Abstract: A hollow stabilizer having an excellent fatigue property and higher strength compared to the conventional ones has a chemical composition containing 0.26% to 0.30% of C, 0.05% to 0.35% of Si, 0.5% to 1.0% of Mn, 0.05% to 1.0% of Cr, 0.005% to 0.05% of Ti, 0.0005% to 0.005% of B, and 0.0005% to 0.005% of Ca, wherein; Al, P, S, N, and O are limited to 0.08% or less, 0.05% or less, less than 0.0030%, 0.006% or less, and 0.004% or less, respectively, a remainder of the chemical composition consists of Fe and unavoidable impurities, a value of a product of the Mn content and the S content is 0.0025 or less, and a critical cooling rate Vc90 represented by a predetermined equation is 40° C./s or less; and wherein a metallic structure comprises a tempered martensite, a length of elongated MnS present at a center part in a thickness direction of the hollow stabilizer is 150 ?m or less, a HRC is from 40 to 50, a thickness to outer diameter ratio is 0.