Abstract: The present application concerns a coated film comprising a substantially biodegradable substrate having a biodegradable coating thereon at a coat weight of not more than 12 gsm, as well as useful articles sealed inside a package at least partly comprising such a film, and also a process for producing a coated film comprising providing a substantially biodegradable film substrate and applying a biodegradable coating to the substrate at a coat weight of less than 12 gsm by means of a hot melt coating step.

Abstract: There is described a substantially planar self-supporting sheet (preferably an thermoplastic film e.g. formed from a polyolefin such as BOPP) comprising on at least one side thereof a substantially continuous adherent coating, thereon to create a barrier to oxygen, the coating comprising nano-particles, the sheet characterized in that: (a) the nano-particles form a substantially continuous phase on the sheet; and/or (b) the nano-particles are present in an amount of at least about 20% by dry weight of the coating; and/or (c) the coating is substantially free of polymeric binder, synthetic hydrophilic resin and/or a resin with a hydrophilic/hydrophobic character. The coated sheets have a high oxygen barrier, with preferred OTR values (at 23° C. and 0% RH)<10 cm3/m2/day. Preferred nano-particles are biopolymers such as starch and the coating is preferably substantially free of wax which has been found to reduce oxygen barrier effectiveness.

Abstract: There is described a substantially planar self-supporting sheet (preferably an thermoplastic film e.g. formed from a polyolefin such as BOPP) comprising on at least one side thereof a substantially continuous adherent coating thereon to create a barrier to oxygen, the coating comprising nano-particles, the sheet characterised in that: (a) the nano-particles form a substantially continuous phase on the sheet; and/or (b) the nano-particles are present in an amount of at least about 20% by dry weight of the coating; and/or (c) the coating is substantially free of polymeric binder, synthetic hydrophilic resin and/or a resin with a hydrophilic/hydrophobic character. The coated sheets have a high oxygen barrier, with preferred OTR values (at 23° C. and 0% RH)<10 cm3/m2/day. Preferred nano-particles are biopolymers such as starch and the coating is preferably substantially free of wax which has been found to reduce oxygen barrier effectiveness.