Abstract: The invention relates to a coating mixture for applying a polymeric, corrosion-preventing protective layer to a metallic base for protecting an edge area, a soldered point, a weld seam or a repair point or for sealing the seam of one or more optionally interjoined strips, metal sheets or shaped parts.

Abstract: A process for protecting an edge area, a soldered point, a weld seam or a repair point or for sealing a seam of one or more optionally interjoined strips, metal sheets or shaped parts, containing the steps of applying a coating mixture to at least a part of a surface of a metallic substrate, applying actinic radiation, and forming a firmly adhering, ductile, corrosion-preventing coating on the substrate.

Abstract: The invention relates to a coating mixture for applying a polymeric, corrosion-preventing protective layer to a metallic base for protecting an edge area, a soldered point, a weld seam or a repair point or for sealing the seam of one or more optionally interjoined strips, metal sheets or shaped parts.

Abstract: The invention relates to a mixture for applying a polymer, non-corrosive, electroconductive coating which can be shaped in a low-abrasive manner, to a base. Said mixture contains at least one substance A in the form of electroconductive hard particles, at least one substance B in the form of very soft or soft, inorganic, sliding, electroconductive or semiconductive particles, and/or at least one substance C in the form of metallic, soft or hard, electroconductive or semiconductive particles and/or soot, and optionally other constituents such as an anticorrosion pigment D, the sum of the parts by weight of the inorganic sliding particles B and the metallic particles and/or soot C amounting to between 0.25 and 99.5% of the parts by weight of the water-insoluble or only slightly water-soluble pigmentation S (A+B+C), and the size of the electroconductive hard particles A amounting to less than 10 ?m in relation to the particle size transfer value d99.

Abstract: A method for coating metallic surfaces with a paint or paint-like coating prior to forming.

Abstract: The invention relates to a method for coating a metallic strip. The strip or optionally, the strip sections produced from said strip in the subsequent process, is/are first coated with at least one anticorrosion layer—according to an alternative form of embodiment, this can be left out—and then with at least one layer of a paint-like coating containing polymers. After being coated with at least one anticorrosion layer or after being coated with at least one layer of a paint-like coating, the strip is divided into strip sections. The coated strip sections are then formed, joined and/or coated with at least one (other) paint-like coating and/or paint coating.

Abstract: The invention relates to a coating mixture for applying a polymeric, corrosion-preventing protective layer to a metallic base for protecting an edge area, a soldered point, a weld seam or a repair point or for sealing the seam of one or more optionally interjoined strips, metal sheets or shaped parts.

Abstract: The invention relates to a coating mixture for applying a polymeric, corrosion-preventing protective layer to a metallic base for protecting an edge area, a soldered point, a weld seam or a repair point or for sealing the seam of one or more optionally interjoined strips, metal sheets or shaped parts.

Abstract: A method for coating metallic surfaces with a paint or paint-like coating prior to forming.

Abstract: A method for coating a metal strip or strip sections produced from the strip in a subsequent step are first coated with at least one anticorrosive coating and then with at least one coating of a paint-like polymer-containing coating. The coated strip is divided up in strip sections and the coated strip sections are then formed, joined and/or coated with at least one further paint-like coating and/or coat of paint. The paint-like coating is an aqueous dispersion that contains, in addition to water, at least one UV-crosslinkable water-soluble and/or water-dispersible resin, at least one wax as the forming additive, at least one photoinitiator, and at least one corrosion inhibitor. The coating is dried and, In another embodiment, the strip is first coated with at least one paint-like polymer containing coating without prior application of an anticorrosive coating.

Abstract: The invention relates to a mixture for applying a polymer, non-corrosive, electroconductive coating which can be shaped in a low-abrasive manner, to a base. Said mixture contains at least one substance A in the form of electroconductive hard particles, at least one substance B in the form of very soft or soft, inorganic, sliding, electroconductive or semiconductive particles, and/or at least one substance C in the form of metallic, soft or hard, electroconductive or semiconductive particles and/or soot, and optionally other constituents such as an anticorrosion pigment D, the sum of the parts by weight of the inorganic sliding particles B and the metallic particles and/or soot C amounting to between 0.25 and 99.5% of the parts by weight of the water-insoluble or only slightly water-soluble pigmentation S (A+B+C), and the size of the electroconductive hard particles A amounting to less than 10 ?m in relation to the particle size transfer value d99.

Abstract: The invention relates to a coating mixture for applying a polymeric, corrosion-preventing protective layer to a metallic base for protecting an edge area, a soldered point, a weld seam and/or a repair point or for sealing the seam of one or more optionally interjoined strips, metal sheets and/or shaped parts. According to the invention, the coating mixture is largely or entirely free of water and/or of organic solvents, whereby it contains at least one radically polymerizable binding agent and at least one compound that forms free radicals when subjected to the action of actinic radiation. This radically polymerizable compound is largely or completely cured with the formed free radicals when subjected to actinic irradiation.

Abstract: The invention relates to a method for coating a metallic strip. The strip or optionally, the strip sections produced from said strip in the subsequent process, is/are first coated with at least one anticorrosion layer—according to an alternative form of embodiment, this can be left out—and then with at least one layer of a paint-like coating containing polymers. After being coated with at least one anticorrosion layer or after being coated with at least one layer of a paint-like coating, the strip is divided into strip sections. The coated strip sections are then formed, joined and/or coated with at least one (other) paint-like coating and/or paint coating.

Abstract: The invention relates to a method for coating a metal strip for use in the automotive, aircraft or aerospace industry. The strip or the strip sections produced on the basis thereof in a later step is/are first coated with at least one anticorrosive coating and then with at least one coating of a paint-like polymer-containing coating. The strip, once coated with at least one anticorrosive coating or once coated with at least one coat of a paint-like coating, is divided up in strip sections. Said coated strip sections are then formed, joined and/or coated with at least one (further) paint-like coating and/or coat of paint. The paint-like coating is achieved by coating the surface with an aqueous dispersion that contains, in addition to water, at least one UV-crosslinkable water-soluble and/or water-dispersible resin, at least one wax as the forming additive, at least one photoinitiator, and at least one corrosion inhibitor.

Abstract: A method is disclosed for applying phosphate coatings to surfaces of zinc, iron, aluminum, and the alloys thereof by wetting with a phosphatizing solution containing divalent cations and phosphate to form a liquid film, and subsequently drying on the liquid film wherein the metal surfaces are wetted with a phosphatizing solution, which is free from elements of sub-groups 5 and 6 of the Periodic Table, said phosphatizing solution containing:0.5 to 8 g/l nickel;2 to 20 g/l manganese;18 to 170 g/l of phosphate (calculated as P.sub.2 O.sub.5);and has an acid number of 0.4 to 0.8, such that after drying on, a phosphate layer having a weight per unit area of 0.3 to 3.0 g/m.sup.2, is obtained, where in the case of phosphatizing surfaces of iron, aluminum or the alloys thereof, the phosphatizing solution necessarily contains 0.5 to 5 g/l of zinc, and in the case of phosphatizing surfaces of zinc or zinc alloys the phosphatizing solution either contains zinc or is free from zinc.