Abstract: An iron-cobalt alloy containing in weight percentages: 10 to 22% of Co; traces to 2.5% of Si; traces to 2% of Al; 0.1 to 1% of Mn; traces to 0.0100% of C, a total of O, N and S content ranging between traces of 0.0070%; a total of Si, Al, Cr, Mo, V, Mn content ranging between 1.1 and 3.5%; a total of Cr, Mo and V content ranging between traces of 3%; a total of Ta and Nb content ranging between traces and 1%; and the rest being iron and impurities resulting from production wherein: 1.23×(Al+Mo) %+0.84 (Si+Cr+V) %?0.15×(Co %?15)?2.1, and 14.5×(Al+Cr) %+12×(V+Mo) %+25×Si %?21. The inventive alloy is useful for making electromagnetic actuator mobile cores.

Abstract: The invention concerns a ferromagnetic alloy whereof the chemical composition comprises, in wt. %: 32.5%?Ni?72.5%; 5%?Cr?18%; 0.01%?Mn?4%; C?1%; optionally one or more elements selected among Mo, V, Co, Cu, Si, W, Nb and Al, the total contents of said elements being not more than 10%, the remainder being iron and impurities resulting from preparation, the chemical composition further satisfying the following relationships: Cr?1.1Ni+23.25?0%; 45Cr+11Ni?1360; Ni+3Cr?60% if Ni?37.5; Cr?7.5 if Ni?37.5. The invention also concerns the use of said alloy for making heating elements for induction heated cooking appliances.

Abstract: An iron-cobalt alloy containing in weight percentages: 10 to 22% of Co; traces to 2.5% of Si; traces to 2% of Al; 0.1 to 1% of Mn; traces to 0.0100% of C, a total of O, N and S content ranging between traces of 0.0070%; a total of Si, Al, Cr, Mo, V, Mn content ranging between 1.1 and 3.5%; a total of Cr, Mo and V content ranging between traces of 3%; a total of Ta and Nb content ranging between traces and 1%; and the rest being iron and impurities resulting from production wherein: 1.23×(Al+Mo) %+0.84 (Si+Cr+V) %?0.15×(Co %?15)?2.1, and 14.5×(Al+Cr) %+12×(V+Mo) %+25×Si %?21. The inventive alloy is useful for making electromagnetic actuator mobile cores.

Abstract: The invention concerns an iron-cobalt alloy, characterised in that it comprises in weight percentages: 10 to 22% of Co; traces to 2.5% of Si; traces to 2% of Al; 0.1 to 1% of Mn; traces to 0.0100% of C; a total of O, N and S content ranging between traces and 0.0070%; a total of Si, Al, Cr, Mo, V, Mn content ranging between 1.1 and 3.5%; a total of Cr, Mo and V content ranging between traces and 3%; a total of Ta and Nb content ranging between traces and 1%; the rest being iron and impurities resulting from production; and in that: 1.23×(Al+Mo)%+0.84 (Si+Cr+V)%?0.15×(Co%?15)?2.1 and in that 14.5×. (Al+Cr)%+12×(V+Mo)%+25×Si%?21. The inventive alloy is useful for making electromagnetic actuator mobile cores.

Abstract: The invention concerns a ferromagnetic alloy whereof the chemical composition comprises, in wt. %: 32.5% ?Ni ?72.5%; 5% ?Cr?18%; 0.01% ?Mn?4%, C?1%; optionally one or more elements selected among Mo, V, Co, Cu, Si, W, Nb and Al, the total contents of said elements being not more than 10%, the remainder being iron and impurities resulting from preparation, the chemical composition further satisfying the following relationships: Cr?1.1Ni+23.25?0%; 45Cr+11Ni?1360 ;Ni+3Cr?60% if Ni?37.5; Cr?7.5 if Ni?37.5. The invention also concerns the use of said alloy for making heating elements for induction heated cooking appliances.

