Abstract: A method for converting a starting material containing at least 40 wt.-% of calcium silicon (hydr)oxide phases and calcium aluminum (hydr)oxide phases into an SiO2 rich SCM and a calcium carbonate additive includes the steps: providing the starting material with a D90 of ?1 mm, mixing the starting material with water or adjusting the water content to provide a starting material slurry having a solid:liquid weight ratio from 2:1 to 1:100, passing the starting material slurry together with carbon dioxide into a gravity separation reactor, subjecting the starting material slurry and carbon dioxide to centrifugal motion inside the reactor, and removing a heavy slurry from a first outlet of the reactor, removing a light slurry of lower density particles from a second outlet of the reactor, and removing liquid at a third outlet of the reactor.

Abstract: A method for manufacturing concrete parts has the steps of: providing a hydraulic cement and aggregate; mixing the cement and aggregate with water to provide a fresh concrete; introducing CO2 into the fresh concrete in an amount resulting in a carbonation degree of more than 0.5 wt.-% and less than 5 wt.-% of the total carbonatable Ca and Mg phases for a first carbonation step; curing the fresh concrete until at least 15 wt.-% of the calcium aluminates are hydrated to provide a green concrete part; subjecting the green concrete part to CO2 in an amount resulting in a carbonation degree of more than 10 wt.-% of the total carbonatable Ca and Mg phases for a final carbonation step; and storing the part for 0.5 hours to 28 days for further hydration of not-yet carbonated, not-yet hydrated cement to provide the concrete part. and concrete parts obtainable with the method.

Abstract: The present invention relates to a supplementary cementitious material, a method for producing the supplementary cementitious material, the use of the supplementary cementitious material, a binder comprising the supplementary cementitious material, a method for the preparation of the binder and use of the binder to make hydraulic building materials like concrete.

Abstract: A method for manufacturing supplementary cementitious material and sequestering CO2 by carbonating concrete fines has the following steps: grinding the concrete fines obtained from crushed concrete demolition waste in a mill at a temperature from 1 to 10° C. above the water dew point in a carbonating atmosphere provided by a gas containing from 10 to 99 Vol.-% CO2, circulating the ground and partially carbonated concrete fines in a fluidized bed reactor in contact with the carbonating atmosphere, and withdrawing decarbonated gas and carbonated concrete fines.

Abstract: A method of exhaust gas scrubbing includes providing recycled concrete fines as a waste material rich in carbonatable Ca and/or Mg phases and with d90?1000 ?m and a Rosin-Rammler slope n from 0.6 to 1.4 , injecting the waste material into an exhaust gas stream containing CO2 and/or SOx for reaction with CO2 and/or SOx at a relative humidity of 50 to 100 Vol.-% and a temperature from 40 to 130° C. in an amount of dry waste material ranging from 5 to 30 kg/m3, withdrawing a partly carbonated and/or sulphurized waste material and purified exhaust gas, and recycling a part of the partly carbonated and sulphurized waste material while the remainder is discharged, as well as use of a waste material slurry for exhaust gas cleaning of CO2 and/or SOx.

Abstract: A method for manufacturing hydraulically hardening building materials, includes the steps of: providing concrete demolition waste with a maximum particle size of up to 150 mm as a starting material, mixing the starting material with water to form a feedstock slurry, introducing carbon dioxide or a precursor thereof into the feedstock slurry to form carbonated concrete fines in an amount from 1 to 100 wt.-% of the hardened binder contained in the starting material and to detach the concrete fines from the aggregate contained in the starting material to form a product slurry, and mixing the product slurry with a cement forming the building material, and use of the obtainable building material for manufacturing building structures as well as method for manufacturing a supplementary cementitious material slurry.

Abstract: A method for manufacturing a binder of a hydratable material includes providing a starting material from one or more raw materials convertible by tempering at 600 to 1200° C. into the hydratable material, tempering the starting material to provide the hydratable material containing not more than 10% by weight monocalcium silicate and at least 15% by weight hydratable phases in the form of lime and dicalcium silicate, wherein the residence time and the tempering temperature are adapted to obtain the hydratable material by converting not more than 80% by weight of the starting material, and cooling the hydratable material to provide the binder comprising the hydratable material. The binder can be mixed with water and optionally one or more of aggregate, additives, admixtures to obtain a binder paste that is placed, hydrated and carbonated to produce a building product.

Abstract: A method for manufacturing supplementary cementitious material and sequestering CO2 by carbonating concrete fines has the following steps: grinding the concrete fines obtained from crushed concrete demolition waste in a mill at a temperature from 1 to 10° C. above the water dew point in a carbonating atmosphere provided by a gas containing from 10 to 99 Vol.-% CO2, circulating the ground and partially carbonated concrete fines in a fluidized bed reactor in contact with the carbonating atmosphere, and withdrawing decarbonated gas and carbonated concrete fines.

Abstract: A method of exhaust gas scrubbing includes providing recycled concrete fines as a waste material rich in carbonatable Ca and/or Mg phases and with d90?1000 ?m and a Rosin-Rammler slope n from 0.6 to 1.4 , injecting the waste material into an exhaust gas stream containing CO2 and/or SOx for reaction with CO2 and/or SOx at a relative humidity of 50 to 100 Vol.-% and a temperature from 40 to 130° C. in an amount of dry waste material ranging from 5 to 30 kg/m3, withdrawing a partly carbonated and/or sulphurized waste material and purified exhaust gas, and recycling a part of the partly carbonated and sulphurized waste material while the remainder is discharged, as well as use of a waste material slurry for exhaust gas cleaning of CO2 and/or SOx.

