Abstract: Pellets incorporated with a carbonaceous material of the present invention contain a carbonaceous material and iron ore mainly composed of iron oxide. The maximum fluidity of the carbonaceous material in softening and melting, and the ratio of iron oxide particles of 10 &mgr;m or smaller in the iron ore are within the range above a line which connects in turn points A, B and C shown in FIG. 1, including the line. This permits the production of pellets incorporated with a carbonaceous material having excellent thermal conductivity and high strength. Reduction of the pellets incorporated with a carbonaceous material produces reduced iron having high strength after reduction and a low fines ratio with improved productivity.

Abstract: Pellets incorporated with a carbonaceous material of the present invention contain a carbonaceous material and iron ore mainly composed of iron oxide. The maximum fluidity of the carbonaceous material in softening and melting, and the ratio of iron oxide particles of 10 &mgr;m or smaller in the iron ore are within the range above a line which connects in turn points A, B and C shown in FIG. 1, including the line. This permits the production of pellets incorporated with a carbonaceous material having excellent thermal conductivity and high strength. Reduction of the pellets incorporated with a carbonaceous material produces reduced iron having high strength after reduction and a low fines ratio with improved productivity.

Abstract: Pellets incorporated with a carbonaceous material of the present invention contain a carbonaceous material and iron ore mainly composed of iron oxide. The maximum fluidity of the carbonaceous material in softening and melting, and the ratio of iron oxide particles of 10 &mgr;m or smaller in the iron ore are within the range above a line which connects in turn points A, B and C shown in FIG. 1, including the line. This permits the production of pellets incorporated with a carbonaceous material having excellent thermal conductivity and high strength. Reduction of the pellets incorporated with a carbonaceous material produces reduced iron having high strength after reduction and a low fines ratio with improved productivity.

Abstract: A carbonaceous material is controlled such that the amount of carbon is from 7 to 60 mass % based on the total amount of iron and Zn in a starting mixture comprising one or more of ducts containing iron oxide and Zn oxide and a binder in an amount to bond the dusts, and water is added to prepare green pellets incorporated with the carbonaceous material. Then, dry pellets prepared by drying the thus prepared green pellets into a reduction furnace, the dry pellets are heated by heat transfer, mainly, radiation such that a temperature elevation rate is from 3 to 13° C./sec within a temperature range from 150 to 900° C. of the pellets, thereby reducing Zn oxide and evaporating Zn, as well as reducing iron oxide to produce reduced iron pellets.

Abstract: A carbonaceous material is controlled such that the amount of carbon is from 7 to 60 mass % based on the total amount of iron and Zn in a starting mixture comprising one or more of ducts containing iron oxide and Zn oxide and a binder in an amount to bond the dusts, and water is added to prepare green pellets incorporated with the carbonaceous material. Then, dry pellets prepared by drying the thus prepared green pellets into a reduction furnace, the dry pellets are heated by heat transfer, mainly, radiation such that a temperature elevation rate is from 3 to 13.degree. C./sec within a temperature range from 150 to 900.degree. C. of the pellets, thereby reducing Zn oxide and evaporating Zn, as well as reducing iron oxide to produce reduced iron pellets.

Abstract: A method for estimating the geographical distribution of a cohesive zone in a blast furnace which is intermittently charged with an iron ore material to produce molten iron substantially in a continuous manner is disclosed. The method comprises altering the whole or part of the composition of the charging iron ore material at a certain time point, measuring variations in the composition of produced molten iron ore slag over a given time period, and estimating the shape of the cohesive zone in the furnace on the basis of a pattern of variation of one selected component and the speed of gravitational descent of the charged material through the furnace.