Abstract: The invention relates to a composite element comprising a) a core made of a foam or of a porous material, b) an outer layer applied to the core a), and, c) a foil c) made of a thermoplastic and differing from the outer layer b).

Abstract: The invention relates to a composite material having two or more superimposed wood layers. Said layers are joined together by means of a one component polyurethane adhesive containing a prepolymer having free NCO groups and a wood having a volume fraction of libriform fibres in the region of between 50-70% is used.

Abstract: The invention relates to the use of a composite material having two or more superimposed layers of wood as a support element in structural engineering, nautical, vehicle and aircraft constructions, energy production systems, mining or in the production of furniture. The wood layers are joined together by means of a one component polyurethane adhesive containing a prepolymer with free NCO groups and the wood has a structure having a volume fraction of libriform fibers of between 50%-70%.

Abstract: The invention relates to a composite element comprising a) a core made of a foam or of a porous material, b) an outer layer applied to the core a), and, c) a foil c) made of a thermoplastic and differing from the outer layer b).

Abstract: The invention relates to a composite material having two or more superimposed wood layers. Said layers are joined together by means of a one component polyurethane adhesive containing a prepolymer having free NCO groups and a wood having a volume fraction of libriform fibres in the region of between 50-70% is used.

Abstract: The invention relates to the use of a composite material having two or more superimposed layers of wood as a support element in structural engineering, nautical, vehicle and aircraft constructions, energy production systems, mining or in the production of furniture. The wood layers are joined together by means of a one component polyurethane adhesive containing a prepolymer with free NCO groups and the wood has a structure having a volume fraction of libriform fibres of between 50%-70%.

Abstract: Compact and preferably cellular polyurethane elastomers based on polyisocyanate mixtures containing 3,3′-dimethylbiphenyl 4,4′-diisocyanate are produced by reacting a) relatively high molecular weight polyhydroxyl compounds and, if desired, b) low molecular weight hydroxyl-containing chain extenders and/or crosslinkers with c) 3,3′-dimethylbiphenyl 4,4′-diisocyanate and at least one additional aromatic diisocyanate selected from the group consisting of tolylene diisocyanate, diphenylmethane diisocyanate, 1,2-diphenylethane diisocyanate and phenylene diisocyanate, and/or at least one aliphatic diisocyanate having from 4 to 12 carbon atoms and/or at least one cycloaliphatic diisocyanate having from 6 to 18 carbon atoms, where the formative components (a), (c) and, if used, (b) are advantageously reacted by the prepolymer method, in the presence or absence of d) catalysts, e) blowing agents and f) additives.

Abstract: Compact and preferably cellular polyurethane elastomers are produced by reacting a) polyhydroxyl compounds having molecular weights of from 800 to 6000 and, if desired, b) chain extenders and/or crosslinkers having molecular weights of up to 800 [lacuna] c) naphthylene 1,5-diisocyanate and at least one additional aromatic diisocyanate selected from the group consisting of tolylene diisocyanate, diphenylmethane diisocyanate, 3,3′-dimethylbiphenyl diisocyanate, 1,2-diphenylethane diisocyanate and phenylene diisocyanate, and/or aliphatic diisocyanate having from 4 to 12 carbon atoms and/or cycloaliphatic diisocyanate having from 6 to 18 carbon atoms, where the formative components (a), (c) and, if used, (b) are preferably reacted by the prepolymer method, in the presence or absence of d) catalysts, e) blowing agents and f) additives. Isocyanate prepolymers suitable for this purpose are also described.

Abstract: Compact and preferably cellular polyurethane elastomers are prepared by reacting a) relatively high molecular weight polyhydroxyl compounds and if desired, b) low molecular weight chain extenders and/or crosslinkers with c) phenylene 1,4-diisocyanate (p-PDI) and at least one additional aromatic diisocyanate selected from the group consisting of tolylene diisocyanate, diphenylmethane diisocyanate, 3,3′-dimethylbiphenyl diisocyanate, 1,2-diphenylethane diisocyanate and/or aliphatic diisocyanate, having from 4 to 12 carbon atoms and/or cycloaliphatic diisocyanate having from 6 to 18 carbon atoms, where the formative components (a), (c) and, if used, (b) are advantageously reacted by the prepolymer method, in the presence or absence of d) catalysts, e) blowing agents and f) additives. Isocyanate prepolymers suitable for this purpose are described.

Abstract: A microcellular PU elastomer having improved dynamic-mechanical properties and based on an isocyanate component consisting essentially of 4,4'-MDI and also further customary constituents has, after heating at from 100 to 120.degree. C. for from 8 to 24 hours, a melting range of from 130.degree. C. as the minimum lower limit to 230.degree. C. as a minimum upper limit, measured by differential scanning calorimetry (DSC) at a heating rate of 20.degree. C./min, and a urea content of from 14 to 18% by weight.A process is also provided for preparing such a microcellular PU elastomer having improved dynamic mechanical properties. The microcellular PU elastomers can be used for producing damping elements.

