium, and 2-8 wt % alkaline earth metal. The specific surface area of the catalyst is 70-150 m2/g, the pore volume is 0.3-0.6 ml/g, and the crystal form of the carrier may be ? form or ?, ? mixed form mainly composed of ? form. The catalyst is suitable for the selective hydrogenation of medium or low distillate oil, especially for the first stage selective hydrogenation of pyrolysis gasoline. The catalyst has good hydrogenation performance, and can keep good hydrogenation activity and stability especially under the condition that the feed contains a small quantity of water, and the content of colloid, arsenic, and diolefin is higher.

Abstract: A selective nickel-based hydrogenation catalyst with alumina as carrier and the preparation thereof, characterized in that: provided that the catalyst is weighed 100%, it comprises nickel oxide 14-20% as active component, lanthanum oxide and/or cerium oxide 1-8%, VIB element oxide 1-8% as aids, 2-8% silica, 1-8% alkaline earth metal oxides. The catalyst specific surface area is 60-150 m2/g, and the pore volume is 0.4-0.6 ml/g. The catalyst has good hydrogenation performance, especially impurity and colloid resistance and hydrogenation stability. The catalyst can be applied to the diolefin selective hydrogenation of medium or low-distillate oil, especially of the full-distillates pyrolysis gasoline.