Abstract: A semiconductive glaze product is provided, which exhibits low thermal expansion coefficient without adversely affecting other glaze characteristics, and which, when applied to an insulator, attains enhanced mechanical strength of the insulator. The semiconductive glaze product contains a glaze composition and a flux. The glaze composition contains a KNaO—MgO—CaO—Al2O3-SiO2 base glaze, in which the compositional proportions of KNaO, MgO, and CaO, as represented by the Seger formula, are 0.1 to 0.4, 0.2 to 0.6, and balance, respectively. The glaze composition contains a metal oxide composition including tin oxide and antimony oxide, wherein the amount of flux is 10 parts by weight or less on the basis of 100 parts by weight of the glaze composition.

Abstract: The present invention provides a semiconductive glaze product which exhibits low thermal expansion coefficient without adversely affecting other glaze characteristics, and which, when applied to an insulator, attains enhanced mechanical strength of the insulator; a method for producing the semiconductive glaze product; and an insulator coated with the semiconductive glaze product. The semiconductive glaze product contains a glaze composition and a flux, the glaze composition containing a KNaO—MgO—CaO—Al2O3—SiO2-based base glaze in which the compositional proportions of basic components; i.e., KNaO, MgO, and CaO, as represented by the Seger formula, are 0.1 to 0.4, 0.2 to 0.6, and balance, respectively, and containing a metal oxide composition including tin oxide and antimony oxide, wherein the amount of the flux is 10 parts by weight or less on the basis of 100 parts by weight of the glaze composition.

Abstract: A process for producing a concrete product, which includes a step of preparing a primary concrete by mixing a super dry consistency concrete having a unit amount of water of at most 100 kg/cm.sup.3, a step of preparing a secondary concrete by weighing a suitable amount of the primary concrete and adding at least water, a water reducing agent and a setting accelerator thereto, followed by remixing, and a step of molding the secondary concrete in a formwork.