Abstract: The invention concerns an iron-cobalt alloy, characterised in that it comprises in weight percentages: 10 to 22% of Co; traces to 2.5% of Si; traces to 2% of Al; 0.1 to 1% of Mn; traces to 0.0100% of C; a total of O, N and S content ranging between traces and 0.0070%; a total of Si, Al, Cr, Mo, V, Mn content ranging between 1.1 and 3.5%; a total of Cr, Mo and V content ranging between traces and 3%; a total of Ta and Nb content ranging between traces and 1%; the rest being iron and impurities resulting from production; and in that: 1.23×(Al+Mo) %+0.84 (Si+Cr+V) %−0.15×(Co %−15)≦2.1 and in that 14.5×. (Al+Cr) %+12×(V+Mo) %+25×Si %≧21. The inventive alloy is useful for making electromagnetic actuator mobile cores.

Abstract: Masking device for a flat-screen color-display cathode-ray tube, comprising a support frame for a tensioned shadow mask and a tensioned shadow mask. The support frame is made of a hardened Fe—Ni alloy having a thermal expansion coefficient between 20° C. and 150° C. of less than 5×10−6 K−1 and a yield stress Rp0.2 at 20° C. of greater than 700 MPa; the tensioned shadow mask is made of an Fe—Ni alloy having a thermal expansion coefficient between 20° C. and 150° C. of less than 3×10−6 K−1; the Fe—Ni alloys are chosen so that: below a temperature T1, the mean expansion coefficient &agr;20-T, between 20° C. and T, of the alloy of the support frame is greater than the mean expansion coefficient &agr;20-T of the alloy of the shadow mask, and above T1 the coefficient &agr;20-T of the alloy of the frame is less than the coefficient &agr;20-T of the alloy of the shadow mask, where T1<350° C. and preferably <300° C.

Abstract: A maraging steel strip or part and process for manufacture of a strip or of a part cut out of a strip of cold-rolled maraging steel and hardened by a hardening heat treatment. In the process, before the hardening heat treatment is performed, the strip or the part is subjected to cold plastic deformation with a degree of working greater than 30% and the strip or the part is subjected to recrystallization annealing in order to obtain a fine-grained structure with ASTM index higher than 8. The composition by weight of the maraging steel is: 12%≦Ni≦24.5%; 2.5%≦Mo≦12%; 4.17%≦Co≦20%, Al %≦0.15%; Ti≦0.1%; N≦0.003%; Si≦0.1%; Mn≦0.1%; C≦0.005%; S≦0.001%; P≦0.005%; H≦0.0003%; O≦0.001%; iron and impurities resulting from smelting, the chemical composition also satisfying the relationships: 20%≦Ni+Mo≦27%; 50≦Co×Mo≦200; Ti×N≦2×10−4.

Abstract: Strip made of an austenitic Fe—Ni alloy or Fe—Ni—Co alloy or Fe—Ni—Co—Cu alloy, the chemical composition of the alloy of which comprises, in % by weight: 30%≦Ni≦70%; 0%≦Cu+2×Co≦20%; 0%≦Mn+Cr<5%; 0%≦W+2×Mo≦2%; 0%≦Ti+V+Nb+Al≦1%; 0.0005%≦B≦0.007%; the balance being iron and impurities such as C, S, P, O and N; the chemical composition being such that Fe+Ni+Cu+Co≧95%. The alloy has a cubic texture with a cubic texture index Dc≧7. Process for manufacturing a strip. Process for manufacturing a part by mechanical cutting.

Abstract: A maraging steel strip or part and process for manufacture of a strip or of a part cut out of a strip of cold-rolled maraging steel and hardened by a hardening heat treatment. In the process, before the hardening heat treatment is performed, the strip or the part is subjected to cold plastic deformation with a degree of working greater than 30% and the strip or the part is subjected to recrystallization annealing in order to obtain a fine-grained structure with ASTM index higher than 8. The composition by weight of the maraging steel is: 12%≦Ni≦24.5%; 2.5%≦Mo≦12%; 4.17%≦Co≦20%, Al%≦0.15%; Ti≦0.1%; N≦0.003%; Si≦0.1%; Mn≦0.1%; C≦0.005%; S≦0.001%; P≦0.005%; H≦0.0003%; O≦0.001%; iron and impurities resulting from smelting, the chemical composition also satisfying the relationships: 20%≦Ni+Mo≦27%; 50≦Co×Mo≦200; Ti×N≦2×10−4.

