Abstract: A Fischer-Tropsch catalyst, useful for conversion of synthesis gas to olefins, is prepared from a catalyst precursor composition including iron oxide and an alkali metal on a substantially inert support, and then treated by a process including as ordered steps (1) reduction in a hydrogen-containing atmosphere at a pressure of 0.1 to 1 M Pa and a temperature from 280° C. to 450° C.; (2) carburization in a carbon monoxide-containing atmosphere at a pressure from 0.1 to 1 M Pa and a temperature from 200° C. to less than 340° C.; and (3) conditioning in a hydrogen- and carbon monoxide-containing atmosphere at a pressure from 0.1 to 2 MPa and a temperature from 280° C. to 340° C.

Abstract: A Fischer-Tropsch catalyst, useful for conversion of synthesis gas to olefins, is prepared from a catalyst precursor composition including iron oxide and an alkali metal on a substantially inert support, and then treated by a process including as ordered steps (1) reduction in a hydrogen-containing atmosphere at a pressure of 0.1 to 1 M Pa and a temperature from 280° C. to 450° C.; (2) carburization in a carbon monoxide-containing atmosphere at a pressure from 0.1 to 1 M Pa and a temperature from 200° C. to less than 340° C.; and (3) conditioning in a hydrogen- and carbon monoxide-containing atmosphere at a pressure from 0.1 to 2 MPa and a temperature from 280° C. to 340° C.