Abstract: The present invention is related generally to recovering metals from waste electronics, and more particularly to a process to recover copper and gold commonly found in waste printed circuit boards using a lixiviant containing a weak acid such as citric acid or acetic acid, a particular concentration of table salt and an oxidizer. By using this lixiviant, the copper found in the printed circuit board reacts to form copper salts and gold becomes detached. Importantly this recovery method of copper and gold found in waste PCBs is fast, does not pose environmental hazards and is economically feasible.

Abstract: The present invention is related generally to recovering metals from waste electronics, and more particularly to a process to recover copper and gold commonly found in waste printed circuit boards using a lixiviant containing a weak acid such as citric acid or acetic acid, a particular concentration of table salt and an oxidizer. By using this lixiviant, the copper found in the printed circuit board reacts to form copper salts and gold becomes detached. Importantly this recovery method of copper and gold found in waste PCBs is fast, does not pose environmental hazards and is economically feasible.

Abstract: The present invention is related generally to recovering metals from waste electronics, and more particularly to a process to recover copper and gold commonly found in waste printed circuit boards using a lixiviant containing a weak acid such as citric acid or acetic acid, a particular concentration of table salt and an oxidizer. By using this lixiviant, the copper found in the printed circuit board reacts to form copper salts and gold becomes detached. Importantly this recovery method of copper and gold found in waste PCBs is fast, does not pose environmental hazards and is economically feasible.

Abstract: The present invention is related generally to recovering metals from waste electronics, and more particularly to a process to recover copper and gold commonly found in waste printed circuit boards using a lixiviant containing a weak acid such as citric acid or acetic acid, a particular concentration of table salt and an oxidizer. By using this lixiviant, the copper found in the printed circuit board reacts to form copper salts and gold becomes detached. Importantly this recovery method of copper and gold found in waste PCBs is fast, does not pose environmental hazards and is economically feasible.

Abstract: An improved overcoat layer for an organic photoconductor drum of an electrophotographic image forming device is provided. The overcoat layer is prepared from a curable composition including a crosslinkable siloxane, nano metal oxide particles sized less than 400 nm in combination with a urethane acrylate resin having at least 6 functional groups. The outermost layer of an organic photoconductors is coated with the overcoat formulation of the present invention then cured. The resulting cured overcoated organic photoconductor has improved wear resistance and importantly does not negatively altering the electrophotographic properties of the organic photoconductor.

Abstract: An improved overcoat layer for an organic photoconductor drum of an electrophotographic image forming device is provided. The overcoat layer is prepared from a curable composition including a crosslinkable siloxane, nano metal oxide particles sized less than 400 nm in combination with a urethane acrylate resin having at least 6 functional groups. The outermost layer of an organic photoconductors is coated with the overcoat formulation of the present invention then cured. The resulting cured overcoated organic photoconductor has improved wear resistance and importantly does not negatively altering the electrophotographic properties of the organic photoconductor.

Abstract: An improved overcoat layer for an organic photoconductor drum of an electrophotographic image forming device is provided. The overcoat layer is prepared from a curable composition including a crosslinkable siloxane, nano metal oxide particles sized less than 400 nm in combination with a urethane acrylate resin having at least 6 functional groups. The outermost layer of an organic photoconductors is coated with the overcoat formulation of the present invention then cured. The resulting cured overcoated organic photoconductor has improved wear resistance and importantly does not negatively altering the electrophotographic properties of the organic photoconductor.

Abstract: An improved overcoat layer for an organic photoconductor drum of an electrophotographic image forming device is provided. The overcoat layer is prepared from a curable composition including a crosslinkable siloxane, nano metal oxide particles sized less than 400 nm in combination with a urethane acrylate resin having at least 6 functional groups. The outermost layer of an organic photoconductors is coated with the overcoat formulation of the present invention then cured. The resulting cured overcoated organic photoconductor has improved wear resistance and importantly does not negatively altering the electrophotographic properties of the organic photoconductor.

Abstract: An improved overcoat layer for an organic photoconductor drum of an electrophotographic image forming device is provided. The overcoat layer is prepared from a curable composition including a crosslinkable siloxane, an acrylic polymer with pigment affinic groups, nano metal oxide particles sized less than 400 nm in combination with a urethane acrylate resin having at least 6 functional groups. The outermost layer of an organic photoconductors is coated with the overcoat formulation of the present invention then cured. The resulting cured overcoated organic photoconductor has improved wear resistance and importantly does not negatively altering the electrophotographic properties of the organic photoconductor.

Abstract: An improved overcoat layer for an organic photoconductor drum of an electrophotographic image forming device is provided. The overcoat layer is prepared from a curable composition including a crosslinkable siloxane, nano metal oxide particles sized less than 400 nm in combination with a urethane acrylate resin having at least 6 functional groups. The outermost layer of an organic photoconductors is coated with the overcoat formulation of the present invention then cured. The resulting cured overcoated organic photoconductor has improved wear resistance and importantly does not negatively altering the electrophotographic properties of the organic photoconductor.

