Abstract: Provided is a toner that uses a crystalline resin, and demonstrates favorable dispersibility of the crystalline resin in the toner, demonstrates superior low-temperature fixability, and is able to inhibit fogging. The toner has a toner particle comprising a resin A, which has a long-chain alkyl group having an average number of carbon atoms of 27 to 50, and a crystalline resin, wherein the SP value (cal/cm3)1/2 of the crystalline resin is 9.00 to 12.00, and in a GC/MS analysis of components that volatize when the toner is heated for 10 minutes at 200° C., the amount of volatile components of saturated hydrocarbons having 30 to 37 carbon atoms is 90 ppm to 260 ppm of toluene equivalent, based on mass.

Abstract: The present invention provides a toner that exhibits an excellent low-temperature fixability and an excellent ejected paper adhesiveness during high-speed printing, without affecting the long-term storage stability, in which the toner has a toner particle that contains a resin component, wherein the toner has, in a DSC curve measured with a differential scanning calorimeter, a glass transition temperature of at least 50° C. and not more than 65° C. and a cold crystallization peak during cooling of at least 40° C. and not more than 70° C., and has an endothermic peak in a DSC curve measured with a differential scanning calorimeter for the resin component of at least 70° C. and not more than 95° C.

Abstract: Provided is a toner having good endurance stability and good low-temperature fixability in high-speed printing, and having good resistance to the adhesion of printed paper. The toner is a magnetic toner having, on the surface of toner particle containing a binder resin and an ester compound as a releasing agent, inorganic fine particle “a” and organic-inorganic composite fine particle having a volumetric specific heat of from 2,900 kJ/(m3·° C.) to 4,200 kJ/(m3·° C.), in which a coverage A of the surface of the toner particle with the inorganic fine particle “a” is 45.0% or more and 70.0% or less.

Abstract: A toner having compatibility between transfer properties and cleaning properties is provided. A toner wherein a fine particle A containing a primary particle having a number average particle diameter (D1) of 80 nm or more and 400 nm or less is present on the surface of a toner particle at a coverage ratio of 5 to 40%, a fixing rate of 30 to 90% by mass, and a variation coefficient of 0.1 to 0.5 in a region of 0.5 ??m2.

Abstract: The toner comprises: toner particles each containing a binder resin and a releasing agent; and an organic-inorganic composite fine particle, wherein: the organic-inorganic composite fine particle comprises: a vinyl resin particle containing a vinyl resin, the vinyl resin containing THF-insoluble matter in an amount of 95% by mass or more; and inorganic fine particles which are exposed at surfaces of the respective organic-inorganic composite fine particles, the organic-inorganic composite fine particle 1) has a plurality of convexes derived from the inorganic fine particles on the surfaces thereof, 2) has a number average particle size of 70-500 nm, and 3) has a shape factor SF-2 as measured at a magnification of 200,000 times of 103-120, and an absolute value of difference between an SP value of the releasing agent and an SP value of the vinyl resin is 0.50 (cal/cm3)1/2 or less.

Abstract: A toner excellent in end-portion hot offset properties is provided. A toner including toner particles and an external additive, wherein the toner particles contain a binder resin, and organic-inorganic composite fine particles dispersed in the binder resin, and the organic-inorganic composite fine particles (1) have a number-average particle diameter of 70 nm or more and 500 nm or less, (2) have a structure in which inorganic fine particles are embedded in a resin particle, convexes derived from the inorganic fine particles being present on surfaces of the organic-inorganic composite fine particles, (3) have a shape factor SF-2 of 103 or more and 120 or less, and (4) contain a resin component in which a proportion of THF-insoluble matter based on a mass of the resin component is 95% by mass or more.

Abstract: To provide a toner that can keep its melt-sticking to sleeve from occurring and, even in double-sided printing, can keep high-temperature offset from occurring and obtain high-quality images on both the surface and the back. The toner comprises toner particles each of which contains a binder resin containing a resin formed by the reaction of i) a resin (A) having a softening point TA (° C.) of 70° C. to 105° C. and having a peak top of endothermic peaks at 55° C. to 120° C. with ii) a resin (B) having a softening point TB (° C.) of 120° C. to 160° C. and having a peak top of endothermic peaks at 55° C. to 120° C., and, in its viscoelasticity characteristics, has a storage elastic modulus at temperature 180° C. (G?180) of 3.0×103 Pa to 3.0×104 Pa, where the loss tangent tan ? has at least one peak having a peak top within the range of 50° C. to 70° C. and, when peak top temperature of the peak is represented by T(° C.), the loss tangent at T+10(° C.) [tan ?(T+10)] is 1.0 to 1.

