Abstract: A silver halide industrial radiographic material comprising on at least one side of a support a hydrophilic gelatinous non-spectrally sensitized radiation-sensitive emulsion layer, having grains, coated in a total amount in the range from 6 to 20 g, expressed as an equivalent amount of silver nitrate per square meter, and at least one non-radiation sensitive protective gelatinous antistress overcoat layer thereupon, wherein a ratio of gelatin to silver, expressed as silver nitrate in the said layer arrangement is at least 0.70, wherein said gelatinous layers are hardened by a gelatin cross-linking agent in an amount in order to have a dissolving time of at least 40 minutes, said time being defined as the period of time from the moment when the silver halide photographic material, dipped into 50 ml of an aqueous solution of 1.5% by weight of sodium hydroxide at 50° C.

Abstract: A silver halide industrial radiographic material comprising on at least one side of a support a hydrophilic gelatinous non-spectrally sensitized radiation-sensitive emulsion layer, having grains, coated in a total amount in the range from 6 to 20 g, expressed as an equivalent amount of silver nitrate per square meter, and at least one non-radiation sensitive protective gelatinous antistress overcoat layer thereupon, wherein a ratio of gelatin to silver, expressed as silver nitrate in the said layer arrangement is at least 0.70, wherein said gelatinous layers are hardened by a gelatin cross-linking agent in an amount in order to have a dissolving time of at least 40 minutes, said time being defined as the period of time from the moment when the silver halide photographic material, dipped into 50 ml of an aqueous solution of 1.5% by weight of sodium hydroxide at 50 °C.

Abstract: A system has been disclosed for use in radiographic industrial non-destructive testing materials and personal monitoring, making use therefor, of tabular silver brom(oiod)ide emulsion grains having {111} major faces, an average equivalent circular diameter of at least 0.5 &mgr;m and an average thickness of less than 0.30 &mgr;m, having been chemically sensitized by the steps of adding at least a gold salt in order to provide the surface of said tabular grains with at least 6000 atoms of gold per &mgr;m2 of its grain surface and per (0.1 &mgr;m of thickness)2; and at least a sulfite salt in such an amount that the ratio of the number of gold atoms per &mgr;m2 and (concentration of said sulfite salt, expressed in mmole per mole of silver)2 is at least 200000.

Abstract: A direct X-ray system for industrial radiography like non-destructive testing applications, and personal monitoring, being particularly less sensitive to pressure phenomena, has been disclosed, said system consisting of a direct X-ray black-and-white negative-working radiographic film material, comprised of a transparent support coated on at least one side thereof with a tabular grain emulsion layer, substantially free from spectrally sensitizing dyes, in which at least 50 percent of total grain projected area of all grains is accounted for by silver bromoiodide tabular grains having an iodide content of less than 5 mole %, based on silver, having an average aspect ratio of at least 2, and having a volume greater than 0.

Abstract: A direct X-ray system for industrial radiography, like non-destructive testing applications, and personal monitoring, being particularly less sensitive to pressure phenomena, has been disclosed, said system consisting of a direct X-ray black-and-white negative-working radiographic film material, comprised of a transparent support coated on at least one side thereof with a tabular grain emulsion layer, substantially free from spectrally sensitizing dyes, in which at least 50 percent of total grain projected area of all grains is accounted for by silver bromoiodide tabular grains having an iodide content of less than 5 mole %, based on silver, having an average aspect ratio of at least 2, and having a volume greater than 0.

Abstract: A system has been disclosed for use in radiographic industrial non-destructive testing materials and personal monitoring, making use therefor, of tabular silver brom(oiod)ide emulsion grains having {111} major faces, an average equivalent circular diameter of at least 0.5 &mgr;m and an average thickness of less than 0.30 &mgr;m, having been chemically sensitized by the steps of adding at least a gold salt in order to provide the surface of said tabular grains with at least 6000 atoms of gold per &mgr;m2 of its grain surface and per (0.1 &mgr;m of thickness)2; and at least a sulfite salt in such an amount that the ratio of the number of gold atoms per &mgr;m2 and (concentration of said sulfite salt, expressed in mmole per mole of silver)2 is at least 200000.