Abstract: A microcellular PU elastomer having improved dynamic mechanical properties and based on an isocyanate component consisting essentially of 4,4'-MDI and further customary constituents has a physicochemical structure which, in the gel permeation chromatograph (GPC) of a solution of the microcellular polyurethane elastomer prepared at 90.degree. C. in N,N-dimethylformamide containing 1 percent of di-n-butylamine measured against polymethyl methacrylate (PMMA) as standard, displays a signal occurring in addition to low molecular weight main signal and comprising one or more peaks at an (apparent) molar mass of greater than 250,000 g/mol which becomes smaller or disappears on addition of lithium chloride to this solution, and a urea content of from 14 to 18% by weight.A process is also provided for preparing such a microcellular PU elastomer having improved dynamic mechanical properties. The microcellular PU elastomers can be used for producing damping elements.

Abstract: Thermoplastic polyurethanes are prepared by reacting (a) isocyanates with (b) compounds reactive toward isocyanates, in the presence or absence of (c) chain extenders, (d) catalysts and (e) customary auxiliaries and additives and adding crosslinked polyurethanes in comminuted form before, during and/or after the reaction.

Abstract: In an apparatus for producing foamed plastics parts, a closed mold (1) is filled with polymer molding compound and, after the elapse of a reaction time, the finished part is removed. A plurality of identical molds (1) run on mold carriers (5) through a production installation. For the purpose of reducing the production outlay, a demolding device (11) shared by all the molds (1) is brought into operative connection successively with the molds (1) and in each case one mold (1) is opened. The movements required in this operation are executed by the demolding device (11). An unlocking unit (19) and a swiveling unit (20) of the demolding device (11) are brought into engagement with the mold (1) by a positioning unit (21), after which the mold (1) is unlocked and one mold half (1a) of the mold (1) is swung open. For unlocking the mold (1), the latter is raised against spring force and a positive locking is brought out of engagement.

Abstract: 4,4'-disubstituted bis(2,6-diisopropylphenyl)carbodiimides of the formula (I) ##STR1## where R is 1-methyl-1-phenylethyl, phenoxy or tert-butyl, a process for their preparation, their use as stabilizers against hydrolytic degradation of polyaddition and polycondensation products containing ester groups, and the novel 4-(1-methyl-1-phenylethyl)-2,6-diisopropyl-, 4-phenoxy-2,6-diisopropyl- and 4-tert-butyl-2,6-diisopropylphenyl isocyanates which can be used for their preparation.

Abstract: 4,4'-disubstituted bis-(2,6-diisopropylphenyl)carbodiimides of the formula (I) ##STR1## where R is 1-methyl-1-phenylethyl, phenoxy or tert-butyl, a process for their preparation, their use as stabilizers against hydrolytic degradation of polyaddition and polycondensation products containing ester groups, and the novel 4-(1-methyl-1-phenylethyl)-2,6-diisopropyl-, 4-phenoxy-2,6-diisopropyl- and 4-tert-butyl-2,6-diisopropylphenyl isocyanates which can be used for their preparation.

Abstract: Novel carbodiimides and/or oligomeric polycarbodiimides containing terminal isocyanate, urethane and/or urea groups are obtainable, for example, by condensation of 1,3-bis(1-methyl-1-isocyanatoethyl)benzene with elimination of carbon dioxide followed, if desired, by reaction of all or some of the free isocyanate groups of the resultant (poly)carbodiimides with aliphatic, cycloaliphatic or araliphatic amines, alcohols and/or alkoxypolyoxyalkylene alcohols, and are used as stabilizers against hydrolytic degradation of polyaddition and polycondensation products containing ester groups.

Abstract: 4,4'-disubstituted bis-2,6-diisopropylphenyl)carbodiimides of the formula (I) ##STR1## where R is 1-methyl-1-phenylethyl, phenoxy or tert-butyl, a process for their preparation, their use as stabilizers against hydrolytic degradation of polyaddition and polycondensation products containing ester groups, and the novel 4-(1-methyl-1-phenylethyl)-2,6-diisopropyl-, 4-phenoxy-2,6-diisopropyl- and 4-tert-butyl-2,6-diisopropylphenyl isocyanates which can be used for their preparation.

Abstract: There is now provided a carbodiimide or polycarbodiimide of the formula: ##STR1## where the R radicals are identical or different and are selected from the group consisting of --NHCONHR.sup.1 --, --NHCONR.sup.1 R.sup.2 --, and --NHCOOR.sup.3 --, where R.sup.1 and R.sup.2 may be identical or different and are alkyl, cycloalkyl, or aralkyl, and R.sup.3 is identical to R.sup.1 or is alkoxypolyoxyalkylene, and n is an integer from 0 to 10.There is also provided an ester containing plastic which contains this carbodiimide as an anti-hydrolysis agent. The plastics may be a polyurethane cellular or non-cellular elastomer or thermoplastic.

Abstract: The present invention relates to novel carbodiimides or oligomeric polycarbodiimides containing terminal isocyanate, urea and/or urethane groups, methods for their preparation, and their use as hydrolysis stabilizers.

Abstract: The invention pertains to drip retardant flexible polyurethane foams prepared by the reaction of an isocyanate with a polyol resin containing a drip retardant made of either a trialkyl end-capped amine functional silicone polymer or a trialkly end-capped carbinol functional silicone polymer to effectively prevent the foam from dripping while burning and encourage char formation.