Abstract: Soft magnetic alloy of the iron-nickel type, the chemical composition of which comprises, in % by weight: 34%≦Ni≦40%; 7%≦Cr≦10%; 0.5%≦Co≦3%; 0.1%≦Mn≦1%; O≦0.007%; S≦0.002%; N≦0.004%; with N+S+O≦0.01%; iron and impurities 5 resulting from the production process. Use in motors especially suited for use in horology.

Abstract: Masking device for a flat-screen color-display cathode-ray tube, comprising a support frame for a tensioned shadow mask and a tensioned shadow mask. The support frame is made of a hardened Fe—Ni alloy having a thermal expansion coefficient between 20° C. and 150° C. of less than 5×10−6 K−1 and a yield stress Rp0.2 at 20° C. of greater than 700 MPa; the tensioned shadow mask is made of an Fe—Ni alloy having a thermal expansion coefficient between 20° C. and 150° C. of less than 3×10−6 K−1; the Fe—Ni alloys are chosen so that: below a temperature T1, the mean expansion coefficient &agr;20-T, between 20° C. and T, of the alloy of the support frame is greater than the mean expansion coefficient &agr;20-T of the alloy of the shadow mask, and above T1 the coefficient &agr;20-T of the alloy of the frame is less than the coefficient &agr;20-T of the alloy of the shadow mask, where T1<350° C. and preferably <300° C.

Abstract: Cooking vessel intended to be induction heated, comprising a heating part made of a ferromagnetic alloy having a Curie temperature of between 150° C. and 370° C. and a magnetostriction coefficient &lgr;s≦5×10−6 in absolute value. FeNiCuX ferromagnetic alloy for the manufacture of the cooking vessel, the chemical composition of which comprises from 50% to 85% of Ni, less than 50% of Cu, less than 12% of X=Cr+Mo+Mn+Si+Al+W+Nb+V+Ti, the balance being iron and impurities; the composition satisfies the relationships (35/25)×(75-Ni)≦Cu≦(50/35)×(85-Ni) and (7/20)×(Ni-65)≦X≦(12/35)×(Ni-50). Production method and method of use.

Abstract: Cooking vessel intended to be induction heated, comprising a heating part made of a ferromagnetic alloy having a Curie temperature of between 150° C. and 370° C. and a magnetostriction coefficient &lgr;s≦5×10−6 in absolute value. FeNiCuX ferromagnetic alloy for the manufacture of the cooking vessel, the chemical composition of which comprises from 50% to 85% of Ni, less than 50% of Cu, less than 12% of X=Cr+Mo+Mn+Si+Al+W+Nb+V+Ti, the balance being iron and impurities; the composition satisfies the relationships (35/25)×(75−Ni)≦Cu≦(50/35)×(85−Ni) and (7/20)×(Ni−65)≦X≦(12/35)×(Ni−50). Production method and method of use.

Abstract: Soft magnetic alloy of the iron-nickel type, the chemical composition of which comprises, by weight: 40%≦Ni+Co≦65%; 0%≦Co≦7%; 2%≦Cr≦5%; 1%≦Ti≦3%; 0%≦Al≦0.5%; 0%≦Mn+Si≦2%; optionally, up to 3% Mo, 2% W, 2% V, 1.5% Nb, 1% Ta and 3% Cu, the sum of the Cr, Mo, W, V, Nb, Ta and Cu contents being less than 7% and the sum of the Mo, W, V, Nb, Ta and Cu contents being less than 4%; the balance being iron and impurities, such as carbon, sulfur and phosphorus, resulting from the smelting process, the chemical composition furthermore satisfying the relationships: Cr<5−0.015×(Ni+Co−52.5)2, if: Ni+Co≦52.5; Cr<5−0.040×(Ni+Co−52.5)2, if: Ni+Co≧52.5; the alloy having a saturation induction Bs of greater than 0.9 tesla, a coercive field of less than 10 A/m, an electrical resistivity p of greater than 60 &mgr;&OHgr;.cm and a hardness of greater than 200 HV. Process for manufacturing the alloy and uses.

Abstract: An iron--cobalt alloy the chemical composition of which comprises, by weight: 35%.ltoreq.Co.ltoreq.55%; 0.5%.ltoreq.V.ltoreq.2.5%; 0.02%.ltoreq.Ta+2.times.Nb.ltoreq.0.2%; 0.0007%.ltoreq.B.ltoreq.0.007%; C.ltoreq.0.05%; the balance being iron and impurities resulting from the smelting operation.

