Abstract: A chalcogenide glass composition composed of arsenic (As), selenium (Se), sulfur (S), and antimony (Sb) is presented. The composition includes arsenic in the range from 25% to 45% by weight relative to the total weight of the composition, selenium in the range from 40% to 65% by weight relative to the total weight of the composition, sulfur in the range from 2% to 15% by weight relative to the total weight of the composition, and antimony in the range from 0% to 15% by weight relative to the total weight of the composition. The variability of constituents on a weight basis is greater than the related arts, thus facilitating a broader range of design options. The glass composition is preferred to have a thermal expansion coefficient of about 23.6×10?6/° C., a temperature coefficient of refractive index less than about 1×10?6/° C., a glass transition temperature less than 200 degrees Celsius, and/or a glass softening temperature less than 250 degrees Celsius.

Abstract: A chalcogenide glass composition composed of arsenic (As), selenium (Se), sulfur (S), and antimony (Sb) is presented. The composition includes arsenic in the range from 25% to 45% by weight relative to the total weight of the composition, selenium in the range from 40% to 65% by weight relative to the total weight of the composition, sulfur in the range from 2% to 15% by weight relative to the total weight of the composition, and antimony in the range from 0% to 15% by weight relative to the total weight of the composition. The variability of constituents on a weight basis is greater than the related arts, thus facilitating a broader range of design options. The glass composition is preferred to have a thermal expansion coefficient of about 23.6×10?6/° C., a temperature coefficient of refractive index less than about 1×10?6/° C., a glass transition temperature less than 200 degrees Celsius, and/or a glass softening temperature less than 250 degrees Celsius.

Abstract: A compact, inexpensive and rugged fiber collimating lens and lens array achieve large beam diameters and provide long working distances. A special single-mode fiber is inserted between a standard single-mode input fiber and a GRIN fiber lens, typically quarter-pitch or slightly longer. The specialty fiber condenses the mode field diameter (MFD) of the beam in the input fiber into its smaller MFD. As a result, the fiber collimating lens provides greater beam expansion due to the larger divergence angle of the specialty fiber, which in turn provides longer working distances.

Abstract: A compact, inexpensive and rugged fiber collimating lens and lens array achieve large beam diameters and provide long working distances. A special single-mode fiber is inserted between a standard single-mode input fiber and a GRIN fiber lens, typically quarter-pitch or slightly longer. The specialty fiber condenses the mode field diameter (MFD) of the beam in the input fiber into its smaller MFD. As a result, the fiber collimating lens provides greater beam expansion due to the larger divergence angle of the specialty fiber, which in turn provides longer working distances.