Abstract: The invention relates to a UV additive for aminoplast resins, to a method for producing a UV additive as well as to uses thereof. Said UV additive contains soluble sterically-hindered nitroxyl compounds in an aqueous aminoplast precondensate. A UV additive for aminoplast resins with several application forms is thus obtained.

Abstract: Aminoplast resins are cured using inorganic particles as curing agents. The inorganic particles have a laminated structure and include interlamellarly exchangeable cations such as alkali cations, alkaline-earth cations, aluminum cations, iron cations and/or manganese cations. The aminoplast resins may be cured to produce semi-finished products and molding materials.

Abstract: The invention relates to polymer modified inorganic particles with a layer structure with an average particle diameter of 5 nm to 20,000 nm, containing 20 to 5000 mass % interlamellarly, in relation to the anhydrous inorganic particle, of a mixture of aminoplasts and water. These polymer modified inorganic particles are produced by swelling the inorganic particles with aldehydes and then reacting the inorganic particles with multifunctional C1–C30 amino compounds. The invention also relates to plastic containing polymer modified particles with a layer structure and to semi-finished products and moulded material produced from the same.

Abstract: The invention relates to products, especially moulding materials of polymers containing triazine segments and consisting of mixtures of meltable 4–18 ring oligotriazine ethers which are soluble in highly polar solvents, and in which the triazine rings are predominantly linked by alkylene diamino groups. Said moulding materials can contain up to 50 mass % of other reactive polymers such as ethylene copolymers, maleic acid anhydride copolymers, modified maleic acid anhydride copolymers, poly(meth)acrylates, polyamides, polyester and/or polyurethanes, up to 75 mass % of filling materials and/or reinforcing fibres, and up to 2 mass % of stabilisers, UV absorbers and/or auxiliary agents. The moulding materials of polymers containing triazine segments can be processed by means of conventional fusion methods and can be used as hot-melt adhesives and for producing plates, tubes, profiles, injection moulded parts, fibres, coatings and foamed material.

Abstract: The invention relates to modified inorganic particles with a layer structure with an average particle diameter of 5 nm to 20000 nm, comprising an outer shell consisting of aminoplasts which contain, interlamellarly, multifunctional C1–C30 amino compounds of the melamine, melamine derivative, urea, urea derivative, guanidine, guanidine derivative, cyanamide, dicyandiamide, sulphonamide and/or aniline-type. The invention also relates to the production of said modified inorganic particles and to their use in thermoplastics and duroplastics.

Abstract: Mixtures of triazine derivatives free from polyalkylene oxide Mixtures of triazine derivatives free from polyalkylene oxide are produced from 20 to 70 percent by weight of triazine derivatives with hydroxyalkyl amino groups and 80 to 30 percent by weight of triazine derivatives with bis(hydroxyalkyl) imino groups by catalytic reaction of alkylpropylene oxides with triazine derivatives at a melamine derivative/alkylpropylene oxide molar ratio of 1:1.5 to 1:10 in the presence of metal alkyls, metal hydrides, metal alcoholates and/or metal alkylamides as catalysts. The triazine derivative/hydroxy group mixtures free from polyalkylene oxide are particularly suited for producing plastic materials, flame retardants, additives, pharmaceuticals, textile auxiliaries, and paints or finishes.

Abstract: Polymers are prepared from A) 60 to 95 percent by weight of a mixture including A1) 20 to 70 percent by weight of hydroxyalkyl amino triazines and A2) 30 to 80 percent by weight of bis(hydroxyalkyl) amino triazines B) 5 to 40 percent by weight of polyfunctional compounds selected from one or more of B1) polyisocyanates and/or oligomeric polyesters or polyethers with isocyanate end groups, B2) aliphatic dicarboxylic acids, esters, chlorides or anhydrides, or aromatic polybasic acids, esters, chlorides or anhydrides, B3) aliphatic or aromatic diglycidal compounds or triglycidyl compounds, and, optionally, C) 1 to 20 percent by weight of aliphatic, cycloaliphatic or aromatic dihydroxy compounds, polyalkylene glycols and aliphatic aldehydes.

Abstract: Use of modified olefin polymers for production of polyolefin products with improved toughness, strength and heat resistance. Polyolefin products with high requirements for toughness, strength and heat resistance, produced from modified olefin polymers based on modified propylene polymers which have been modified by reaction with bifunctional monomers in the presence of free-radical generators in the solid phase. The polyolefin products are particularly suitable for shock-absorbing components of motor vehicles, such as bumpers, spoilers and side edge protection elements.

Abstract: Use of modified olefin polymers for production of polyolefin products with improved toughness, strength and heat resistance. Polyolefin products with high requirements for toughness, strength and heat resistance, produced from modified olefin polymers based on modified propylene polymers which have been modified by reaction with bifunctional monomers in the presence of free-radical generators in the solid phase. The polyolefin products are particularly suitable for shock-absorbing components of motor vehicles, such as bumpers, spoilers and side edge protection elements.

Abstract: Polyolefin fibers and polyolefin yarns of high strength and elongation and textile fabrics produced therefrom, which consist of modified propylene polymers, unmodified propylene polymers and adjuvants, are produced by melting the polyolefin mixtures in the extruder, transferring the melt by extrusion pumps to the spinnerets and drawing off the extruded filaments by high-speed galettes and/or winders.