Abstract: Stepper motor of the type comprising a rotor (1), a stator (2) and a coil (3) consisting of a magnetic core (4) and of a winding (5), in which the stator (2) consists of a soft magnetic alloy of the FeNiCr type, the chemical composition of which includes, by weight: 40%.ltoreq.Ni+Co.ltoreq.60%, 0%.ltoreq.Co.ltoreq.7%, 8%.ltoreq.Cr.ltoreq.13.5%, 8%.ltoreq.Cr+Mn+Si+Mo+Nb+V+W.ltoreq.13.5%, the remainder being iron and impurities resulting from the manufacture. Soft magnetic alloy.

Abstract: An iron-nickel alloy useful for the manufacture of a stretched shadow mask, the chemical composition of the iron-nickel alloy containing by weight: 69%.ltoreq.Ni.ltoreq.83%, 0%.ltoreq.Mo.ltoreq.7%, 0%.ltoreq.Cu.ltoreq.8%, 0%.ltoreq.Co.ltoreq.1.5%, 0%.ltoreq.W.ltoreq.7%, 0%.ltoreq.Nb.ltoreq.7%, 0%.ltoreq.V.ltoreq.7%, 0%.ltoreq.Cr.ltoreq.7%, 0%.ltoreq.Ta.ltoreq.7%, 0%.ltoreq.C.ltoreq.0.1%, 0%.ltoreq.Mn.ltoreq.1%, 0%.ltoreq.Si.ltoreq.1%, 0%.ltoreq.Ti.ltoreq.1.2%, 0%.ltoreq.Al.ltoreq.1.2%, 0%.ltoreq.Zr.ltoreq.1.2%, 0%.ltoreq.Hf.ltoreq.1.2%, S.ltoreq.0.010% the balance being iron and impurities resulting from smelting, the chemical composition furthermore satisfying the relationships:Co+ni+1.5.times.Cu.gtoreq.79.5%; 3.times.(Co+Ni)-2.times.Cu.gtoreq.206%; Co+Ni+7.times.Cu.ltoreq.130%; 7.times.(Co+Ni)+2.times.Cu.ltoreq.581%; Mo+W+Nb+V+Cr+Ta.ltoreq.7%; Ti+al+Zr+Hf.ltoreq.1.2%; C+Mn+Si.ltoreq.1%; 80.5.ltoreq.Co+Ni+0.80.times.Cu.ltoreq.81.7%.

Abstract: An iron-nickel alloy, the chemical composition of which includes by weight:30%.ltoreq.Ni+Co.ltoreq.85%;0%.ltoreq.Co+Cu+Mn.ltoreq.10%;0%.ltoreq.Mo+W+Cr.ltoreq.4%;0%.ltoreq.V+Si.ltoreq.2%;0%.ltoreq.Nb+Ta.ltoreq.1%;0.003%.ltoreq.C.ltoreq.0.05% 0.003%.ltoreq.Ti.ltoreq.0.15%;0.003%.ltoreq.Ti+Zr+Hf.ltoreq.0.15%;0.001%<S+Se+Te<0.015%;and the remainder, iron and impurities resulting from production; in addition, the chemical composition satisfies the relationship:0.ltoreq.Nb+Ta+Ti+Al.ltoreq.1%.A cold-rolled strip with a cubic texture and its uses.

Abstract: Method for producing soft magnetic alloys with very high permeability, in which an ingot is cast containing in its composition more than 70% nickel or more than 45% cobalt, the metal having, or not having, been subjected to a secondary metallurgical step, the ingot is remelted under an electroconductive slag, the remelted ingots being converted into strips after hot rolling then cold rolling, the strips then being subjected to a treatment for developing magnetic characteristics, in which method the alloy is remelted under an electroconductive slag comprising at least the first three components of the system: CaF.sub.2, CaO, SiO.sub.2, Al.sub.2 O.sub.3, and defining a zone in a ternary diagram delimited by the following proportions by weight:CaF.sub.2 (50-75)%CaO (20-30)%SiO.sub.2 (5-15)%with Al.sub.2 O.sub.3 <3%.