Abstract: The present disclosure provides for a polyurethane elastomer foam formed by reacting a mixture that includes 60 to 50 weight percent (wt. %) of a polyol formulation and 40 to 50 wt. % isocyanate pre-polymer (wt. % based on the total weight of the mixture). The polyol formulation includes 85 to 92 wt. % of a polytetramethylene ether glycol (PTMEG) with a weight average molecular weight of 1900 to 2100 and a hydroxyl number of about 53 to about 60; 4 to 10 wt. % of monoethylene glycol; a blowing agent; a catalyst; and a surfactant (wt. % values for the polyol formulation based on the total weight of the polyol formulation). The isocyanate pre-polymer includes 55 to 70 wt. % of a isocyanate blend having at least 90 wt. % of 4,4?-diphenylmethane diisocyanate; and 30 to 45 wt. % of the PTMEG, where the isocyanate pre-polymer has an isocyanate content of 16 to 21 wt.

Abstract: The present disclosure provides for a polyurethane elastomer foam formed by reacting a mixture that includes 60 to 50 weight percent (wt. %) of a polyol formulation and 40 to 50 wt. % isocyanate pre-polymer (wt. % based on the total weight of the mixture). The polyol formulation includes 85 to 92 wt. % of a polytetramethylene ether glycol (PTMEG) with a weight average molecular weight of 1900 to 2100 and a hydroxyl number of about 53 to about 60; 4 to 10 wt. % of monoethylene glycol; a blowing agent; a catalyst; and a surfactant (wt. % values for the polyol formulation based on the total weight of the polyol formulation). The isocyanate pre-polymer includes 55 to 70 wt. % of a isocyanate blend having at least 90 wt. % of 4,4?-diphenylmethane diisocyanate; and 30 to 45 wt. % of the PTMEG, where the isocyanate pre-polymer has an isocyanate content of 16 to 21 wt.

Abstract: Embodiments of the invention encompass polyurethane elastomers which are a reaction product of a reaction mixture that includes a) at least one polyester made using a dicarboxylic acid having a carbon chain of from 9 to 20; b) at least one chain extender; and c) at least one polyisocyanate. At least 20% of the total carbon content of the polyurethane elastomer is from renewable carbon.