Abstract: Provided is a toner that shows both developability and electrostatic offset resistance. The toner includes a charge controlling agent that is represented by the following formula (1), and that has peaks at 15.000°±0.150° and 20.100°±0.150° in CuK? X-ray diffraction spectrum obtained in 2? range of 10° or more to 40° or less where ? represents Bragg angle, one of the peaks being a peak having a maximum intensity and the other being a peak having a second maximum intensity.

Abstract: A toner is provided which is superior in the long-term storage stability and has high low-temperature fixing properties. In a DSC curve as measured with a differential scanning calorimeter, the toner has a glass transition temperature of not less than 50° C. and not more than 60° C.; and the toner has, in regard to a resin composition contained therein, a difference of not less than 0.060 W/g in heat flow between a point on the curve at a temperature of 40° C. and a baseline in the range exceeding the glass transition temperature; and in viscoelastic characteristics measured at a frequency of 6.28 rad/sec, the toner has a storage elastic modulus (G?40) at a temperature of 40° C. of not less than 7.0×108 Pa and not more than 2.0×109 Pa, and a storage elastic modulus (G?70) at a temperature of 70° C. of not less than 1.0×105 Pa and not more than 1.0×107 Pa.

Abstract: The toner includes a resin component containing a crystalline polyester resin and a polyester-type resin that has a long-chain monomer bonded by condensation at a terminal, the toner having, in a total heat flow measured by a temperature-modulated differential scanning calorimeter, an endothermic peak resulting from the crystalline polyester resin in a specific temperature range, and the percentage of the endothermic quantity of the endothermic peak in a reversing heat flow with respect to the endothermic quantity of the endothermic peak in the total heat flow being at least 20.0%.

Abstract: The present invention provides a toner that exhibits an excellent low-temperature fixability and an excellent ejected paper adhesiveness during high-speed printing, without affecting the long-term storage stability, in which the toner has a toner particle that contains a resin component, wherein the toner has, in a DSC curve measured with a differential scanning calorimeter, a glass transition temperature of at least 50° C. and not more than 65° C. and a cold crystallization peak during cooling of at least 40° C. and not more than 70° C., and has an endothermic peak in a DSC curve measured with a differential scanning calorimeter for the resin component of at least 70° C. and not more than 95° C.

Abstract: Provided is a toner that has excellent low-temperature fixability and is capable of obtaining an image having a stable image density, in which the occurrence of image defects is suppressed. The toner includes toner base particles, each of which contains a binder resin and a magnetic material, and organic-inorganic composite fine particles on each of the toner base particles. Each of the organic-inorganic composite fine particles comprises a vinyl resin particle, and inorganic fine particles which are embedded in the vinyl resin particle, and at least a part of which are exposed. The volumetric specific heat of the organic-inorganic composite fine particles and the volumetric specific heat of the toner base particles satisfy a predetermined provision.

Abstract: The toner comprises: toner particles each containing a binder resin and a releasing agent; and an organic-inorganic composite fine particle, wherein: the organic-inorganic composite fine particle comprises: a vinyl resin particle containing a vinyl resin, the vinyl resin containing THF-insoluble matter in an amount of 95% by mass or more; and inorganic fine particles which are exposed at surfaces of the respective organic-inorganic composite fine particles, the organic-inorganic composite fine particle 1) has a plurality of convexes derived from the inorganic fine particles on the surfaces thereof, 2) has a number average particle size of 70-500 nm, and 3) has a shape factor SF-2 as measured at a magnification of 200,000 times of 103-120, and an absolute value of difference between an SP value of the releasing agent and an SP value of the vinyl resin is 0.50 (cal/cm3)1/2 or less.

Abstract: Provided is magnetic toner capable of favorably maintain fluidity of the magnetic toner in a developing unit even after a large number of image formation. The magnetic toner to which an external additive that has 1) a number average particle diameter of 70 or more and 200 or less, 2) a shape factor SF-1 of 100 or more and 250 or less, and 3) a shape factor SF-2 of 105 or more and 250 or less, is added, and a covering rate by silica on the surfaces of toner particles is 40.0% or more and 70.0% or less, and the magnetic toner has specific fluidity.

