Abstract: Following a determination that the distance along the Z-direction between the substrate and the mask is greater than the distance along the Z-direction to the nearest end of depth of field (DOF) for a camera from the near side of the mask, a control unit reduces the distance between the X-Y position of a substrate-mark and the X-Y position of the associated mask-mark, with a high-speed relative approach along the Z-direction between the substrate and the mask. Following a determination that the distance along the Z-direction between the substrate and the mask is equal to or less than the distance along the Z-direction to the nearest end of depth of field (DOF) from the near side of the mask, the control unit reduces the distance between the X-Y position of the substrate-mark and the X-Y position of the associated mask-mark, with a reduced-speed relative approach along the Z-direction.

Abstract: Provided are: a polycarbonate-based resin composition, including a polycarbonate-based resin (A) containing a polycarbonate-polyorganosiloxane copolymer (A1) having a predetermined structure, and 0.1 part by mass or more to 40 parts by mass or less of a white pigment (B) with respect to 100 parts by mass of the polycarbonate-based resin (A), wherein the white pigment (B) has an organic layer on a surface thereof, and a highest peak temperature of an evolved gas analysis curve of the organic layer obtained by evolved gas analysis with a pyrolysis gas chromatograph apparatus and a FID detector is 390° C. or more; and a molded article thereof.

Abstract: Provided are: a polycarbonate-based resin composition, including a polycarbonate-based resin (A) containing a polycarbonate-polyorganosiloxane copolymer (A1) having a predetermined structure, 0.1 part by mass or more to 40 parts by mass or less of a white pigment (B) with respect to 100 parts by mass of the polycarbonate-based resin (A), and 0.005 part by mass or more to 1.0 part by mass or less of a metal deactivator (C) with respect to 100 parts by mass of the polycarbonate-based resin (A); and a molded article thereof.

Abstract: Provided is a polycarbonate resin composition, including: an aromatic polycarbonate resin (A); and a polyether compound (B) having a polyoxyalkylene structure, in which: the polycarbonate resin composition includes 0.005 part by mass to 5 parts by mass of the polyether compound (B) with respect to 100 parts by mass of the aromatic polycarbonate resin (A); and the polycarbonate resin composition satisfies at least one of the following conditions (1) and (2): (1) an amount of potassium in the polyether compound (B) is 6 ppm by mass or less; and (2) an amount of sodium in the polyether compound (B) is 1 ppm by mass or less.

Abstract: A set of film thickness calculation values of constituent films of a lamination structure is calculated at a set of non-treating regions unexposed to laser light, the non-treating regions residing close to a set of treating regions to be annealed, and a set of crystallization levels of the set of treating regions is calculated by a fitting between a second spectral spectrum measurement values of the set of treating regions and a second spectral spectrum calculation values computed from the set of film thickness calculation values, for use to adjust a set of laser energies of laser light to be irradiated on a TFT substrate to be laser annealed at the next time.

Abstract: Provided is a polycarbonate resin composition, including, with respect to 100 parts by mass of an aromatic polycarbonate resin (A), 0.005 part by mass to 1 part by mass of a phosphorus-based compound (B) having an aryl group, and 0.005 part by mass to 5 parts by mass of a polyether compound (C) having a specific polyoxyalkylene structure, in which: an amount of a compound having a phenol structure produced by decomposition of the phosphorus-based compound (B) 1,500 hours after standing thereof under conditions of 40° C. and a humidity of 90% is 5 mass % or less with respect to the phosphorus-based compound (B); and when a weight of the phosphorus-based compound (B) is measured with a thermogravimetric-differential thermal analysis machine under a nitrogen atmosphere, a temperature at which the weight becomes smaller than the weight before the measurement by 2% is 340° C. or more.

Abstract: Provided is a polycarbonate resin molding material, including an aromatic polycarbonate resin (A), in which the polycarbonate resin molding material has: a content of o-hydroxyacetophenone measured by a predetermined method (1) of 1 ppm by mass or less; and a YI value measured by a predetermined method (2) of 1.21 or less.

Abstract: Provided are: a polycarbonate-based resin composition, including a polycarbonate-based resin (A) containing a polycarbonate-polyorganosiloxane copolymer (A1) having a predetermined structure, and 0.1 part by mass or more to 40 parts by mass or less of a white pigment (B) with respect to 100 parts by mass of the polycarbonate-based resin (A), wherein the white pigment (B) has an organic layer on a surface thereof, and a highest peak temperature of an evolved gas analysis curve of the organic layer obtained by evolved gas analysis with a pyrolysis gas chromatograph apparatus and a FID detector is 390° C. or more; and a molded article thereof.

Abstract: Provided is a polycarbonate-based resin composition, including a polycarbonate-based resin (A) containing a predetermined polycarbonate-polyorganosiloxane copolymer (A1), and 0.5 part by mass to 40 parts by mass of a white pigment (B) and 0.02 part by mass to 5.0 parts by mass of a hydrolysis resistant agent (C) with respect to 100 parts by mass of the polycarbonate-based resin (A).

Abstract: Provided is a polycarbonate resin composition, including: an aromatic polycarbonate resin (A); and a polyether compound (B) having a polyoxyalkylene structure, in which: the polycarbonate resin composition includes 0.005 part by mass to 5 parts by mass of the polyether compound (B) with respect to 100 parts by mass of the aromatic polycarbonate resin (A); and the polycarbonate resin composition satisfies at least one of the following conditions (1) and (2): (1) an amount of potassium in the polyether compound (B) is 6 ppm by mass or less; and (2) an amount of sodium in the polyether compound (B) is 1 ppm by mass or less.

