Abstract: Certain methods enable the production of steel components with well-adhering metallic coatings that protect against corrosion. In some examples, a flat steel product produced from a steel material having a yield point of 150-1100 MPa and a tensile strength of 300-1200 MPa may be coated with an anticorrosion coating of an alloy that comprises 35-70% by weight aluminum, 35-60% by weight zinc, 0.1-10% by weight magnesium, up to 10% by weight Si, and up to 5% by weight Fe. A blank obtained from the flat steel product may then be heated to at least 800° C. and formed into a steel component. Alternatively, the steel component may be formed into the steel component first and then heated to at least 800° C. Regardless, the steel component may then be hardened by sufficiently rapid cooling the steel component from a sufficiently high temperature.

Abstract: A process for producing a component from a steel product coated with a protective Al—Si coating, and an intermediate product that arises during the course of such a process and that can be used to produce components of the type concerned here. The steel product coated with the Al—Si coating, undergoes a first heating stage in which the temperature and the duration of the heat treatment are set such that the Al—Si coating is only partially pre-alloyed with Fe from the steel product. Then, the steel product, in a second heating stage, is heated to a heating temperature, above the Ac1 temperature, at which the steel product has an at least partially austenitic structure, wherein the temperature and the duration of the second heating stage are set such that the Al—Si coating is fully alloyed with Fe from the steel product.

Abstract: A process for producing a component from a steel product coated with a protective Al—Si coating, and an intermediate product that arises during the course of such a process and that can be used to produce components of the type concerned here. The steel product coated with the Al—Si coating, undergoes a first heating stage in which the temperature and the duration of the heat treatment are set such that the Al—Si coating is only partially pre-alloyed with Fe from the steel product. Then, the steel product, in a second heating stage, is heated to a heating temperature, above the Ac1 temperature, at which the steel product has an at least partially austenitic structure, wherein the temperature and the duration of the second heating stage are set such that the Al—Si coating is fully alloyed with Fe from the steel product.