Abstract: In a manufacturing method of a valve spring, a coiled valve spring made of an oil-tempered wire is applied with nitriding treatment and is supported to be rotated about its center axis. During a shot peening process of the coiled valve spring, cut wires of Hv 650 to 850 in hardness and 1.0 to 0.6 mm in diameter are shot to the coiled valve spring at a first step, in a roller-type shot machine and cut wires of Hv 650 to 850 in hardness and 0.4 to 0.2 mm in diameter are shot to the coiled valve spring at a second step in a tumbling shot machine, the time for the second step being longer than the time for the first step.

Abstract: The present invention provides, at low cost, a valve spring steel having a tensile strength as high as 210 to 240 kgf/mm.sup.2 after oil tempering. The high strength spring steel comprises, based on weight, 0.65 to 0.85% of C, 1.90 to 2.40% of Si, 0.50 to 1.00% of Mn, 0.70 to 1.30% of Cr, 0.10 to 0.30% of Mo, 0.20 to 0.50% of V, 0.01 to 0.04% of Nb and the balance Fe and unavoidable impurities and is subjected to heating at temperature of 1,050 to 1,250.degree. C. and then to rolling so that carbides in the steel have a size of up to 0.15 .mu.m in terms of equivalent circle. A valve spring having a tensile strength as high as 210 to 240 kgf/mm.sup.2 after oil tempering and stabilized quality can be produced while the material cost is greatly reduced by decreasing costly alloying components as much as possible.