Abstract: Disclosed herein is a method of pretreatment of a metallic substrate for a subsequent metal cold forming process. The method includes at least steps (1) and (2), namely providing at least one substrate having at least one surface at least partially made of at least one metal (step (1)), contacting the at least one surface of the substrate provided in step (1) with an aqueous lubricant composition (B) (step (2)), where the aqueous lubricant composition (B) includes besides water at least constituents (b1) to (b4) and optionally (b5). Further disclosed herein are a pretreated metallic substrate obtained by the method, a method of cold forming of a metallic substrate, and an aqueous lubricant composition (B).

Abstract: Disclosed herein is a method for pretreatment of a metallic substrate for a subsequent metal cold forming process, said method including (1) providing at least one substrate, (2) contacting the at least one surface of the substrate provided in step (1) with an aqueous lubricant composition (A). and optionally (3) drying the coating film obtained after having performed step (2). Further disclosed herein are a pretreated metallic substrate obtainable by the aforementioned method, a method of cold forming of a metallic substrate including a step of subjecting the inventive pretreated metallic substrate to a cold forming process, an aqueous lubricant composition (A) as defined above, and a master batch for preparing the aqueous composition (A).

Abstract: Methods for treatment shaped bodies are described herein. The methods generally include contacting at least one shaped body with an aqueous acidic composition to form a conversion layer on a surface of the at least one shaped body, wherein the surface includes iron or steel and a carbon content in a range of 0 to 2.06 wt. % and a chrome content in a range of 0 to <10 wt. % and wherein the surface is optionally galvanized or alloy galvanized. The aqueous acidic composition includes water; from 2 to 500 g/L oxalic acid; and from 0.01 to 20 g/L of at least one catalyst based on guanidine, nitrate or combinations thereof, wherein a pickling removal of the aqueous acidic composition is in a range of 1 to 6 g/m2.

Abstract: Methods for treatment shaped bodies are described herein. The methods generally include contacting at least one shaped body with an aqueous acidic composition to form a conversion layer on a surface of the at least one shaped body, wherein the surface includes iron or steel and a carbon content in a range of 0 to 2.06 wt. % and a chrome content in a range of 0 to <10 wt. % and wherein the surface is optionally galvanized or alloy galvanized. The aqueous acidic composition includes water; from 2 to 500 g/L oxalic acid; and from 0.01 to 20 g/L of at least one catalyst based on guanidine, nitrate or combinations thereof, wherein a pickling removal of the aqueous acidic composition is in a range of 1 to 6 g/m2.