Abstract: A roughened plated sheet including a roughened plated layer having a roughened nickel plated layer and a zinc plated layer formed on at least one surface of a metal substrate in this order from the metal substrate side, wherein a ten-point average roughness Rzjis of a surface of the roughened plated layer, according to laser microscope measurement, is 3 ?m or more, and the metal substrate is a steel sheet.

Abstract: Provided is a roughened plated sheet comprising a roughened plated layer having a roughened nickel plated layer and a zinc plated layer formed on at least one surface of a metal substrate in this order from the metal substrate side, wherein a ten-point average roughness Rzjis of a surface of the roughened plated layer, according to laser microscope measurement, is 3 ?m or more.

Abstract: Provided is a roughened plated sheet comprising a roughened plated layer having a roughened nickel plated layer and a zinc plated layer famed on at least one surface of a metal substrate in this order from the metal substrate side, wherein a ten-point average roughness Rzjis of a surface of the roughened plated layer, according to laser microscope measurement, is 3 ?m or more.

Abstract: A laminated metal sheet obtained by laminating a polyester film on a metal sheet, wherein the polyester film has a double refraction represented by the following relation,.DELTA.n=n.sub.m -n.sub.twherein n.sub.m is a refractive index in the direction of a maximum orientation of the film, and n.sub.t is a refractive index in the direction of thickness of the film,which is higher on the side of the front surface of the polyester film than on the side of the metal sheet, and has a peak in the double refraction in a way of thickness from the side of the front surface toward the side of the metal sheet. A seamless can formed from such a laminated metal sheet exhibits excellent shock resistance, flavor-retaining property, corrosion resistance and like properties.

Abstract: Electroplated steel sheet suitable for soldering is provided herein by coating the plated steel sheet with a post-treatment solution in the range of 0.02 to 2 .mu.m in dry thickness. The post-treatment solution contains from 2 to 100 g/l of at least one water-soluble or water-dispersed material. The post-treatment solution may further contain chromium ion, hereafter referred to as Cr.sup.6+, from 0.01 to 3 g/l, and/or organic amine soap from 10 to 100 g/l. A suitable pH value of the post-treatment solution is from 3 to 10.

Abstract: A laminated draw-formed container obtained by draw-forming a laminated material of a metal plate on which a resin film is laminated into a cup with bottom, wherein the resin film comprises a polyester composition which contains a polyethylene terephthalate component as a chief component and further contains a polyethylene isophthalate component and a polybutylene terephthalate component, the resin film having a density of from 1.32 to 1.39 g/cc at any part of the container and further having, on the upper part of the container, a trans ratio of ethylene glycol residue of from 0.1 to 1.5 as found by the ATR method, as well as a process for producing the container. The draw-formed container exhibits excellent shock resistance irrespective of the passage of time, and particularly dent resistance and barrier property against corrosive components, as well as intimate adhesion to the metal substrate.

Abstract: Electroplated steel sheet suitable for soldering is provided by coating the plated steel sheet with a post-treatment solution in the range of 0.01 to 2 um in dry thickness. The post-treatment solution contains from 2 to 200 g/liter of at least one water-soluble or water-dispersed materials other than phosphoric esters, and/or from 5 to 200 g/liter of phosphoric esters, and also contains from 2 to 100 g/liter of at least one water-soluble or water-dispersable organic fluoro compound. The post-treatment solution may further contain from 0.01 to 3 g/liter of Cr.sup.6+ ion, and/or from 10 to 100 g/liter of organic amine soap. A suitable pH value of the post-treatment solution is between 3 and 10.