Abstract: An improved overcoat layer for an organic photoconductor drum of an electrophotographic image forming device is provided. The overcoat layer is prepared from a curable composition including a crosslinkable siloxane, an acrylic polymer with pigment affinic groups, nano metal oxide particles sized less than 400 nm in combination with a urethane acrylate resin having at least 6 functional groups. The outermost layer of an organic photoconductors is coated with the overcoat formulation of the present invention then cured. The resulting cured overcoated organic photoconductor has improved wear resistance and importantly does not negatively altering the electrophotographic properties of the organic photoconductor.

Abstract: An improved overcoat layer for an organic photoconductor drum of an electrophotographic image forming device is provided. The overcoat layer is prepared from a curable composition including a crosslinkable siloxane, an acrylic polymer with pigment affinic groups, nano metal oxide particles sized less than 400 nm in combination with a urethane acrylate resin having at least 6 functional groups. The outermost layer of an organic photoconductors is coated with the overcoat formulation of the present invention then cured. The resulting cured overcoated organic photoconductor has improved wear resistance and importantly does not negatively altering the electrophotographic properties of the organic photoconductor.

Abstract: An improved overcoat layer for an organic photoconductor drum of an electrophotographic image forming device is provided. The overcoat layer is prepared from a curable composition including a crosslinkable siloxane, an acrylic polymer with pigment affinic groups, nano metal oxide particles sized less than 400 nm in combination with a urethane acrylate resin having at least 6 functional groups. The outermost layer of an organic photoconductors is coated with the overcoat formulation of the present invention then cured. The resulting cured overcoated organic photoconductor has improved wear resistance and importantly does not negatively altering the electrophotographic properties of the organic photoconductor.

Abstract: An improved overcoat layer for an organic photoconductor drum of an electrophotographic image forming device is provided. The overcoat layer is prepared from a curable composition including a crosslinkable siloxane, an acrylic polymer with pigment affinic groups, nano metal oxide particles sized less than 400 nm in combination with a urethane acrylate resin having at least 6 functional groups. The outermost layer of an organic photoconductors is coated with the overcoat formulation of the present invention then cured. The resulting cured overcoated organic photoconductor has improved wear resistance and importantly does not negatively altering the electrophotographic properties of the organic photoconductor.

Abstract: An improved overcoat layer for an organic photoconductor drum of an electrophotographic image forming device is provided. The overcoat layer is prepared from a curable composition including a crosslinkable siloxane, an acrylic polymer with pigment affinic groups, nano metal oxide particles sized less than 400 nm in combination with a urethane acrylate resin having at least 6 functional groups. The outermost layer of an organic photoconductors is coated with the overcoat formulation of the present invention then cured. The resulting cured overcoated organic photoconductor has improved wear resistance and importantly does not negatively altering the electrophotographic properties of the organic photoconductor.

Abstract: The present invention related to generally to a process to recover metals from waste electronics, and more particularly a process to recover gold from waste electronics. The gold is first delaminated in a first step using a solution containing a weak acid in combination with an oxidizer. The second step isolates and purifies the delaminated gold from the chip debris using solvents, water and a wetting agent/surfactant. The proposed two step method of gold recovery from electronic waste is effective without the need for strong or costly chemicals or leaching.

Abstract: The present invention related to generally to a process to recover metals from waste electronics, and more particularly a process to recover gold from waste electronics. The gold is first delaminated in a first step using a solution containing a weak acid in combination with an oxidizer. The second step isolates and purifies the delaminated gold from the chip debris using solvents, water and a wetting agent/surfactant. The proposed two step method of gold recovery from electronic waste is effective without the need for strong or costly chemicals or leaching.

Abstract: A charge transport molecule contains four radical polymerizable functional groups of the general structure exemplified below: where R1 and R2 contain a spacer group and a radical polymerizable functional group, R3 and R4 are hydrogen atoms, and R5 and R6 contain a spacer group and a radical polymerizable functional group wherein the spacer group of R1, R2, R5 and R6 is an ethyl group and the radical polymerizable functional group of R1, R2, R5 and R6 is an acrylate group.

Abstract: An overcoat layer for an organic photoconductor drum includes a curable composition having about 20 to about 80 percent by weight of a charge transport molecule containing four radical polymerizable functional groups as exemplified below: where R1 and R2 contain a spacer group and a radical polymerizable functional group, R3 and R4 are hydrogen atoms, and R5 and R6 contain a spacer group and a radical polymerizable functional group. The curable composition may also include a non-radical polymerizable additive, such as a surfactant, and/or a curing agent.

Abstract: An improved organic photoconductor drum having a protective overcoat layer and method to make the same is provided. The protective overcoat layer is prepared from a curable composition including nano metal oxide particles sized less than 400 nm in combination with an urethane acrylate resin having at least 6 functional groups.