Abstract: A workpiece for a fuel injection component is made of a steel having compositions, by mass %, of C: 0.08 to 0.16%, Si: 0.10 to 0.30%, Mn: 1.00 to 2.00%, S: 0.005 to 0.030%, Cu: 0.01 to 0.30%, Ni: 0.40 to 1.50%, Cr: 0.50 to 1.50%, Mo: 0.30 to 0.70%, V: 0.10 to 0.40%, s-Al: 0.001 to 0.100%, and Fe and unavoidable impurities as remaining components. After heating the workpiece to a temperature of 950° C. or more and 1350° C. or less, the workpiece is subjected to a hot forging, and thereafter cooled at an average cooling rate of 0.1° C./sec. or more in a temperature range from 800° C. to 500° C., and at the average cooling rate of 0.02° C./sec. or more and 10° C./sec. or less in the subsequent temperature range from 500° C. to 300° C. to set an area ratio of a bainite structure after hot forging to 85% or more.

Abstract: The present invention provides an age hardening type bainitic microalloyed steel having a composition which includes, in terms of mass %: 0.06-0.35% of C; 0.01-2.00% of Si; 0.10-3.00% of Mn; 0.001-0.200% of S; 0.001-2.00% of Cu; 0.40-3.00% of Ni; 0.10-3.00% of Cr; 0.10-1.00% of Mo; 0.10-1.00% of V; and 0.001-0.100% of s-Al, with the remainder being Fe and unavoidable impurities, and which satisfies a value of the following expression (1) to be 20 or larger and a value of the following expression (2) to be 0.82 or larger: 3×[C]+10×[Mn]+2×[Cu]+2×[Ni]+12×[Cr]+9×[Mo]+2×[V]??expression (1); 1.66×[C]+0.18×[Si]+0.27×[Mn]+0.09×[Ni]+0.32×[Cr]+0.34×[Mo]+0.44×[V]??expression (2), in which each [ ] in the expression (1) and the expression (2) indicates a content of the element shown therein in terms of mass %.

Abstract: A workpiece for a fuel injection component is made of a steel having compositions, by mass %, of C: 0.08 to 0.16%, Si: 0.10 to 0.30%, Mn: 1.00 to 2.00%, S: 0.005 to 0.030%, Cu: 0.01 to 0.30%, Ni: 0.40 to 1.50%, Cr: 0.50 to 1.50%, Mo: 0.30 to 0.70%, V: 0.10 to 0.40%, s-Al: 0.001 to 0.100%, and Fe and unavoidable impurities as remaining components. After heating the workpiece to a temperature of 950° C. or more and 1350° C. or less, the workpiece is subjected to a hot forging, and thereafter cooled at an average cooling rate of 0.1° C./sec. or more in a temperature range from 800° C. to 500° C., and at the average cooling rate of 0.02° C./sec. or more and 10° C./sec. or less in the subsequent temperature range from 500° C. to 300° C. to set an area ratio of a bainite structure after hot forging to 85% or more.

Abstract: The present invention relates to a part obtained from an age hardening type bainitic microalloyed steel, a process for producing the part, and the age hardening type bainitic microalloyed steel. In particular, the present invention relates to a part which has been controlled so as to have higher values of strength than conventional parts, a process for producing the part, and the age hardening type bainitic microalloyed steel.

Abstract: The present invention relates to a part obtained from an age hardening type bainitic microalloyed steel, a process for producing the part, and the age hardening type bainitic microalloyed steel. In particular, the present invention relates to a part which has been controlled so as to have higher values of strength than conventional parts, a process for producing the part, and the age hardening type bainitic microalloyed steel.

Abstract: The present invention provides an age hardening type bainitic microalloyed steel having a composition which includes, in terms of mass %: 0.06-0.35% of C; 0.01-2.00% of Si; 0.10-3.00% of Mn; 0.001-0.200% of S; 0.001-2.00% of Cu; 0.40-3.00% of Ni; 0.10-3.00% of Cr; 0.10-1.00% of Mo; 0.10-1.00% of V; and 0.001-0.100% of s-Al, with the remainder being Fe and unavoidable impurities, and which satisfies a value of the following expression (1) to be 20 or larger and a value of the following expression (2) to be 0.82 or larger: 3×[C]+10×[Mn]+2×[Cu]+2×[Ni]+12×[Cr]+9×[Mo]+2×[V]??expression (1); 1.66×[C]+0.18×[Si]+0.27×[Mn]+0.09×[Ni]+0.32×[Cr]+0.34×[Mo]+0.44×[V]??expression (2), in which each [ ] in the expression (1) and the expression dicates a content of the element shown therein in terms of mass %.

Abstract: A steel for a belt-type CVT pulley made of chromium steel or chromium molybdenum steel according to the present invention has a component composition that satisfies predetermined formulae regarding the mass % of Mn, Ni, Cr, Mo, Si, Nb and Ti. In addition, the steel for a belt-type CVT pulley contains, in terms of mass %, as essentially added elements, 0.15% to 0.25% of C, 0.40% to 1.00% of Mn, more than 1.80% and 2.20% or less of Cr, 0.005% to 0.030% of N, and 0.010% to 0.060% of Al, and as arbitrarily added elements, 0.20% or less of Si, 0.03% or less of P, 0.05% or less of S, 0.3% or less of Cu, 0.3% or less of Ni, and 0.2% or less of Mo, with the remainder being Fe and inevitable impurities.