Abstract: A cementitious composition capable of forming high early strength cement when admixed with water may comprise, for each 100% by weight, no more than about 60% by weight C3S, at least about 4% by weight C2S, and between about 7% and about 11% by weight SO3, wherein the cementitious composition has a particle size distribution such that substantially all of its particles are of a size of about 10 microns or smaller. A cementitious composition may have a ratio of weight % SO3 to weight % Al2O3 of at least about 1.5 and a particle size distribution such that substantially all of its particles are of a size of about 10 microns or smaller. An apparatus and method for making such a cementitious composition are also described.

Abstract: A cementitious composition capable of forming a high, early-phase strength cement may comprise construction grade cement and ground blast furnace slag, the ground blast furnace slag having a Blaine fineness less than about 250 m2/kg. The cementitious composition may comprise, for each 100% by weight, greater than about 50% by weight construction grade portland cement and less than about 50% by weight ground blast furnace slag, and the cementitious composition may have a Blaine fineness less than about 300 m2/kg. Methods of making and using such a cementitious composition to cement a structure are also described.

Abstract: A cementitious composition capable of forming a high, early-phase strength cement may comprise construction grade cement and ground blast furnace slag, the ground blast furnace slag having a Blaine fineness less than about 250 m2/kg. The cementitious composition may comprise, for each 100% by weight, greater than about 50% by weight construction grade portland cement and less than about 50% by weight ground blast furnace slag, and the cementitious composition may have a Blaine fineness less than about 300 m2/kg. Methods of making and using such a cementitious composition to cement a structure are also described.

Abstract: A cementitious composition capable of forming high early strength cement when admixed with water may comprise, for each 100% by weight, no more than about 60% by weight C3S, at least about 4% by weight C2S, and between about 7% and about 11% by weight SO3, wherein the cementitious composition has a particle size distribution such that substantially all of its particles are of a size of about 10 microns or smaller. A cementitious composition may have a ratio of weight % SO3 to weight % Al2O3 of at least about 1.5 and a particle size distribution such that substantially all of its particles are of a size of about 10 microns or smaller. An apparatus and method for making such a cementitious composition are also described.

Abstract: An apparatus for making a cementitious composition may comprise a grinding mill for producing a cementitious composition from clinker and gypsum and classifiers for separating the cementitious composition into various portions. A primary portion of the cementitious composition has a particle size distribution such that substantially all of its particles are of a size of about 10 microns or smaller. A secondary portion and a remainder portion of the cementitious composition are combinable to form a resultant cementitious composition selected from Type I portland cement and Type III portland cement.

Abstract: A cementitious composition capable of forming a high, early-phase strength cement may comprise construction grade cement and ground blast furnace slag, the ground blast furnace slag having a Blaine fineness less than about 250 m2/kg. The cementitious composition may comprise, for each 100% by weight, greater than about 50% by weight construction grade portland cement and less than about 50% by weight ground blast furnace slag, and the cementitious composition may have a Blaine fineness less than about 300 m2/kg. Methods of making and using such a cementitious composition to cement a structure are also described.

Abstract: A cementitious composition capable of forming high early strength cement when admixed with water may comprise, for each 100% by weight, no more than about 60% by weight C3S, at least about 4% by weight C2S, and between about 7% and about 11% by weight SO3, wherein the cementitious composition has a particle size distribution such that substantially all of its particles are of a size of about 10 microns or smaller. A cementitious composition may have a ratio of weight % SO3 to weight % Al2O3 of at least about 1.5 and a particle size distribution such that substantially all of its particles are of a size of about 10 microns or smaller. An apparatus and method for making such a cementitious composition are also described.

Abstract: A cementitious composition capable of forming high early strength cement when admixed with water may comprise, for each 100% by weight, no more than about 60% by weight C3S, at least about 4% by weight C2S, and between about 7% and about 11% by weight SO3, wherein the cementitious composition has a particle size distribution such that substantially all of its particles are of a size of about 10 microns or smaller. A cementitious composition may have a ratio of weight % SO3 to weight % Al2O3 of at least about 1.5 and a particle size distribution such that substantially all of its particles are of a size of about 10 microns or smaller. An apparatus and method for making such a cementitious composition are also described.

Abstract: A cementitious composition capable of forming a high, early-phase strength cement may comprise construction grade cement and ground blast furnace slag, the ground blast furnace slag having a Blaine fineness less than about 250 m2/kg. The cementitious composition may comprise, for each 100% by weight, greater than about 50% by weight construction grade portland cement and less than about 50% by weight ground blast furnace slag, and the cementitious composition may have a Blaine fineness less than about 300 m2/kg. Methods of making and using such a cementitious composition to cement a structure are also described.

Abstract: A cementitious composition capable of forming high early strength cement when admixed with water may comprise, for each 100% by weight, no more than about 60% by weight C3S, at least about 4% by weight C2S, and between about 7% and about 11% by weight SO3, wherein the cementitious composition has a particle size distribution such that substantially all of its particles are of a size of about 10 microns or smaller. A cementitious composition may have a ratio of weight % SO3 to weight % Al2O3 of at least about 1.5 and a particle size distribution such that substantially all of its particles are of a size of about 10 microns or smaller. An apparatus and method for making such a cementitious composition are also described.