Abstract: A manufacturing method by which alumina-silica based fibers excellent in mechanical strength can be readily and securely obtained. The method obtains precursor fibers as a material by using an alumina-silica based fiber spinning stock solution for use in an inorganic salt method. Next, the precursor fibers are heated under an environment which makes it difficult to carry out an oxidizing reaction on the carbon component contained in the precursor fibers. Thus, the precursor fibers are sintered to obtain alumina-silica based fibers.

Abstract: A manufacturing method by which alumina-silica based fibers excellent in mechanical strength can be readily and securely obtained. The method obtains precursor fibers as a material by using an alumina-silica based fiber spinning stock solution for use in an inorganic salt method. Next, the precursor fibers are heated under an environment which makes it difficult to carry out an oxidizing reaction on the carbon component contained in the precursor fibers. Thus, the precursor fibers are sintered to obtain alumina-silica based fibers.

Abstract: A manufacturing method by which alumina-silica based fibers excellent in mechanical strength can be readily and securely obtained. The method obtains precursor fibers as a material by using an alumina-silica based fiber spinning stock solution for use in an inorganic salt method. Next, the precursor fibers are heated under an environment which makes it difficult to carry out an oxidizing reaction on the carbon component contained in the precursor fibers. Thus, the precursor fibers are sintered to obtain alumina-silica based fibers.

Abstract: A holding seal material which has alumina-silica based fibers aggregated into a mat shape as a constituent element. The holding seal material is placed in a gap between a ceramic body capable of allowing a fluid to flow through the inside thereof and a metal shell covering the outer circumference of the ceramic body. In the holding seal material, a crystallization rate is made different depending on portions of the holding seal material. An outer portion of the holding seal material disposed with respect to the metal shell is crystallized at a lower rate than an inner portion of the holding seal material disposed with respect to the ceramic body.

Abstract: A manufacturing method by which alumina-silica based fibers excellent in mechanical strength can be readily and securely obtained. The method obtains precursor fibers as a material by using an alumina-silica based fiber spinning stock solution for use in an inorganic salt method. Next, the precursor fibers are heated under an environment which makes it difficult to carry out an oxidizing reaction on the carbon component contained in the precursor fibers. Thus, the precursor fibers are sintered to obtain alumina-silica based fibers.

Abstract: A manufacturing method by which alumina-silica based fibers excellent in mechanical strength can be readily and securely obtained. The method obtains precursor fibers as a material by using an alumina-silica based fiber spinning stock solution for use in an inorganic salt method. Next, the precursor fibers are heated under an environment which makes it difficult to carry out an oxidizing reaction on the carbon component contained in the precursor fibers. Thus, the precursor fibers are sintered to obtain alumina-silica based fibers.

Abstract: A manufacturing method by which alumina-silica based fibers excellent in mechanical strength can be readily and securely obtained. The method obtains precursor fibers as a material by using an alumina-silica based fiber spinning stock solution for use in an inorganic salt method. Next, the precursor fibers are heated under an environment which makes it difficult to carry out an oxidizing reaction on the carbon component contained in the precursor fibers. Thus, the precursor fibers are sintered to obtain alumina-silica based fibers.

Abstract: A manufacturing method by which alumina-silica based fibers excellent in mechanical strength can be readily and securely obtained. The method obtains precursor fibers as a material by using an alumina-silica based fiber spinning stock solution for use in an inorganic salt method. Next, the precursor fibers are heated under an environment which makes it difficult to carry out an oxidizing reaction on the carbon component contained in the precursor fibers. Thus, the precursor fibers are sintered to obtain alumina-silica based fibers.

Abstract: An object of the present invention is to provide a manufacturing method by which alumina-silica based fibers excellent in mechanical strength can be readily and securely obtained, and the present invention obtains precursor fibers as a material by using an alumina-silica based fiber spinning stock solution for use in an inorganic salt method. Next, the precursor fibers are heated under an environment which makes it difficult to carry out an oxidizing reaction on the carbon component contained in the precursor fibers. Thus, the precursor fibers are sintered to obtain alumina-silica based fibers.