Abstract: A method for manufacturing a binder of a hydratable material includes providing a starting material from one or more raw materials convertible by tempering at 600 to 1200° C. into the hydratable material and tempering the starting material to provide the hydratable material containing not more than 10% by weight monocalcium silicate and at least 15% by weight hydratable phases in the form of lime and dicalcium silicate. The residence time and the tempering temperature are adapted to obtain the hydratable material by converting not more than 80% by weight of the starting material, and the hydratable material is then cooled to provide the binder comprising the hydratable material. The binder can be mixed with water and optionally one or more of aggregate, additives, admixtures to obtain a binder paste that is placed, hydrated and carbonated to produce a building product.

Abstract: A method of manufacturing building elements has the steps: providing a binder comprising at least 8% by weight ternesite, at least 15% by weight dicalcium silicate and at least 5% by weight ye'elimite, each with respect to the total binder, as hydraulically reactive phases; mixing the binder with water to form a paste; casting the paste into a desired shape for the building element; reacting the paste hydraulically to form calcium-silicate-hydrates, calcium-aluminium-silicate-hydrates, portlandite, brucite, strätlingite, hydrotalcite-like phases and ettringite/AFm and capillary pores, and carbonation hardening to provide the building element and to building elements obtainable by the method.

Abstract: The present invention relates to a composite cement obtainable by grinding Portland cement clinker and latent hydraulic material together, preferably in the presence of at least one amine grinding aid, to provide a ground mixture and combining the ground mixture with a mineral filler. It further relates to a method of manufacturing the composite cement comprising the steps of grinding a latent hydraulic material and a portland cement clinker together, preferably in the presence of at least one amine, to provide a ground mixture and combining the ground mixture with one or more mineral fillers as well as to binders and to using the cement or binders as building material.

Abstract: A method for manufacturing a binder of a hydratable material includes providing a starting material from one or more raw materials convertible by tempering at 600 to 1200° C. into the hydratable material, tempering the starting material to provide the hydratable material containing not more than 10% by weight monocalcium silicate and at least 15% by weight hydratable phases in the form of lime and dicalcium silicate, wherein the residence time and the tempering temperature are adapted to obtain the hydratable material by converting not more than 80% by weight of the starting material, and cooling the hydratable material to provide the binder comprising the hydratable material. The binder can be mixed with water and optionally one or more of aggregate, additives, admixtures to obtain a binder paste that is placed, hydrated and carbonated to produce a building product.

Abstract: A method of manufacturing building elements has the steps: providing a binder comprising at least 8% by weight ternesite, at least 15% by weight dicalcium silicate and at least 5% by weight ye'elimite, each with respect to the total binder, as hydraulically reactive phases; mixing the binder with water to form a paste; casting the paste into a desired shape for the building element; reacting the paste hydraulically to form calcium-silicate-hydrates, calcium-aluminium-silicate-hydrates, portlandite, brucite, stratlingite, hydrotalcite-like phases and ettringite/AFm and capillary pores, and carbonation hardening to provide the building element and to building elements obtainable by the method.

Abstract: A method for manufacturing a binder of a hydratable material includes providing a starting material from one or more raw materials convertible by tempering at 600 to 1200° C. into the hydratable material and tempering the starting material to provide the hydratable material containing not more than 10% by weight monocalcium silicate and at least 15% by weight hydratable phases in the form of lime and dicalcium silicate. The residence time and the tempering temperature are adapted to obtain the hydratable material by converting not more than 80% by weight of the starting material, and the hydratable material is then cooled to provide the binder comprising the hydratable material. The binder can be mixed with water and optionally one or more of aggregate, additives, admixtures to obtain a binder paste that is placed, hydrated and carbonated to produce a building product.

Abstract: This invention relates to a method for producing a supplementary cementitious material comprising the steps: providing a starting material containing dolomite and aluminium silicate, converting the starting material to the supplementary cementitious material by burning under reducing conditions in the temperature range of >700 to 1100° C. or by burning in the temperature range of 625 to 950° C. in the presence of a mineraliser, and cooling the supplementary cementitious material. The invention further relates to a binder comprising cement and to the ground supplementary cementitious material.

Abstract: The present invention relates to a composite cement obtainable by grinding Portland cement clinker and latent hydraulic material together, preferably in the presence of at least one amine grinding aid, to provide a ground mixture and combining the ground mixture with a mineral filler. It further relates to a method of manufacturing the composite cement comprising the steps of grinding a latent hydraulic material and a portland cement clinker together, preferably in the presence of at least one amine, to provide a ground mixture and combining the ground mixture with one or more mineral fillers as well as to binders and to using the cement or binders as building material.

Abstract: This invention relates to a method for producing a supplementary cementitious material comprising the steps: providing a starting material containing dolomite and aluminium silicate, converting the starting material to the supplementary cementitious material by burning under reducing conditions in the temperature range of >700 to 1100° C. or by burning in the temperature range of 625 to 950° C. in the presence of a mineraliser, and cooling the supplementary cementitious material. The invention further relates to a binder comprising cement and to the ground supplementary cementitious material.

Abstract: The present invention relates to a method of enhancing the latent hydraulic and/or pozzolanic reactivity of materials, especially of waste and by-products, comprising the steps: providing a starting material containing sources for CaO and at least one of SiO2 and AI2O3 mixing the starting material with water at a water/solids ratio from 0.1 to 100 hydrothermal treating of the starting material mixed with water in an autoclave at a temperature of 100 to 300° C. and a residence time from 0.1 to 24 hours to provide an autoclaved product suitable as supplementary cementitious material.

Abstract: A method for producing a supplementary cementitious material (SCM) that includes providing a starting material containing dolomite and aluminium silicate, converting the starting material to the supplementary cementitious material by burning in the temperature range of >800 to 1100° C. or by burning in the temperature range of 725 to 950° C. in the presence of a mineralizer and cooling the supplementary cementitious material.