Abstract: A toner excellent in end-portion hot offset properties is provided. A toner including toner particles and an external additive, wherein the toner particles contain a binder resin, and organic-inorganic composite fine particles dispersed in the binder resin, and the organic-inorganic composite fine particles (1) have a number-average particle diameter of 70 nm or more and 500 nm or less, (2) have a structure in which inorganic fine particles are embedded in a resin particle, convexes derived from the inorganic fine particles being present on surfaces of the organic-inorganic composite fine particles, (3) have a shape factor SF-2 of 103 or more and 120 or less, and (4) contain a resin component in which a proportion of THF-insoluble matter based on a mass of the resin component is 95% by mass or more.

Abstract: A toner is provided in which low-temperature fixing properties and high-temperature offset resistance can be compatible, and the environmental stability of image density can also be obtained. A toner obtained by condensation polymerization of an alcohol component containing not less than 70 mol % of an aliphatic polyalcohol with a carboxylic acid component, and including a polyester resin having a concentration of an ester group of not less than 25% by mass and not more than 55% by mass, and a compound represented by the following formula (1) as a charge-controlling agent: (wherein A1, A2, and A3 each independently represent H, a nitro group, or a halogen atom; B1 represents H or an alkyl group; M represents an Fe atom, a Cr atom, or an Al atom; X+ represents a H ion, an alkali metal ion, a NH4 ion, an alkylammonium ion, or mixed ions thereof.

Abstract: A toner having toner particles, each of which contains a binder resin and a colorant, wherein in viscoelastic properties of the toner as measured with a rotating flat plate rheometer at a frequency of 6.28 rad/sec: a storage elastic modulus at the temperature of 60° C. (G?60) is in a range from 1.0×107 to 1.0×109 (Pa), and a maximal value (G?p) exists for the storage elastic modulus in a temperature range from 110° C. to 140° C., with this G?p being in a range from 5.0×104 to 5.0×106 (Pa).

Abstract: To provide a toner that can keep its melt-sticking to sleeve from occurring and, even in double-sided printing, can keep high-temperature offset from occurring and obtain high-quality images on both the surface and the back. The toner comprises toner particles each of which contains a binder resin containing a resin formed by the reaction of i) a resin (A) having a softening point TA (° C.) of 70° C. to 105° C. and having a peak top of endothermic peaks at 55° C. to 120° C. with ii) a resin (B) having a softening point TB (° C.) of 120° C. to 160° C. and having a peak top of endothermic peaks at 55° C. to 120° C., and, in its viscoelasticity characteristics, has a storage elastic modulus at temperature 180° C. (G?180) of 3.0×103 Pa to 3.0×104 Pa, where the loss tangent tan ? has at least one peak having a peak top within the range of 50° C. to 70° C. and, when peak top temperature of the peak is represented by T(° C.), the loss tangent at T+10(° C.) [tan ?(T+10)] is 1.0 to 1.

Abstract: A toner comprising toner particles, each of which contains a binder resin and a colorant, wherein the binder resin includes a resin having an endothermic peak at a temperature of 55° C. to 120° C. in a DSC curve; the toner has a softening point Tm of 90° C. to 140° C.; in the viscoelastic characteristic of the toner measured at a frequency of 6.28 rad/sec, the storage elastic modulus at a temperature of 180° C. is 1.0×102 Pa to 1.0×104 Pa; in a chart with the temperature on the x-axis and tan ? on the y-axis, tan ? has a peak having a peak top in the range of 50° C. to 70° C.; tan ? (P) at the peak top temperature is 2.0 to 10.0; the ratio of the tan ? (P) at the peak top temperature to tan ? (Tm) at a temperature of Tm (tan ? (P)/tan ? (Tm)) is in the range of 2.5 to 8.0.

Abstract: A toner is provided which is superior in the long-term storage stability and has high low-temperature fixing properties. In a DSC curve as measured with a differential scanning calorimeter, the toner has a glass transition temperature of not less than 50° C. and not more than 60° C.; and the toner has, in regard to a resin composition contained therein, a difference of not less than 0.060 W/g in heat flow between a point on the curve at a temperature of 40° C. and a baseline in the range exceeding the glass transition temperature; and in viscoelastic characteristics measured at a frequency of 6.28 rad/sec, the toner has a storage elastic modulus (G?40) at a temperature of 40° C. of not less than 7.0×108 Pa and not more than 2.0×109 Pa, and a storage elastic modulus (G?70) at a temperature of 70° C. of not less than 1.0×105 Pa and not more than 1.0×107 Pa.