Abstract: Modified polypropylenes of improved processability are produced by a continuous method by absorptively charging polypropylene particles at 20° to 120° C. with a gas mixture, which contains oxygen and bifunctional, unsaturated monomers, and melting the mixture. The modified polypropylenes of improved processability as well as mixtures with unmodified polypropylenes are suitable for the production of films, sheets, fibers, panels, coatings, pipes, hollow objects and foamed materials.

Abstract: Structurally isomeric poly(alkyl ethylenes) with H and Y structures, polymeric bridging segments and a Y index of 2×10−3 to 8×10−3 (kJ/mole/degree), have decreased instability in the melt and more advantageous processing properties. The structurally isomeric poly(alkyl ethylenes) with H and Y structures are synthesized by an irradiating method, a melt reaction method or a solid phase reaction method by reacting poly(alkyl ethylenes) with 0.05 to 5% by weight of monofunctional, difunctional and polyfunctional monomers, optionally in the presence of peroxides. The structurally isomeric poly(alkyl ethylenes) are suitable for producing films, sheets, panels, coatings, pipes, hollow objects and foams.

Abstract: Heterophasic polyolefin alloys, with a semi-interpenetrating network structure and an outstanding combination of high stiffness, low temperature toughness and optionally a low coefficient of thermal expansion of propylene polymers and elastomers, are produced by melt compounding propylene polymers with a co-continuous blend, which contains 5 to 60% by weight of gel and was produced by reacting mixtures of propylene polymers and elastomeric polyolefins or styrene butadiene ethylene terpolymers with ethylenically unsaturated, hydrolyzable organosilane compounds in the presence of silanol condensation catalysts. Heterophasic polyolefin alloys are suitable for the production of films, sheets, fibers, panels, coatings, injection molded article, pipes, hollow objects and foams.

Abstract: Polyolefin fibers and polyolefin yarns of high strength and elongation and textile fabrics produced therefrom, which consist of modified propylene polymers, unmodified propylene polymers and adjuvants, are produced by melting the polyolefin mixtures in the extruder, transferring the melt by extrusion pumps to the spinnerets and drawing off the extruded filaments by high-speed galettes and/or winders.

Abstract: Thermoplastic elastomers of good dyeability and high strength and elasticity, the incorporated elastomeric particles of which have and average particle diameter of 0.05 to 5 &mgr;m. The thermoplastic elastomers are formed according to a method in which mixtures of propylene homopolymers and/or propylene copolymers, elastomeric C4 C12 olefin copolymers and/or terpolymers and C8 to C14 diacrylates, C7 to C16 diallyl compounds, C9 to C15 dimethacrylates, C7 to C10 divinyl compounds, C12 to C17 acrylate esters of polyalcohols, C15 to C21 methacrylate esters of polyalcohols and/or C9 C12 triallyl compounds are added to a melt. The thermoplastic elastomers, as well as mixtures of the thermoplastic elastomers with conventional polyolefins, are suitable for use in the vehicle industry, in the domestic appliances industry, in the construction industry and in medical technology.

Abstract: Structurally isomeric poly(alkyl ethylenes) with H and Y structures, polymeric bridging segments and a &PSgr; index of 2×10−3 to 8×10−3 (kJ/mole/degree), have decreased instability in the melt and more advantageous processing properties.

Abstract: Thermoplastic elastomers of high strength, high elasticity and good dyeability, the incorporated elastomeric particles of which have an average particle diameter of 0.05 to 5 &mgr;m, from propylene homopolymers and/or propylene copolymers, elastomeric C2 to C8 olefin copolymers and/or terpolymers and multifunctional, unsaturated monomers are formed by a method, for which mixtures of propylene homopolymers and/or propylene copolymers, elastomeric C2 to C8 olefin copolymers and/or terpolymers and readily volatile C4 to C7 dienes are reacted in the melt. The thermoplastic elastomers, as well as mixtures with conventional polyolefins, are suitable for use in the vehicle industry, in the domestic appliances industry, in the building sector and in medical technology.

Abstract: Polyolefin foam materials of high dimensional stability at elevated temperatures are produced from modified polypropylenes and unmodified polypropylenes. The modified polypropylenes used are produced by mixing polypropylene particles with thermally decomposing free radical-forming agents, absorbing readily volatile bifunctional monomers and heating and melting the mixture. Areas of application for the polyolefin foam materials of high dimensional stability at elevated temperatures are the packaging sector, motor vehicle parts, sports and leisure equipment, industrial applications, as well as applications in the building sector.

Abstract: Polyolefin fibers and polyolefin yarns of high strength and elongation and textile fabrics produced therefrom. Polyolefin fibers and polyolefin yarns of high strength and elongation and textile fabrics produced therefrom, which consist of modified propylene polymers, unmodified propylene polymers and adjuvants, are produced by melting the polyolefin mixtures in the extruder, transferring the melt by extrusion pumps to the spinnerets and drawing off the extruded filaments by high-speed galettes and/or winders. The polyolefin fibers and polyolefin yarns of high strength and elongation and the textile fabrics produced therefrom are suitable for the production of textiles for the home, multilayered textiles, industrial textiles, nonwoven materials in medicine and hygiene and elastic hygiene articles.

Abstract: Modified polypropylenes of improved processability are produced by a continuous method by absorptively charging polypropylene particles at 20° to 120° C. with a gas mixture, which contains oxygen and bifunctional, unsaturated monomers, and melting the mixture. The modified polypropylenes of improved processability as well as mixtures with unmodified polypropylenes are suitable for the production of films, sheets, fibers, panels, coatings, pipes, hollow objects and foamed materials.