Abstract: Provided is a polycarbonate resin molding material, including an aromatic polycarbonate resin (A), in which the polycarbonate resin molding material has: a content of o-hydroxyacetophenone measured by a predetermined method (1) of 1 ppm by mass or less; and a YI value measured by a predetermined method (2) of 1.21 or less.

Abstract: Provided is a polycarbonate resin composition, including, with respect to 100 parts by mass of an aromatic polycarbonate resin (A), 0.005 part by mass to 1 part by mass of a phosphorus-based compound (B) having an aryl group, and 0.005 part by mass to 5 parts by mass of a polyether compound (C) having a polyoxyalkylene structure, in which the phosphorus-based compound (B) includes such a compound that an amount of a compound having a phenol structure produced by decomposition of the compound 1,500 hours after standing thereof under conditions of 40° C. and a humidity of 90% is 5 mass % or less with respect to the phosphorus-based compound (B).

Abstract: Provided is a polycarbonate resin composition, including, with respect to 100 parts by mass of an aromatic polycarbonate resin (A), 0.005 part by mass to 1 part by mass of a phosphorus-based compound (B) having an aryl group, and 0.005 part by mass to 5 parts by mass of a polyether compound (C) having a specific polyoxyalkylene structure, in which: an amount of a compound having a phenol structure produced by decomposition of the phosphorus-based compound (B) 1,500 hours after standing thereof under conditions of 40° C. and a humidity of 90% is 5 mass % or less with respect to the phosphorus-based compound (B); and when a weight of the phosphorus-based compound (B) is measured with a thermogravimetric-differential thermal analysis machine under a nitrogen atmosphere, a temperature at which the weight becomes smaller than the weight before the measurement by 2% is 340° C. or more.

Abstract: Provided is a polycarbonate resin molding material, including an aromatic polycarbonate resin (A), in which the polycarbonate resin molding material has: a content of o-hydroxyacetophenone measured by a predetermined method (1) of 1 ppm by mass or less; and a YI value measured by a predetermined method (2) of 1.21 or less.

Abstract: Provided are an aromatic polycarbonate resin composition, including, with respect to 100 parts by mass of an aromatic polycarbonate resin (A), 0.005 to 0.5 parts by mass of a diphosphite compound (B) represented by the following general formula (I) and 0.001 to 0.5 parts by mass of an alicyclic epoxy compound (C), and an optical molded article: in the formula (I), R1, R2, R4, R5, R7, R8, R10, and R11 each independently represent a hydrogen atom, an alkyl group, or the like, R3, R6, R9, and R12 each independently represent an alkyl group, an aryl group, an aralkyl group, or the like, and m each independently represent an integer of 0 to 3.

Abstract: Provided is an aromatic polycarbonate resin molded body, which is obtained by molding a resin molding material containing an aromatic polycarbonate resin (A), in which: the molded body has a thin-walled portion having a thickness of 0.5 mm or less; the molded body has an o-hydroxyacetophenone content of 1 ppm by mass or less and a nitrogen atom content of 15 ppm or less; and the molded body is free of an absorption maximum in a wavelength range of from 500 nm to 600 nm.

Abstract: Provided is a polycarbonate resin composition pellet, which has a light transmittance at a wavelength of 380 nm of 97.0% or more when the light transmittance is measured by using a methylene chloride solution having a concentration of 12 g/dL, the solution being charged into a quartz glass cell having an optical path length of 5 cm, and which has a viscosity-average molecular weight (Mv) of from 11,000 to 22,000.

Abstract: Provided is a polycarbonate resin composition including, with respect to 100 parts by mass of an aromatic polycarbonate resin mixture (A) consisting of 5 to 100 mass % of an aromatic polycarbonate-polyorganosiloxane copolymer (A-1) and 95 to 0 mass % of an aromatic polycarbonate resin (A-2) except the component (A-1), the aromatic polycarbonate resin mixture (A) having a content of a polyorganosiloxane unit is 1 mass % or more, 0.002 to 0.200 parts by mass of a phosphorus-based antioxidant (B) and 0 to 0.200 parts by mass of an epoxidation stabilizer (C), in which a reduction ratio P between the viscosity-average molecular weights of the resin composition before and after a pressure cooker test calculated from the calculation equation (I) is 20% or less.

Abstract: Provided is a polycarbonate resin molding material, including an aromatic polycarbonate resin (A), in which the polycarbonate resin molding material has: a content of o-hydroxyacetophenone measured by a predetermined method (1) of 1 ppm by mass or less; and a YI value measured by a predetermined method (2) of 1.21 or less.

Abstract: Provided is a polycarbonate resin composition, including, with respect to 100 parts by mass of an aromatic polycarbonate resin (A), 0.005 part by mass to 1 part by mass of a phosphorus-based compound (B) having an aryl group, and 0.005 part by mass to 5 parts by mass of a polyether compound (C) having a polyoxyalkylene structure, in which the phosphorus-based compound (B) includes such a compound that an amount of a compound having a phenol structure produced by decomposition of the compound 1,500 hours after standing thereof under conditions of 40° C. and a humidity of 90% is 5 mass % or less with respect to the phosphorus-based compound (B).